EN 172-1994 en Personal Eye Protection - Sunglare Filters for Industrial Use (Incorporates Amendments A1 2000 and A2 2001)《人眼防护 工业用遮光过滤镜 包含修改件A1-2000和A2-2001》.pdf

1、BRITISH STANDARD Personal eye protection Sunglare filters for industrial use The European Standard EN 172:1994, with the incorporation of amendments A1:2000 and A2:2001, has the status of a British Standard ICs 13.340.20 BS EN 17211995 Incorporating Amendment Nos. I and 2 Wk is the spectral distribu

2、tion of radiation of CIE standard illuminant D65; is the spectral visibility function for daylight vision; is the spectral transmittance of the signal lens; is the spectral transmittance of the sunglare filter. B.3 Infra-red transmittance The transmittance 71% is obtained by integration between the

3、limits 780 nm and 2 O00 nm based on the solar spectral distribution of radiation 2000 nm Eh x T(A) x dA J780 nm SIR = ,2000 nm The values ofE2 are given in Annex A ofprEN 165. 11 O BSI 30 January 2002 EN 172:1994 Totals a The blue flashing Annex C (normative) Standard illuminant D 100.000 o 100.000

4、o light is not based on standard illuminan The product ofthe spectral radiation distribution ofsignal lights and standard illuminant D, and spectral brightness sensitivity for daylight vision as specified in CIE Publication 15 (1971). Wavelength nm 3 80 390 400 410 420 43 O 440 450 460 470 480 490 5

5、00 510 520 530 540 550 560 570 580 590 600 610 620 63 O 640 650 660 670 680 690 700 710 720 73 O 740 750 760 770 780 SA(A) x V(A) x T,(A) in relative values Red 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.0

6、00 o 0.000 o 0.000 o 0.428 9 6.628 9 18.238 2 20.382 6 17.654 4 13.291 9 9.384 3 6.069 8 3.646 4 2.005 8 1.114 9 0.559 O 0.290 2 0.153 3 0.074 2 0.038 6 0.023 2 0.007 7 0.004 5 0.002 2 0.001 o Yellow 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.00

7、0 o 0.000 o o. 1 0.951 5 3.279 4 7.518 7 10.734 2 12.053 6 12.263 4 11.660 1 10.521 7 8.965 4 7.254 9 5.353 2 3.735 2 2.406 4 1.441 8 0.789 2 0.437 6 0.219 1 0.113 7 0.060 1 0.029 O 0.015 2 0.008 9 0.003 O 0.001 7 0.000 9 0.000 4 Green 0.000 o 0.000 o 0.001 4 0.004 7 0.017 1 0.056 9 O. 128 4 0.252 2

8、 0.485 2 0.902 1 1.671 8 2.997 6 5.355 3 9.083 2 13.018 O 14.908 5 14.762 4 12.468 7 9.406 1 6.328 1 3.896 7 2.164 O 1.127 6 0.619 4 0.296 5 0.048 1 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 0.000 o 100.000 o 4, but on the distrib

9、 Blue“ 0.000 1 0.000 8 0.004 2 0.019 4 0.088 7 0.352 8 0.867 1 1.596 1 2.638 O 4.040 5 4.902 5 7.886 2 10.156 6 13.056 O 12.836 3 9.663 7 7.206 1 5.780 6 3.254 3 1.397 5 0.848 9 1.015 5 1.002 o 0.639 6 0.325 3 0.335 8 0.969 5 2.245 4 1.359 9 0.630 8 1.216 6 1.149 3 0.712 O 0.391 8 0.205 5 0.104 9 0.

10、051 6 0.025 4 0.012 9 0.006 5 0.003 3 0.000 o 0.000 5 0.003 1 0.010 4 0.035 4 0.095 2 0.228 3 0.420 7 0.668 8 0.989 4 1.524 5 2.141 5 3.343 8 5.131 1 7.041 2 8.785 1 9.424 8 9.792 2 9.415 6 8.675 4 7.887 O 6.354 O 5.374 o 4.264 8 3.161 9 2.088 9 1.386 1 0.810 O 0.462 9 0.249 2 0.126 O 0.054 1 0.027

11、8 0.014 8 0.005 8 0.003 3 0.001 4 0.000 6 0.000 4 0.000 o 0.000 o 100.000 o ion for 3 200 K. .oo.ooo o 12 O BSI 30 January 2002 EN 172: 1994 1 Axis scales / 1 -I Bottom I register bar Split field polanzers Split field rotation I- levers Figure D.l -Apparatus for determination of axis polarization An

12、nex D (normative) Test for determining the axis of polarization D.l Apparatus Apair of individually mountedsplitJieldpolarizers. These polarizem are cut to give a +3“ to -3“ angle about the horizontal. The top and bottom halves of the polarizem are then butt jointed together and glass mounted. The p

13、olarizem are capable ofbeing rotated by means of a lever carrying a corresponding pointer. The pointer transverses a scale calibrated in degrees left or right ofzero. The split fields are illuminated from behind by a diffused light source (see Figure D. 1). D.2 Procedure Mount the sunglasses (as wor

14、n) on the apparatus, i.e. the front towards the split fields on a horizontal register bar and ensure that the split field appears in the centre of the lens by means ofvertical adjusters. For the left hand lens, move the lever from side to side until the top and bottom halves of the illuminated split

15、 field appears of equal density when viewed through the lens. Read off the pointer position to give the deviation in degrees (plus or minus) of the polarizing axis of the lens from the vertical. Repeat the procedures for the right hand lens. 13 O BSI 30 January 2002 EN 172:1994 Annex E (informative)

16、 Test for determination of fatigue of photochromic materials E.l Apparatus The source is intended to reproduce as closely as possible the spectral energy distribution ofsolar radiation defined as air mass m = 2 P. Moon, Journal ofFranklin Institute, Vol. 230 (1940), pages 583-6171 with an intensity

17、of 60 O00 lux. At present this is best realized in practice with a xenon high pressure arc lamp combined with a heat absorbing filter as indicated in Annex F. E.2 Preparation of samples Samples ofworking thickness are stored in the dark at 65 “C for one hour. The samples are subjected to tenclear-da

18、rkcycles at (23 f 5) “C. Eachcycle consists of 15 min exposure as describedin 5.3.1 and 30 min storage in the dark. The samples are then stored at (23 f 5) “C in the dark for a minimum of 48 h and not more than 96 h. The clear and dark conditions are then determined in accordance with 5.3.1. E.3 Pro

19、cedure The samples are subjected to 500 clear-dark cycles at (23 f 5) “C. Each cycle consists ofa 15 min exposure as described in 5.3.1 and a 30 min storage period in the dark. The samples are then stored in the dark for not less than 48 h and not more than 96 h at (23 f 5) “C. E.4 Evaluation Clear

20、and dark conditions are determined once again in accordance with 5.3.1. The relative change in luminous transmittance shall not be more than f5 %in the clear condition and not more than f20 %in the dark condition. The thickness of the sample shall be mentioned in the test report. Annex F (informativ

21、e) Spectral transmittance of the heat absorbing filter as specified in 5.3.1 and Annex E. This transmittance curve can be achieved using, for example, a Schott KG 2 of 3 mm thick heat absorbing filter or a Pittsburg 2043,2 mm thick heat absorbing filter. 2 m c .- E v c 0,5 - to a c O al cl3 O Wavele

22、ngth , nm Figure F. 1 14 O BSI 30 January 2002 EN 172: 1994 Annex ZA (informative) Clauses of this European Standard addressing essential requirements or other provisions of EU Directives This European Standard has been prepared under a mandate given to CEN by the European Commission and the Europea

23、n Free Trade Association and supports essential requirements of EU Directive 8 9/686/EEC. WARNING: Other requirements and other EU Directives may be applicable to the product(s) falling within the scope of this standard. The following clauses ofEN 172: 1994 and its amendment Al are likely to support

24、 requirements ofDirective 89/686/EEC, Annex II. Compliance with the clauses ofEN 172: 1994 and its amendment Al provides one with means ofconforming with the specific essential requirements of the Directive concerned and associated EFTA regulations. Table ZA. 1 EU-Directive 89/686/EEC, Annex II I Cl

25、auses of this standard 14 1.1.2 Levels and classes of protection 14 1.1.2.1 Highest level ofprotection possible 1.1.2.2 Classes ofprotection appropriate to different levels ofrisk 14.1.1, 4.1.2 1.2.1 Absence of risks and other “inherent“ nuisance factors 14.2.3 14 3.9.1 Non-ionizing radiation 15 O B

26、SI 30 January 2002 BS EN 172:1995 BSI 389 Chiswick High Road Lon don w4 4AL BSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorporated by Royal Charter. Re vi si ons British Stand

27、ards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using

28、 this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: +44 (0)20 8996 9000. Fax: +44 (0)20 8996 7400. BSI offers members an individual updating service called PLUS which ensures that subscribers aut

29、omatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: +44 (0)20 8996 9001. Fax: +44 (0)20 8996 7001. Email: orders&-. Standards are also available from the BSI website

30、at http:/www.bsi-. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and inte

31、rnational standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel: +44 (0)20 8996 71 11. Fax: +44 (0)20 8996 7048. Email: infomi-

32、. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details ofthese and other benefits contact Membership Administration. Tel: +44 (0)20 8996 7002. Fax: +44 (0)20 8996 700 1. Email: membershipbsi-. Inf

33、ormation regarding online access to British Standards via British Standards Online can be found at http:/www.bsi- Further information about BSI is available on the BSI website at http:/www.bsi-. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK, ofthe publ

34、ications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means - electronic, photocopying, recording or otherwise -without prior written

35、permission from BSI. This does not preclude the free use, in the course of implementing the standard, ofnecessary details such as symbols, and size, type or grade designations. Ifthese details are to be used for any other purpose than implementation then the prior written permission ofBSI must be obtained. Details and advice can be obtained from the Copyright & Licensing Manager. Tel: +44 (0)20 8996 7070. Fax: +44 (0)20 8996 7553. Email: copyright&-.