EN 1062-3-2008 en Paints and varnishes - Coating materials and coating systems for exterior masonry and concrete - Part 3 Determination of liquid water permeability《涂料和清漆 外部砖石建筑和混凝.pdf

1、BS EN1062-3:2008ICS 87.040NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBRITISH STANDARDPaints and varnishes Coating materialsand coating systems forexterior masonry andconcretePart 3: Determination of liquid waterpermeabilityThis British Standardwas published under theauthor

2、ity of the StandardsPolicy and StrategyCommittee on 32008 BSI 2008ISBN 978 0 580 58593 7Amendments/corrigenda issued since publicationDate CommentsBS EN 1062-3:2008National forewordThis British Standard is the UK implementation of EN 1062-3:2008. Itsupersedes BS EN 1062-3:1999 which is withdrawn.The

3、 UK participation in its preparation was entrusted to TechnicalCommittee STI/28, Paint systems for non-metallic substrates.A list of organizations represented on this committee can be obtained onrequest to its secretary.This publication does not purport to include all the necessary provisionsof a co

4、ntract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunityfrom legal obligations.0 SeptemberBS EN 1062-3:2008EUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 1062-3January 2008ICS 87.040 Supersedes EN 1062-3:1998 English VersionPaints and var

5、nishes - Coating materials and coating systemsfor exterior masonry and concrete - Part 3: Determination ofliquid water permeabilityPeintures et vernis - Produits de peinture et systmes derevtements pour maonnerie et bton extrieurs - Partie 3: Dtermination de la permabilit leau liquideBeschichtungsst

6、offe - Beschichtungsstoffe undBeschichtungssysteme fr mineralische Substrate undBeton im Auenbereich - Teil 3: Bestimmung derWasserdurchlssigkeitThis European Standard was approved by CEN on 25 November 2007.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate th

7、e conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the CEN Management Centre or to any CEN member.This European Standard exists in

8、three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as theofficial versions.CEN members are the national standards bodies of

9、Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COM

10、MITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: rue de Stassart, 36 B-1050 Brussels 2008 CEN All rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 1062-3:2008: EBS EN 1062-3:2008EN 1062-

11、3:2008 (E) 2 Contents Page Foreword3 Introduction .4 1 Scope 5 2 Normative references 5 3 Principle5 4 Apparatus .5 5 Sampling.6 6 Test specimens6 6.1 General6 6.2 Substrate 6 6.3 Preparation and coating6 6.4 Drying and conditioning .6 7 Procedure .7 8 Expression of results 7 9 Precision.7 9.1 Repea

12、tability.7 9.2 Reproducibility.8 10 Test report 8 BS EN 1062-3:2008EN 1062-3:2008 (E) 3 Foreword This document (EN 1062-3:2008) has been prepared by Technical Committee CEN/TC 139 “Paints and varnishes”, the secretariat of which is held by DIN. This European Standard shall be given the status of a n

13、ational standard, either by publication of an identical text or by endorsement, at the latest by July 2008, and conflicting national standards shall be withdrawn at the latest by July 2008. This document supersedes EN 1062-3:1998. Attention is drawn to the possibility that some of the elements of th

14、is document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Sta

15、ndard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. BS

16、 EN 1062-3:2008EN 1062-3:2008 (E) 4 Introduction This document is one of a number of parts of EN 1062 dealing with test methods for coating materials and coating systems for exterior masonry and concrete. It should be read in conjunction with EN 1062-1. BS EN 1062-3:2008EN 1062-3:2008 (E) 5 1 Scope

17、This European Standard specifies a method for determining the liquid water permeability of coatings, coating systems and related products, intended for exterior masonry and classification according to EN 1062-1. The method is applicable to coatings and coating systems on porous substrates such as br

18、ick, concrete and renderings. A liquid water permeability w of more than 0,5 kg/(m x h0,5) will not be accurately quantified by the test method described in this standard. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated refe

19、rences, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 1062-1, Paints and varnishes Coating materials and coating systems for exterior masonry and concrete Part 1: Classification EN 23270, Paints and varnis

20、hes and their raw materials Temperatures and humidities for conditioning and testing (ISO 3270:1984) EN ISO 1513, Paints and varnishes Examination and preparation of samples for testing (ISO 1513:1992) EN ISO 15148, Hygrothermal performance of building materials and products Determination of water a

21、bsorption coefficient by partial immersion (ISO 15148:2002) EN ISO 15528, Paints, varnishes and raw materials for paints and varnishes - Sampling (ISO 15528:2000) 3 Principle Exterior masonry coatings play an important role in preventing rain water penetrating into porous mineral substrates. This tr

22、ansmission rate for liquid water is evaluated using blocks of highly porous mineral substrates which are coated by the coating or coating system on one of their faces. The test specimens are immersed under controlled conditions in water and weighed at suitable intervals of time. The liquid water per

23、meability is determined by the change in mass. 4 Apparatus 4.1 Container of suitable size, for deionized water or fresh tap water (potable water), provided with supports for the test specimens. 4.2 Oven capable of being maintained at a temperature of (50 2) C. 4.3 Balance, capable of weighing 2 000

24、g to 0,1 g. BS EN 1062-3:2008EN 1062-3:2008 (E) 6 5 Sampling Take a representative sample of the product to be tested (or of each product in the case of a multi-coat system), as described in EN ISO 15528. Examine and prepare each sample for testing, as described in EN ISO 1513. 6 Test specimens 6.1

25、General The tests shall be performed with at least three test specimens. NOTE Testing with more than three specimens is recommended to be able to eliminate outliers if there are any. A specimen consists of a substrate coated with the coating or coating system to be tested. 6.2 Substrate To determine

26、 the water transmissibility of a coating or coating system, a substrate with a massy mineral substrate shall be used with a homogeneous surface having a significantly higher water absorption than the coating or coating system to be tested. Specimens cut from calcium silicate bricks, clay bricks or m

27、ortar slabs have been found suitable for the determination of the liquid water permeability of coatings and coating systems for exterior masonry and concrete. Unless otherwise agreed, such specimens shall be used as the substrate. The specimens shall have a coefficient of liquid water permeability w

28、 of more than 1 kg/(m2x h0,5) according to EN ISO 15148. The specimens shall be at least 200 cm2in surface area and at least 2,5 cm in thickness. 6.3 Preparation and coating The specimens used as the substrate shall be clean and dry. It is important that the original porosity is taken into account b

29、y using new specimens for each determination. Coat the substrate by applying the coating or coating system to be tested in the specified quantity in accordance with the recommendations of the manufacturer of the coating material(s). The coating shall be free of visible defects. Dry the coating for a

30、t least one week. Before conditioning, seal the reverse side and the edges of the test specimens against water, for example by applying two coats of a two-component coating material based on epoxy resin, overlapping the test surface by at least 5 mm but no more than 10 mm. A thixotropic coating syst

31、em is recommended. 6.4 Drying and conditioning 6.4.1 Drying Unless otherwise agreed, dry the test specimens for a further 7 days with freely circulating air at (23 2) C and (50 5) % relative humidity (see also EN 23270). BS EN 1062-3:2008EN 1062-3:2008 (E) 7 6.4.2 Conditioning NOTE The liquid water

32、permeabilty is influenced by the volatile and/or water-soluble components of the coating. As, in practice, these components can evaporate from the coating during outdoor exposure or be washed out by water (rain), the coating is aged prior to the determination of the liquid water permeability. Subjec

33、t the test specimens to three cycles comprising the following conditions: 24 h storage in water (potable water changed for every cycle) at (23 2) C; 24 h drying at (50 2) C. If the coatings are thermoplastic at 50 C, the test specimens shall be suspended and/or suitably placed in the oven, ensuring

34、that they do not adhere to the parts of the oven and/or to each other. During weekends, or interruption for other reasons, store the test specimens in the standard atmosphere as defined in EN 23270 (23 2) C and (50 5) % relative humidity. After the last cycle store the test specimens at (50 2) C for

35、 at least 24 h. Afterwards, condition the test specimens in the standard atmosphere as defined in EN 23270 (23 2) C and (50 5) % relative humidity for at least 24 h before carrying out the test. 7 Procedure Carry out the determination at (23 2) C, unless otherwise agreed. Weigh the test specimen to

36、the nearest 0,1 g. Fill the container with deionized water or fresh tap water (potable water) and allow the temperature of the water to attain (23 2) C. Support the test specimen on a plastics or metal rack with the maximum possible area of the coated surface under test facing downwards so that this

37、 face is 5 mm to 10 mm below the surface of the water and also at least 10 mm above the base of the container. Ensure full wetting of the surface, i.e. removal of air bubbles by careful wiping with a clean damp lint free cloth or tissue 10 min after the start of the test. After 24 h remove the test

38、specimen from the water, carefully wipe it dry using absorbent paper, and weigh the test specimen to the nearest 0,1 g. NOTE Depending on the time the slope of the curve of water absorption can provide important information about the hygric behaviour of coatings. Therefore, it is recommended to meas

39、ure the water absorption after 10 min, 30 min, 1 h, 2 h, 3 h, 6 h and 24 h. 8 Expression of results The water transmissibility w, in kilograms per square metres per square root of hours, is determined by the mass increase (in kilograms) divided by the area of the test specimens (in square metres) an

40、d by the square root of time (24 h)0,5. The area shall be the area of the testing surface not covered by the overlapping sealing coating (see 6.3). For the classification according to EN 1062-1 the arithmetic mean value from at least three individual measurements shall be used. 9 Precision 9.1 Repea

41、tability The value below which the absolute difference between two single test results, each the mean of triplicates, obtained on identical material by one operator in one laboratory within a short interval of time using the BS EN 1062-3:2008EN 1062-3:2008 (E) 8 standardized test method, can be expe

42、cted to lie with a 95 % probability, is 10 % (relative to the mean of the two test results). 9.2 Reproducibility The value below which the absolute difference between two single test results, each the mean of triplicates, obtained on identical material by operators in different laboratories using th

43、e standardized test method, can be expected to lie with a 95 % probability, is 15 % (relative to the mean of the two test results). 10 Test report The test report shall contain at least the following information: a) reference to this document (EN 1062-3:2008); b) all details necessary to identify th

44、e product tested; c) number of test specimens (replicates); d) type of coating system, method of application, applied mass, number of coats, drying time; e) nature of the substrate and dimensions of the test specimens; f) results of the test, as indicated in clause 8 (individual and mean values and

45、classification according to EN 1062-1); g) particular observations; h) any deviation from the test method specified; i) date of the test. BS EN 1062-3:2008This page has been intentionally left blank BS EN1062-3:2008BSI GroupHeadquarters 389Chiswick High Road,London, W4 4AL, UKTel +44 (0)20 8996 9001

46、Fax +44 (0)20 8996 - British Standards InstitutionBSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on standards in Europe and at theinternational level. It is incorporated by Royal Charter.RevisionsBritish Standards are updated by amendment or

47、 revision. Users of BritishStandards should make sure that they possess the latest amendments oreditions.It is the constant aim of BSI to improve the quality of our products and services.We would be grateful if anyone finding an inaccuracy or ambiguity while usingthis British Standard would inform t

48、he Secretary of the technical committeeresponsible, the identity of which can be found on the inside front cover. Tel:+44 (0)20 8996 9000. Fax: +44 (0)20 8996 7400.BSI offers members an individual updating service called PLUS which ensuresthat subscribers automatically receive the latest editions of standards.Buying standardsOrders for all BSI, international and foreign standards publications should beaddressed to Customer Services. Tel: +44 (0)20 8996 9001. F