EN 10029-2010 en Hot-rolled steel plates 3 mm thick or above - Tolerances on dimensions and shape《热轧钢板厚3毫米或以上 尺寸和形状公差》.pdf

1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationBS EN 10029:2010Hot-rolled steel plates 3 mmthick or above Tolerances ondimensions and shapeIncorporating corrigendum January 2012BS EN 10029:2010 BRITISH STANDARDNational forewo

2、rdThis British Standard is the UK implementation of EN 10029:2010,The UK participation in its preparation was entrusted to TechnicalCommittee ISE/103, Structural Steels Other Than Reinforcements.A list of organizations represented on this committee can beobtained on request to its secretary.This pub

3、lication does not purport to include all the necessaryprovisions of a contract. Users are responsible for its correctapplication. The British Standards Institution 2012ISBN 978 0 580 77602 1ICS 77.140.50Compliance with a British Standard cannot confer immunity fromlegal obligations.This British Stan

4、dard was published under the authority of theStandards Policy and Strategy Committee on 31 December 2010.Amendments/corrigenda issued since publicationDate Text affected31 January 2012 Additional information to National ForewordThis edition no longer contains requirements for individually hot-BS EN

5、10029:1991 which is withdrawn.incorporating corrigendum January 2012. It supersedesrolled quarto stainless steel plates, which have been transferred toBS EN ISO 18286:2010.EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 10029 November 2010 ICS 77.140.50 Supersedes EN 10029:1991English Version H

6、ot-rolled steel plates 3 mm thick or above - Tolerances on dimensions and shape Tles en acier lamines chaud, dpaisseur gale ou suprieure 3 mm - Tolrances sur les dimensions et la forme Warmgewalztes Stahlblech von 3 mm Dicke an - Grenzabmae und Formtoleranzen This European Standard was approved by C

7、EN on 23 October 2010. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standar

8、ds may be obtained on application to the CEN Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to

9、the CEN Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, M

10、alta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG Management Centre: Avenue Marnix 17, B-1000 Brussels 2010 CEN All rights of ex

11、ploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 10029:2010: EBS EN 10029:2010EN 10029:2010 (E) 2 Contents Page Foreword 31 Scope 42 Normative references 43 Terms and definitions .44 Information to be supplied by the purchaser .44.1 Mandatory informati

12、on 44.2 Options .54.3 Designation 55 Form of supply .66 Tolerances on dimensions .66.1 Thickness .66.2 Width .76.3 Length .77 Tolerances on shape .77.1 Edge camber and out-of squareness.77.2 Flatness 88 Measurement 98.1 General 98.2 Thickness .98.3 Width .98.4 Length .98.5 Edge camber . 108.6 Out-of

13、 squareness 108.7 Flatness . 11Annex A (informative) List of product standards where dimensional standard EN 10029 is applied . 12BS EN 10029:2010EN 10029:2010 (E) 3 Foreword This document (EN 10029:2010) has been prepared by Technical Committee ECISS/TC 103 “Structural steels other than reinforceme

14、nts”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by May 2011, and conflicting national standards shall be withdrawn at the latest by May 2011. Attention

15、is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 10029:1991. According to the CEN/CENELEC Internal Regulations, the n

16、ational standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlan

17、ds, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 10029:2010EN 10029:2010 (E) 4 1 Scope This European Standard specifies tolerances on dimensions and shape for hot-rolled non-alloy and alloy steel plates with the following characteris

18、tics: a) Nominal thickness: 3 mm t 400 mm; b) Nominal width: w 600 mm. Tolerances for products of width w 20 000 mm are required, the agreed tolerances on length are to be reported (see 6.3, Table 3); f) for plates with untrimmed edges, the chosen and agreed measuring points for the measurement of t

19、he thickness are to be reported (see 8.2). 4.3 Designation EXAMPLE 20 plates of steel S235JR (1.0038), as specified in EN 10025-2 according to this European Standard with nominal thickness of 25 mm, thickness tolerance class B, nominal width 2 000 mm, nominal length 4 500 mm, with trimmed edges, wit

20、h limited edge camber and out-of-squareness, with special tolerances for flatness: 20 plates EN 10029-B-G-S 25 x 2 000 x 4 500 Steel EN 10025-2 S235JR BS EN 10029:2010EN 10029:2010 (E) 6 5 Form of supply Plate according to this European standard can be supplied: with thickness tolerances of class A,

21、 B, C or D (see 6.1); with trimmed or untrimmed edges (NK) (see 6.2.2); with normal or limited edge camber and out-of-squareness (G) (see 7.1); with normal (N) or special (S) flatness tolerances (see 7.2). 6 Tolerances on dimensions 6.1 Thickness 6.1.1 Tolerances on thickness are given in Table 1. P

22、lates may be supplied with either: class A: for minus thickness tolerances depending on the nominal thickness; class B: for a fixed minus tolerance of 0,3 mm; class C: for a fixed minus tolerance of 0,0 mm; class D: for symmetrical tolerances. Table 1 Tolerances on thickness Dimensions in mm Nominal

23、 thickness t Tolerances on the nominal thickness (see 6.1.1) Class A Class B Class C Class D Lower Upper Lower Upper Lower Upper Lower Upper 3 t 20 000 mm shall be agreed at the time of enquiry and order (see 4.2, option e). 7 Tolerances on shape 7.1 Edge camber and out-of squareness For plate speci

24、fied with normal edge camber and out-of squareness in the order, the edge camber and out of squareness shall be so that it is possible to inscribe a rectangle with the dimensions of the ordered plate within the delivered size. BS EN 10029:2010EN 10029:2010 (E) 8 For plate specified with limited edge

25、 camber and out-of squareness (G) in the order, the maximum values for edge camber and out of squareness shall be agreed at the time of enquiry and order (see 4.2, option c). 7.2 Flatness 7.2.1 General Tolerances on flatness are given in Table 4 for normal tolerances (class N) and in Table 5 for spe

26、cial tolerances (class S). The plate shall be supplied with normal tolerances according to Table 4, only if otherwise specified in the order the plate shall be supplied with special tolerances (see 4.2, option d). Deviation from flatness shall be determined by measuring the distance between the plat

27、e and a straight edge (for details see 8.7). Straight edges of a length of 1 000 mm are used if the wave pitches (distance between the points of contact of the straight edge and the plate) are smaller than or equal to 1 000 mm. For longer wave pitches straight edges of a length of 2 000 mm are used.

28、 Deviations from flatness 2 mm shall not be considered as a wave and not be taken into account. NOTE It is pointed out that bad handling and storage can adversely affect the flatness of the product. The steel types according to Tables 4 and 5 are defined as follows: Steel type L: Products with a spe

29、cified minimum yield strength Re 460 MPa, neither quenched nor quenched and tempered. Steel type H: Products with a specified yield strength Re 460 MPa and all grades of quenched and quenched and tempered products. 7.2.2 Normal tolerances on flatness (class N) If the wave pitch (distance between the

30、 points of contact of the straight edge and the plate) is 1 000 mm the permissible deviation from flatness shall comply with the following requirements: For distances between the points of contact of two waves between 300 mm and 1 000 mm the maximum flatness tolerance is 1 % for steel type L and 1,5

31、 % of the wave pitch for steel type H, but not exceeding the values in Table 4. Table 4 Normal tolerances on flatness (class N) Dimensions in mm Nominal thickness t Steel Type La Steel Type HaMeasuring lengthb 1 000 2 000 1 000 2 000 3 t 5 9 14 12 175 t 8 8 12 11 15 8 t 15 7 11 10 1415 t 25 7 10 10

32、13 25 t 40 6 9 9 1240 t 250 5 8 8 12 250 t 400 6 9 9 13aSee 7.2.1. bUse 1 000 mm measuring length when wave pitch is 1 000 mm. BS EN 10029:2010EN 10029:2010 (E) 9 7.2.3 Special tolerances on flatness (class S) If the wave pitch (distance between the points of contact of the straight edge and the pla

33、te) is 1 000 mm the permissible deviation from flatness shall comply with the following requirements: For distances between the points of contact of two waves between 300 mm and 1 000 mm the maximum flatness tolerance is 0,5 % of the wave pitch for steel type L and 1 % of the wave pitch for steel ty

34、pe H, but not exceeding the values in Table 5. Table 5 Special tolerances on flatness (class S) Dimensions in mm Nominal thickness t Steel Type La Steel Type HaMeasuring lengthb1 000 2 000 1 000 2 000 3 t 5 5 10 7 145 t 8 5 10 7 13 8 t 15 3 6 7 1215 t 25 3 6 7 11 25 t 40 3 6 7 1140 t 250 3 6 6 10 25

35、0 t 400 4 7 7 11aSee 7.2.1. bUse 1 000 mm measuring length when wave pitch is 1 000 mm. 8 Measurement 8.1 General Measurements listed in 8.2 to 8.7 shall be used in case of dispute and be carried out at ambient temperature. 8.2 Thickness Thickness shall be measured at any point situated more than 25

36、 mm from the transverse or longitudinal edges of the plate; other than locally ground area (see 6.1.2). For plates with untrimmed edges, the measuring points shall be agreed at the time of enquiry and order (see 4.2, option f). 8.3 Width Width shall be measured perpendicular to the major axis of the

37、 plate. 8.4 Length The length of the plate is the length of the shorter of both longitudinal edges. BS EN 10029:2010EN 10029:2010 (E) 10 8.5 Edge camber The edge camber value q is the maximum deviation between the longitudinal edge and the straight line joining the two ends of this edge. It is measu

38、red on the concave edge of the plate (see Figure 1). Key 1 Edge camber q 2 Side edge (concave side) 3 Straight edge a Rolling direction Figure 1 Measuring of edge camber 8.6 Out-of squareness The out-of squareness value u is the orthogonal projection of one transverse edge on one longitudinal edge (

39、see Figure 2). Key 1 Out-of squareness u 2 Square 3 Side edge a Rolling direction Figure 2 Measuring of out of squareness BS EN 10029:2010EN 10029:2010 (E) 11 8.7 Flatness To measure flatness the plates shall be placed on a flat surface. Deviation from flatness shall be determined by measuring the d

40、eviation in distance between the plates and a straight edge of 1 000 mm or 2 000 mm long (see Tables 4 and 5) which may be placed in any direction. Only the part situated between the points of contact between the straight-edge and the plate shall be taken into consideration. Deviations shall be meas

41、ured at a point at least 25 mm from the longitudinal edges and at a distance a from the plate ends, depending on whether the normal tolerances or special tolerances apply respectively (see Figure 3). Dimensions in millimetres Key a = 200 mm for normal flatness tolerances a = 100 mm for special flatn

42、ess tolerances Figure 3 Measuring of flatness BS EN 10029:2010EN 10029:2010 (E) 12 Annex A (informative) List of product standards where dimensional standard EN 10029 is applied EN 10025-2, Hot rolled products of structural steels Part 2: Technical delivery conditions for non-alloy structural steels

43、 EN 10025-3, Hot rolled products of structural steels Part 3: Technical delivery conditions for normalized/normalized rolled weldable fine grain structural steels EN 10025-4, Hot rolled products of structural steels Part 4: Technical delivery conditions for thermomechanical rolled weldable fine grai

44、n structural steels EN 10025-5, Hot rolled products of structural steels Part 5: Technical delivery conditions for structural steels with improved atmospheric corrosion resistance EN 10025-6:2004+A1:2009, Hot rolled products of structural steels Part 6: Technical delivery conditions for flat product

45、s of high yield strength structural steels in the quenched and tempered condition EN 10028-2, Flat products made of steels for pressure purposes Part 2: Non-alloy and alloy steels with specified elevated temperature properties EN 10028-3, Flat products made of steels for pressure purposes Part 3: We

46、ldable fine grain steels, normalized EN 10028-4, Flat products made of steels for pressure purposes Part 4: Nickel alloy steels with specified low temperature properties EN 10028-5, Flat products made of steels for pressure purposes Part 5: Weldable fine grain steels, thermomechanically rolled EN 10

47、028-6, Flat products made of steels for pressure purposes Part 6: Weldable fine grain steels, quenched and tempered EN 10083-2, Steels for quenching and tempering Part 2: Technical delivery conditions for non alloy steels EN 10083-3, Steels for quenching and tempering Part 3: Technical delivery cond

48、itions for alloy steels EN 10084, Case hardening steels Technical delivery conditions EN 10085, Nitriding steels Technical delivery conditions EN 10149-2, Hot-rolled flat products made of high yield strength steels for cold forming Part 2: Delivery conditions for thermomecanically rolled steels EN 1

49、0149-3, Hot-rolled flat products made of high yield strength steels for cold forming Part 3: Delivery conditions for normalized or normalized rolled steels EN 10207, Steels for simple pressure vessels Technical delivery requirements for plates, strips and bars EN 10225, Weldable structural steels for fixed offshore structures Technical delivery condition