1、BRITISH STANDARDBS EN 1881:2006Products and systems for the protection and repair of concrete structures Test methods Testing of anchoring products by the pull-out methodThe European Standard EN 1881:2006 has the status of a British StandardICS 91.100.30g49g50g3g38g50g51g60g44g49g42g3g58g44g55g43g50
2、g56g55g3g37g54g44g3g51g40g53g48g44g54g54g44g50g49g3g40g59g38g40g51g55g3g36g54g3g51g40g53g48g44g55g55g40g39g3g37g60g3g38g50g51g60g53g44g42g43g55g3g47g36g58BS EN 1881:2006This British Standard was published under the authority of the Standards Policy and Strategy Committee on 29 December 2006 BSI 2006
3、ISBN 0 580 49827 1National forewordThis British Standard was published by BSI. It is the UK implementation of EN 1881:2006.The UK participation in its preparation was entrusted by Technical Committee B/517, Concrete, to Subcommittee B/517/8, Protection and repair of concrete structures.A list of org
4、anizations represented on B/517/8 can be obtained on request to its secretary.This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunity from legal obligations.Am
5、endments issued since publicationAmd. No. Date CommentsEUROPEAN STANDARDNORME EUROPENNEEUROPISCHE NORMEN 1881October 2006ICS 91.100.30English VersionProducts and systems for the protection and repair of concretestructures - Test methods - Testing of anchoring products by thepull-out methodProduits e
6、t systmes pour la protection et la rparation desstructures en bton - Mthodes dessais - Essaidarrachement dune armature du bton pour les produitsdancrageProdukte und Systeme fr den Schutz und dieInstandsetzung von Betontragwerken - Prfverfahren -Prfung von Verankerungsprodukten mit derAusziehprfungTh
7、is European Standard was approved by CEN on 7 September 2006.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical refere
8、nces concerning such nationalstandards may be obtained on application to the Central Secretariat or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into i
9、ts own language and notified to the Central Secretariat has the same status as the officialversions.CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxem
10、bourg, Malta, Netherlands, Norway, Poland, Portugal, Romania,Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMIT EUROPEN DE NORMALISATIONEUROPISCHES KOMITEE FR NORMUNGManagement Centre: rue de Stassart, 36 B-1050 Brussels 2006 CEN All rights
11、of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 1881:2006: EEN 1881:2006 (E) 2 Contents Page Foreword3 1 Scope 4 2 Normative references 4 3 Test principle4 4 Apparatus .4 5 Preparing for the test 5 5.1 Composition of the concrete test blocks 5 5.2
12、Preparation of moulds.5 5.3 Preparation of concrete test blocks.5 5.4 Preparing the concrete test blocks for anchoring .5 6 Procedure .6 6.1 Carrying out the anchoring operation .6 6.2 Storage of test-pieces after carrying out the anchoring operation6 6.3 Carrying out the test6 7 Test report 7 EN 18
13、81:2006 (E) 3 Foreword This document (EN 1881:2006) has been prepared by Technical Committee CEN/TC 104 “Concrete and related products”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by
14、endorsement, at the latest by April 2007, and conflicting national standards shall be withdrawn at the latest by December 2008. It has been prepared by Sub-committee SC 8 “Protection and repair of concrete structures“, the secretariat of which is held by AFNOR. This European Standard is one of a ser
15、ies dealing with products and systems for the protection and repair of concrete structures. It describes a method of test for determining the pull out resistance offered by a bonding grout or mortar used to anchor reinforcing bar. According to the CEN/CENELEC Internal Regulations, the national stand
16、ards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Ro
17、mania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom. EN 1881:2006 (E) 4 1 Scope This European Standard specifies the conditions for carrying out a pull-out test on a reinforcing steel bar (rebar) anchored in a concrete block. The test applies to products based on hydraulic binde
18、rs or synthetic resins or mixtures of these. It does not include those products intended to be used as grout around tendons used for the prestressing of concrete. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, o
19、nly the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 206-1, Concrete Part 1: Specification, performance, production and conformity EN 1766, Products and systems for the protection and repair of concrete structures
20、 Test methods Reference concretes for testing EN 10080, Steel for the reinforcement of concrete - Weldable reinforcing steel - General EN 12390-2, Testing hardened concrete Part 2: Making and curing specimens for strength tests 3 Test principle A tensile load is applied to a rebar anchored in a conc
21、rete test-piece with the product to be tested. The force and displacement of the rebar relative to the test-piece are measured. The test is performed on concrete, type C (0,40) in accordance with EN 1766. The test shall be carried out on dry and/or wet concrete, as described in 5.4.1 and 5.4.2, and
22、the product may be applied vertically, horizontally or overhead, or in any combination, as requested by the manufacturer. NOTE If a bar is tested after being installed overhead it is not necessary to carry out additional tests in the other orientations. 4 Apparatus The following apparatus is require
23、d. 4.1 One mixer for concrete. 4.2 One mixer for the product to be tested. 4.3 Moulds for the preparation of concrete blocks of minimum dimensions (400 400 250) mm. 4.4 One concrete vibrator, 25 mm diameter (EN 12390-2). 4.5 One rotary percussive drill or one diamond drill, or both, as specified by
24、the manufacturer. 4.6 Three ribbed steel bars type B500B, diameter 16 mm, with a related rib area of 0.075 to 0.085 in accordance with EN 10080 for each test. 4.7 Devices for centring and maintaining alignment of the rebars during anchoring. EN 1881:2006 (E) 5 4.8 One thermometer accurate to within
25、1 C. 4.9 One room or chamber controlled to standard laboratory climate of (21 2) C and (60 10) % RH. 4.10 A tensile testing machine of adequate capacity, capable of measuring load to an accuracy of 2 %, and fitted with a load pacer to control the rate of load increase, or deformation controlled. 4.1
26、1 A device, interlocked with the rebar and one or more displacement sensors, capable of measuring relative movement between the anchored bar and a fixed reference point on the test block to an accuracy of 0,01 mm. 5 Preparing for the test 5.1 Composition of the concrete test blocks The concrete test
27、 blocks shall be cast from concrete type C (0,40) as specified in EN 1766. 5.2 Preparation of moulds Test blocks shall be produced in a room or chamber maintained at (21 2) C. Moulds shall be non-deformable and of minimum dimensions (400 400 250) mm for a single test, or in multiples of the 400 mm d
28、imensions for more than one test. Before filling the mould the inner surface of the mould should be covered with a thin film of non reactive release material to prevent the concrete from adhering to the mould. 5.3 Preparation of concrete test blocks The concrete shall be placed and immediately compa
29、cted in three layers of approximately equal thickness and vibrated using a 25 mm diameter concrete vibrator in such a way as to produce full compaction of the concrete with neither excessive segregation nor laitance. For a block for a single test the vibratory operation shall be carried out at four
30、points, each position being equidistant and at about 125 mm from the two adjacent faces. For larger blocks with dimensions greater than (400 400 250) mm vibration shall be carried out at the same four positions, and also at intermediate points on a square grid pattern of approximately 150 mm. The vi
31、bration should be applied for the minimum time necessary for the full compaction of the concrete. The vibrator should be in a vertical position and not allowed to touch the sides or bottom of the mould. The concrete specimens shall be cured in the moulds for at least 72 h after casting at (21 2) C,
32、either under polyethylene sheeting or at not less than 95 % relative humidity, then demoulded and cured until at least 28 days after casting. During curing the test blocks shall be stored at (21 2) C, either under water for wet testing or, for dry testing, in air at a relative humidity of not less t
33、han 95 %, in accordance with EN 206-1. 5.4 Preparing the concrete test blocks for anchoring 5.4.1 Pull-out from wet concrete At least one day before the intended anchoring operation, each concrete block is removed from the water and a hole drilled by a rotary percussive or diamond drill, as specifie
34、d by the manufacturer, in the centre of the cast (400 400) mm face of the block. For larger blocks (for multiple tests) holes are drilled at a minimum distance of 200 mm from any edge and at least 400 mm from any other hole. Holes shall be drilled to a depth of (150 3) mm. The hole diameter shall be
35、 20 mm for reactive resin products and 30 mm for hydraulic cement products, unless specified otherwise by the manufacturer. Immediately after the drilling operation, the hole(s) shall be cleaned in accordance with the manufacturers instructions and filled with water for at least 24 h. The water shal
36、l then be drained and the test block shall then be placed in its required orientation in a room or chamber maintained at (21 2) C and (60 10) % relative humidity for one hour, after which time the anchoring operation shall be undertaken. EN 1881:2006 (E) 6 5.4.2 Pull-out from dry concrete Seven days
37、 before carrying out the anchoring operation, each concrete test-piece shall be removed from the humidity chamber or room and then stored in a chamber or room maintained at (21 2) C and (60 10) % relative humidity. On the day of the intended anchoring operation, a hole shall be drilled by a rotary p
38、ercussive or diamond drill, as specified by the manufacturer, in the centre of the cast (400 400) mm face of the block. For larger blocks (for multiple tests) holes are drilled at a minimum distance of 200 mm from any edge and at least 400 mm from any other hole. Holes shall be drilled to a depth of
39、 (150 3) mm. The hole diameter shall be 20 mm for reactive resin products and 30 mm for hydraulic cement products, unless specified otherwise by the manufacturer. Immediately after the drilling operation the hole(s) shall be cleaned in accordance with manufacturers instructions and the test block sh
40、all then be placed in its required orientation and the anchoring operation may be undertaken. 6 Procedure 6.1 Carrying out the anchoring operation Before use the rebars shall be prepared in accordance with manufacturers instructions; the prepared rebars, the product, and the equipment and tools requ
41、ired for mixing and placing shall be stored for at least 24 h in a room or chamber maintained at (21 2) C and (60 10) % relative humidity. The product shall be mixed and placed, and the rebars installed, strictly in accordance with the manufacturers instructions. It should be noted that the efficacy
42、 of the product is dependent on the care exercised during use, and therefore the manufacturers recommendations shall be followed. Each rebar, set to the base of its hole, shall be located and supported along the centre line of the hole by the centering devices. 6.2 Storage of test-pieces after carry
43、ing out the anchoring operation The test pieces shall be stored undisturbed for the minimum curing time recommended by the manufacturer, and then up to the time of the test, at (21 2) C and (60 10) % relative humidity. 6.3 Carrying out the test The pullout test consists of applying a tensile force t
44、o the free end of the rebar, Figure 1 gives details of a typical test rig. Before load is applied the displacement measuring device is attached to the rebar as closely as possible to the surface plane of the test block, with the sensor(s) being in contact with the surface at a distance of at least 1
45、50 mm from the rebar. Increasing tensile load is applied to the rebar, at the rate of (1,6 0,1) kN/s, until failure. The applied force and the displacement shall be measured continuously. NOTE When testing test pieces of different orientations the test piece can be rotated to a position where the pu
46、ll-out test is easier to carry out. For each test, the load/displacement behaviour and the maximum load are recorded. EN 1881:2006 (E) 7 7 Test report The test report shall include the following information: a) identification of the product; b) date and place of the test; c) the temperature and rela
47、tive humidity of the room or chamber during the test; d) the conditions for preparing the product; e) the batch number and pack size of product; f) the quantity of mixture prepared; g) the method used for mixing the constituents and the time taken; h) the time between mixing the constituents and ins
48、talling the anchor; i) the exact technique used to prepare the hole; j) the diameter and the measured depth of the hole; k) the surface condition wet or dry; l) the method used to place the anchor (pouring, pumping, ramming, etc.) and the anchor orientation (vertically downwards, horizontally, overh
49、ead); m) the time taken to place the product and install the anchors, and any difficulties encountered; n) the time period between mixing the product and testing; o) the progressive load displacement and the value of the displacement at a load of 75 kN for each test piece; p) a description of the type of failure, or combination of failure types, for each test-piece, as follows: 1) type 1: failure of the rebar; 2) type 2: extraction of the rebar from the anchoring product; 3) type 3: extraction