1、INCH-POUND Beneficial comments (recommendations, additions, deletions) and any pertinent data which may be of us in improving this document should be addressed to: Defense Supply Center Philadelphia, Clothing and Textiles Directorate, Attn: DSCP-COC, bld 6-1 -D, 700 Robbins Ave, Philadelphia, PA 19
2、1 1 1-5096. MIL-DTL-32066 June 14,2000 SUPERSEDING ZZ-G-3 8 1 C July 20, 1977 ; DETAIL MILITARY SPECIFICATION GLOVES, RUBBER, INDUSTRIAL This specification is approved for use by all Department and Agencies of the Department of Defense. 1. SCOPE The rubber gloves covered by this detailed military sp
3、ecification are intended for the following applications: Type I - Handling acid and alkali materials Type II - Fueling operations Type III - Handling organic solvents 2. CLASSIFICATION. The rubber gloves will be in the following types: Type I - Acid and Alkali resistant Type II - Aromatic fuel resis
4、tant Type III - Organic solvent resistant Style 1 - Cuff edge with self binding roll or flat and reinforced. Style 2 - Cuff edge permanently folded, with self binding roll or flat and reinforced. AMSC NIA FSC 8415 Provided by IHSNot for ResaleNo reproduction or networking permitted without license f
5、rom IHS-,-,-MIL-DTL-32066 2. APPLICABLE DOCUMENTS 2.1 General. The documents listed in this section are specified in sections 3 and 4 of this specification. This section does not include documents cited in other sections of this specification or recommended for additional information or as examples.
6、 While every effort has been made to ensure the completeness of this list, document users are cautioned that they must meet all specified requirements documents cited in sections 3 and 4 of this specification, whether or not they are listed. 2.2 Government Documents 2.2.1 Specifications, standards,
7、and handbooks The following specifications, standards, and handbooks form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these documents are those listed in the issue of the Department of Defense Index of Specifications and Standards (DODISS) and su
8、pplement thereto, cited in the solicitation (see 6.2). STANDARDS FEDERAL FED-STD-601 (Unless otherwise indicated, copies of Federal and military specifications, standards and handbooks are available from the Standardization Documents Order Desk, Bldg. 4D, 700 Robbins Avenue, Philadelphia, PA 19 1 1
9、1-5094.) 2.3 Non-Government publications. The following document(s) form a part of this document to the extent specified herein. Unless otherwise specified, the issues of the documents which are DoD adopted are those listed in the issue of the DODISS cited in the solicitation. Unless otherwise speci
10、fied, the issues of documents not listed in the DODISS are the issues of the documents cited in the solicitation (see 6.2). AMERICAN SOCIETY FOR TESTING AND MATERIALS D-412-87 Test Methods For Rubber Properties in Tension (Applications for copies should be addressed to American Society For Testing a
11、nd Materials, 1 O0 Barr Harbor Drive, West Conshohocken, PA 19428.) ANSUASQC Z 1.4 (Applications for copies should be addressed to ANSUASQC American Society for Quality Control 61 1 East Winconsin Ave. , Milwaukee WI 53202) (Non-Government standards and other publications are normally available from
12、 the organizations that prepare or distribute the documents. These documents also may be available in or through libraries or other informational services.) 2.4 Order of precedence. In the event of a conflict between the text of this document and the references cited herein (except for related assoc
13、iated specifications or specification sheets), the text of this document 2 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-32066 takes precedence. Nothing in this document however, supersedes applicable laws and regulations unless a specific
14、exemption has been obtained. 3. REQUIREMENTS 3.1 First article. When specified (see 6.2), the contractor shall furnish sample unit(s) for first article inspection and approval (see 4.2) 3.2 Materials 3.2.1 Rubber compound. The gloves shall be made of a high grade natural or synthetic rubber compound
15、 or a combination thereof, natural or pigmented black in color, suitably compounded and vulcanized to meet the requirements of this document. The gloves shall be made by the tlipping”or other seamless process with the fingers and palm surfaces texturized or embossed to reduce slippage. For Army proc
16、urement only, the rubber compound for the type II, style 2, gloves shall receive prior approval by the appropriate medical service and so listed in the invitation for bids. 3.2.2 Fingers The fingers shall conform in shape to the natural hand insofar as possible, and shall be of the curved finger sty
17、le. The fingers shall be round or slightly elliptical in shape, with the major axis perpendicular to the palm. The tip of the thumb shall turn inward slightly toward the second finger. The thumb shall be circular or slightly elliptical in shape, with its axis running similar to that of the fiigers s
18、pecified herein. The base of the thumb shall be positioned in front of the index finger with the base set out as it is on the natural hand, and shall continue to the palm in a gently elliptical curve so as to keep the thumb crotch area and part just below the thumb crotch area on the palm without a
19、noticeable crease. See figures 2 and 3 that are furnished for informational purposes only. 3.2.3 Cuff edges 3.2.3.1 Style 1 . The top edge of the gloves shall be rolled outward to form a self binding roll or left flat and reinforced with a band of rubber of the same composition as the rubber in the
20、glove. When the glove edge is rolled, the rolled edge shall be 0.150 to 0.250 inch in diameter. When a reinforcement band is used, the reinforced band edge shall be 0.3 13 to 0.437 inch in diameter (see dimension A of figure 2). 3.2.3.2 Style 2. The top edge of the gloves shall be permanently folded
21、 back on itself to form a cuff 1 1/8 to 1 3/8 inch in width (see dimension B of figure 3). The bottom edge of the folded cuff shall be rolled inward or reinforced with a band of rubber as describe in 3.1.3.1 (see dimension A of Figure 3). 3.2.4 Physical and chemical requirements The finished gloves
22、shall conform to the requirements shown in table I. 3 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Characteristic Requirement Min Max cid). MIL-DTL-32066 Table I - Physical and Chemical Requirements Tensile strength, p.s.i. After air heating mediu
23、maging 1500 11 Distilled water 1500 11 Sodium Hydroxide (type I gloves only) 1500 11 Sulfuric acid (type I glove only) 1500 11 Aromatic fuel (type II gloves only) 750 11 Organic solvents (type III gloves only) 1500 11 Cuff edge and reinforcement band combined layers (style 1 and 2) 1700 21 11 Initia
24、l 1600 11 After immersion in: Alcohol (type II gloves only) 1000 11 Elongation percent (%) Initial 250 After immersion in: Aromatic fuel (type II gloves only) Water alcohol (type II gloves only) 200 200 500 21 - - 31 Cuff edge and reinforcement band combined layers (style 1 and 2) Change in volume,
25、percent (type III gloves only) Electrolyte immersion (type I glove only) Tension set, percent - Adhesion between the cuff edge and reinforcement band, pounds per inch (2.5cm) style 1 and2 8.0 21 A/ Cold crack resistance (type I gloves only) Porosity - 61 - 51 !I To convert poundslsquare inch to pasc
26、al (Pa), multiply by 6894 (6.894 - 21 Applicable when the top edge of the glove (style 1) or bottom edge of the glove (style 2), is reinforced with a band of rubber as described in 3.2.3.1. - 31 The electrolyte solution upon removal of the test specimen shall show no evidence of sediment and the col
27、or shall not exceed Standard No. 6 as illustrated in the Gardner Liquid Color Standards apparatus ( see 6.4 ). 4 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-32066 - 4/ To convert pounds per inch to newton (N), per 2.5cm, multiply by 4.45.
28、 - 5/ The gloves shall show no evidence of cracking. - 6/ The gloves shall show no evidence of leakage. - 7/ Determined 24 2 % hours after removal from mixture or organic solvent. 3.4 Thickness - The thickness of the gloves shall conform to the requirements specified in table II and 3.4.1 when teste
29、d as specified in 4.3.2.2.1. Table II - Thickness limits AreaA L/ AreaB S/ Types Min Max Min Max Min Max I .O28 inch .40 inch - - - - II - - .O28 inch .O40 inch .O 17 inch .O40 inch (28 mils) (40 mils) (1 7 mils) (40 mils) III .O28 inch .40 inch (28 mils) (40 mils) (28 mils) (40 mils) NOTE: The desi
30、gnated area A and B as specified in the above table and described in Footnotes L/ and S/, are illustrated in Figure 1 of ASTM standard D-120-70. In addition, a convenient apparatus set-up for determining the glove thickness Is also illustrated in figures 2 and 3. - 1/ Area A extends from the ends of
31、 the thumb and fingers, excluding the tips, up to and - 2/ Area B extends from the tip edge of cuff at glove opening to the line at the thumb crotch, imaginary line around the glove at the thumb crotch. and also includes the thumb tip and finger tips. The thumb or finger tip is the area of rubber fr
32、om the extreme tip of the fiiger to a line around each finger in a plane one half inch distant axially from the tip. 3.4.1 Thumb and finger crotches The thumb and finger crotches of gloves .O28 inch or thicker, shall be not less than 25 percent of the minimum thickness specified. 5 Provided by IHSNo
33、t for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-32066 3.5 Marking. Each glove shall have an inscription as shown below, centered on the palm side. The inscription shall be permanently and legibly marked with a contrasting color permanent type ink, and shall b
34、e not less than % inch in height. For style 1 gloves, the bottom line of the inscription shall finish approximately 1 inch down from the tip rolled or reinforced cuff edge. For style 2 gloves, the bottom line of the inscription shall finish approximately 1 inch down from the rolled or reinforced cuf
35、f edge. GLOVES, RUBBER INDUSTRIAL CONTRACT NO: STOCK NO: TYPE STYLE SIZE NAME OF CONTRACTOR DO NOT USE FOR ELECTRICAL WORK 3.6 Dusting or chlorination. The inside and outside of each finished glove shall be lightly dusted with whiting, talc, or other finely divided mineral matter which does not supp
36、ort mildew growth. As an alternative, the inside and outside of each finished glove may be chlorinated to provide a smooth surface and remove and tackiness. Excessive chlorination shall be avoided to prevent excessive stiffening, discoloration or slipperiness. 3.7 Measurements. The measurements of t
37、he finished gloves shall conform to the dimensions specified in table III. All measurements and tolerances are expressed in inches and the metric equivalents, and shall be taken without pulling or stretching. Table III - Finished Measurement SIZE Measurement 9 10 11 12 14 Toleranace Circumference L/
38、 9 % 10 % 11 % 12% 14% - +% OverallLength S/ 14 14 14 14 14 - +% (inches) (inches) 18 18 18 18 18 - +% - 1/ The size of the finished gloves shall be determined by measuring the circumference of the palm at its widest point. - 2/ The overall length of each glove shall be taken from the tip of the sec
39、ond finger to top open edge (see dimensions Cof figures 1 and 2). 3.8 Workmanship. The finished gloves shall conform to the quality established by this specification. The occurrence of defects shall not exceed the applicable acceptable quality levels. 6 Provided by IHSNot for ResaleNo reproduction o
40、r networking permitted without license from IHS-,-,-MIL-DTL-32066 4. VERIFICATION. 4.1 follows: Classification of inspections The inspection requirements specified herein are classified as 4.1.1 reserves the right to check test such items to determine the validity of the certification. Certificate o
41、f compliance Where certificates of compliance are submitted, the government 4.1.2 First article inspection When required , the first article submitted in accordance with 3.1, shall be inspected as specified in 4.3.2.1 and 4.3.2.2 for compliance with design, construction, workmanship, and dimensional
42、 requirements. 4.2 provisions of ANSUASQC Z 1.4, except where otherwise indicated hereinafter. Quality conformance inspection Sampling for inspection shall be in accordance with the 4.3.1 Component and material inspection In accordance with 4.1 above, components and material shall be tested in accor
43、dance with all the requirements of referenced specification, drawings, and standards unless otherwise excluded, amended, modified, or qualified in this specification or applicable purchase document. In addition, the contractor shall furnish a certificate of compliance for the material identification
44、 of the rubber compound (see 3.2.1 ) and for the dusting powder or chlorination process which is applicable (see 3.6). 4.4.2 Examination of the end item. The defects found during the examination of the end item shall be classified in accordance with 4.3.2.1 and 4.3.2.2 . The applicable inspection le
45、vels and the acceptable quality levels will be a specified in the contract or purchase order. 7 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-32066 4.3.2.1 Visual examination Defects Classification Major Minor Pairing a. Mispared, i.e., two
46、 gloves of different Sizes or two gloves for the same hand b. definite variation in color or appearance Design Any characteristics not in accordance With specified requirements Color Not as specified Construction and Workmanship (applicable to Inside and outside of glove) 101 20 1 102 202 a. Any cut
47、, hole, tear, rip or rupture through material 103 b. Evidence of improper vulcanization e.g., tacky, etc. 104 c. Any repair or patch 105 d. Any blister 106 e. Any solid rubber ridge, run or lump resulting in a thickness greater than the maximum thickness of the rubber allowed for the glove f. Not se
48、amless construction 107 g. Any burned spot which cracks on flexing, bending, or stretching (by hand ) 108 h. Any pinch, thin spot, abaded area, deep crease, readily removable Foreign matter (see note below), or similar defective condition: 203 -Seriously affecting serviceability or appearance (resul
49、ts in a thickness of the rubber at the defect less than the allowable minimum thickness - see 4.3.2.2.1). 109 - Affecting serviceability or appearance, but not seriously i. Any pit questionable in depth, i.e., evidence of being deep enough that Could result in a thickness of the rubber at its base less than the Allowable minimum thickness j. Any pit shallow in depth, i.e., the base of the defect is visible and Should not be expected to result in