EN 60684-3-205-2011 en Flexible insulating sleeving - Part 3 Specifications for individual types of sleeving - Sheet 205 Heat-shrinkable chlorinated polyolefin sleeving flame retar.pdf

1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationFlexible insulating sleevingPart 3: Specifications for individual types of sleeving Sheet 205: Heat-shrinkable polychloroprene sleeving, flame retarded, shrink ratio 1,7:1BS EN 6

2、0684-3-205:2011National forewordThis British Standard is the UK implementation of EN 60684-3-205:2011. It is identical to IEC 60684-3-205:2011.The UK participation in its preparation was entrusted to Technical CommitteeGEL/15, Solid electrical insulating materials.A list of organizations represented

3、 on this committee can be obtained on request to its secretary.This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. The British Standards Institution 2012Published by BSI Standards Limited 2012 ISBN 978 0 580 6352

4、8 1 ICS 29.035.20 Compliance with a British Standard cannot confer immunity from legal obligations.This British Standard was published under the authority of the Standards Policy and Strategy Committee on 31 August 2012.Amendments issued since publicationDate Text affectedBRITISH STANDARDBS EN 60684

5、-3-205:2011EUROPEAN STANDARD EN 60684-3-205 NORME EUROPENNE EUROPISCHE NORM July 2011 CENELEC European Committee for Electrotechnical Standardization Comit Europen de Normalisation Electrotechnique Europisches Komitee fr Elektrotechnische Normung Management Centre: Avenue Marnix 17, B - 1000 Brussel

6、s 2011 CENELEC - All rights of exploitation in any form and by any means reserved worldwide for CENELEC members. Ref. No. EN 60684-3-205:2011 E ICS 29.035.20 English version Flexible insulating sleeving - Part 3: Specifications for individual types of sleeving - Sheet 205: Heat-shrinkable chlorinate

7、d polyolefin sleeving, flame retarded, nominal shrink ratio 1,7:1 and 2:1 (IEC 60684-3-205:2011) Gaines isolantes souples - Partie 3: Spcifications pour types particuliers de gaines - Feuille 205: Gaines thermortractables en polyolfine chlore, retardes la flamme, rapport de rtreint nominal de 1,7:1

8、et 2:1 (CEI 60684-3-205:2011) Isolierschluche - Teil 3: Anforderungen fr einzelne Schlauchtypen - Blatt 205: Wrmeschrumpfschluche aus chloriertem Polyolefin, flammwidrig, nominales Schrumpfverhltnis 1,7:1 und 2:1 (IEC 60684-3-205:2011) This European Standard was approved by CENELEC on 2011-07-26. CE

9、NELEC members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on

10、 application to the Central Secretariat or to any CENELEC member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CENELEC member into its own language and notified to the Central Sec

11、retariat has the same status as the official versions. CENELEC members are the national electrotechnical committees of Austria, Belgium, Bulgaria, Croatia, Cyprus, the Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg,

12、 Malta, the Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 60684-3-205:2011EN 60684-3-205:2011 - 2 - Foreword The text of document 15/626/FDIS, future edition 1 of IEC 60684-3-205, prepared by IEC TC 15, Solid electrical i

13、nsulating materials, was submitted to the IEC-CENELEC parallel vote and was approved by CENELEC as EN 60684-3-205 on 2011-07-26. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and CENELEC shall not be held responsible for ide

14、ntifying any or all such patent rights. The following dates were fixed: latest date by which the EN has to be implemented at national level by publication of an identical national standard or by endorsement (dop) 2012-04-26 latest date by which the national standards conflicting with the EN have to

15、be withdrawn (dow) 2014-07-26 Annex ZA has been added by CENELEC. _ Endorsement notice The text of the International Standard IEC 60684-3-205:2011 was approved by CENELEC as a European Standard without any modification. _ BS EN 60684-3-205:2011- 3 - EN 60684-3-205:2011 Annex ZA (normative) Normative

16、 references to international publications with their corresponding European publications The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced docum

17、ent (including any amendments) applies. NOTE When an international publication has been modified by common modifications, indicated by (mod), the relevant EN/HD applies. Publication Year Title EN/HD YearIEC 60684-1 2003 Flexible insulating sleeving - Part 1: Definitions and general requirements EN 6

18、0684-1 2003 IEC 60684-2 + corr. December + A1 + A2 1997 1997 2003 2005 Flexible insulating sleeving - Part 2: Methods of test EN 60684-2 + A1 + A2 1997 2003 2005 IEC 60757 1983 Code for designation of colours HD 457 S1 1985 ISO 846 1997 Plastics - Evaluation of the action of microorganisms EN ISO 84

19、6 1997 ISO 1817 2005 Rubber, vulcanized - Determination of the effect of liquids - - BS EN 60684-3-205:2011 2 60684-3-205 IEC:2011 CONTENTS INTRODUCTION . 5 1 Scope . . 6 2 Normative references. . 6 3 Designation . . 7 4 Conditions of test . 7 5 Requirements . 7 6 Sleeving conformance. 7 7 Breakdown

20、 voltage . 10 Table 1 Dimensional and mass requirements (nominal shrink ratio 1,7:1) . 8 Table 2 Dimensional and mass requirements (nominal shrink ratio 2:1) . 8 Table 3 Property requirements 9 Table 4 Requirements for breakdown voltage . 11 Table 5 Resistance to selected fluids 11 Table 6 Additiona

21、l property requirements . 12 BS EN 60684-3-205:201160684-3-205 IEC:2011 5 INTRODUCTION This International Standard is one of a series which deals with flexible insulating sleeving for electrical purposes. The series consists of three parts: Part 1: Definitions and general requirements (IEC 60684-1)

22、Part 2: Methods of test (IEC 60684-2) Part 3: Specifications for individual types of sleeving (IEC 60684-3) This standard gives one of the sheets comprising part 3 as follows: Sheet 205: Heat-shrinkable chlorinated polyolefin sleeving, flame retarded, nominal shrink ratio 1,7:1 and 2:1 BS EN 60684-3

23、-205:2011 6 60684-3-205 IEC:2011 FLEXIBLE INSULATING SLEEVING Part 3: Specifications for individual types of sleeving Sheet 205: Heat-shrinkable chlorinated polyolefin sleeving, flame retarded, nominal shrink ratio 1,7:1 and 2:1 1 Scope This part of IEC 60684 gives the requirements for one type of h

24、eat-shrinkable chlorinated polyolefin sleeving, flame retarded, nominal shrink ratio 1,7:1 and 2:1 for use at temperatures up to 120 C. These sleevings are normally supplied with internal diameters up to 102 mm, and the standard colour is black. Sizes or colours other than those specifically listed

25、in this standard may be available as custom items. These items shall be considered to comply with this standard if they comply with the property requirements listed in Tables 3, 4 and 5 except for dimensions and mass, and Table 6, as applicable. Materials which conform to this specification meet est

26、ablished levels of performance. However, the selection of a material by a user for a specific application should be based on the actual requirements necessary for adequate performance in that application and not based on this specification alone 2 Normative references The following referenced docume

27、nts are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. IEC 60684-1:2003, Flexible insulating sleeving Part 1: Definitions and general r

28、equirements IEC 60684-2:1997, Flexible insulating sleeving Part 2: Methods of test Amendment 1 (2003) Amendment 2 (2005) IEC 60757:1983, Code for designation of colours ISO 846:1997, Plastics Evaluation of the action of micro-organisms ISO 1817:2005, Rubber, vulcanized Determination of the effect of

29、 liquids BS EN 60684-3-205:201160684-3-205 IEC:2011 7 3 Designation The sleeving shall be identified by the following designation: Description IEC publication number IEC Part number IEC sheet number Size (expanded and recovered internal diameter in mm) Colour Sleeving IEC 60684 - 3 -205 - 12,7/6,4 -

30、 BK Any colour abbreviation shall comply with IEC 60757, where applicable. Non-standard colours shall be written out in full. 4 Conditions of test Unless otherwise specified, the sleeving shall be shrunk in a forced air circulation oven for (5 1) min at 175 C 3 K prior to testing. 5 Requirements In

31、addition to the general requirements given in IEC 60684-1, the sleeving shall comply with the requirements of Tables 1, 2, 3, 4, 5 and 6 as applicable. 6 Sleeving conformance Product conformance shall normally be based on the results from size 12,7/7,3 mm black sleeving. The colour fastness to light

32、 shall be qualified for all colours. BS EN 60684-3-205:2011 8 60684-3-205 IEC:2011 Table 1 Dimensional and mass requirements (nominal shrink ratio 1,7:1) Size code Internal diameter mm Recovered wall thickness mm Mass per unit length g/m max. Expanded min. Recovered max. 3,2/1,8 3,2 1,8 0,70 0,25 9,

33、91 4,8/2,7 4,8 2,7 0,89 0,25 16,60 6,4/3,6 6,4 3,6 0,89 0,25 20,49 9,5/5,4 9,5 5,4 1,00 0,25 31,52 12,7/7,3 12,7 7,3 1,20 0,40 54,00 15,9/9,1 15,9 9,1 1,30 0,40 69,62 19,1/10,9 19,1 10,9 1,45 0,40 86,68 22,2/12,7 22,2 12,7 1,65 0,50 121,07 25,4/14,5 25,4 14,5 1,77 0,50 144,35 31,8/18,1 31,8 18,1 2,2

34、0 0,50 250,83 38,1/21,8 38,1 21,8 2,40 0,50 271,61 44,5/25,4 44,5 25,4 2,70 0,50 347,03 50,8/29,0 50,8 29,0 2,80 0,50 404,18 76,2/43,4 76,2 43,4 3,20 0,50 660,81 101,6/57,9 101,6 57,9 3,55 0,50 951,38 Table 2 Dimensional and mass requirements (nominal shrink ratio 2:1) Size code Internal diameter mm

35、 Recovered wall thickness mm Mass per unit length g/m max. Expanded min. Recovered max. 6,4/3,2 6,4 3,2 0,89 0,25 18,76 9,5/4,8 9,5 4,8 1,00 0,25 28,68 12,7/6,4 12,7 6,4 1,20 0,40 48,54 15,9/7,9 15,9 7,9 1,30 0,40 61,88 19,1/9,5 19,1 9,5 1,40 0,40 77,13 22,2/11,1 22,2 11,1 1,65 0,50 108,02 25,4/12,7

36、 25,4 12,7 1,77 0,50 128,86 31,1/15,5 31,1 15,5 2,20 0,50 186,33 38,1/19,0 38,1 19,0 2,40 0,50 240,82 44,5/22,2 44,5 22,2 2,70 0,50 308,21 50,8/25,4 50,8 25,4 2,80 0,50 359,13 76,2/38,1 76,2 38,1 3,20 0,50 586,46 101,6/51,0 101,6 51,0 3,55 0,50 845,41 BS EN 60684-3-205:201160684-3-205 IEC:2011 9 Tab

37、le 3 Property requirements Property IEC 60684-2 Clause or subclause Units Max. or min. Requirements Remarks Dimensions internal diameter wall thickness concentricity expanded recovered 3 3.1.2 3.3.2 3.3.3 mm mm % Min. Table 1 and 2 Table 1 and 2 65 85 Heat shock 6 - - No cracking, flowing or drippin

38、g Heat at 200 C 3 K. Longitudinal change 9 % Max. + 1 - 10 Heat the expanded sleeving at 175 C 3 K for (15 1) min. Bending at low temperature 14 There shall be no signs of cracking. Test the expanded sleeving. Test temperature 70 C 3 K. For strips, the mandrel shall be no more than 10 times the wall

39、 thickness. Full section sleeving shall be tested unfilled and the mandrel shall be no more than 10 times the outer diameter. Dimensional stability on storage 16 The dimensions shall be as specified in Table 1. Tensile strength Elongation at break 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 10 225 R

40、ate of jaw separation 100 mm/min. Below 6,5 mm diameter as sleeving; at 6,5 mm diameter and above as dumb-bells. Tensile stress at 200 % Elongation 19.5 aMPa Max. 10,3 Breakdown voltage 21 kV Min. Table 4 Volume resistivity at room temperature 23 23.4.2 cm Min. 1011Flame propagation Time of burning

41、Length burned 26 Method C s mm Max. Max. 15 75 aUse the test procedure from 19.5, but measure the elongation at 200 %. BS EN 60684-3-205:2011 10 60684-3-205 IEC:2011 Table 3 (continued) Property IEC 60684-2 Clause or subclause Units Max. or min. Requirements Remarks Copper corrosion 33 % Max. None a

42、bove the allowable 8 % Heat for (16 0,5) h at 150 C 3 K. Colour fastness to light 34 The colour contrast between the exposed and unexposed parts of the specimens shall be equal to or less than that of the fastness standard Fastness standard No. 5 Resistance to selected fluids Tensile strength Elonga

43、tion at break 36 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 6,9 175 Use the fluids and test temperatures specified in Table 5. Mass per unit length 38 g/m Max. Table 1 and 2 Heat ageing Tensile strength Elongation at break 39 19.1 and 19.2 19.1 and 19.2 MPa % Min. Min. 8,2 175 Heat at 120 C 5 K. Wa

44、ter absorption 40 % Max. 1,0 Restricted shrinkage 41 _ kV _ Min. No cracking or splitting 2 Heat the specimens at 135 C. Long term ageing Elongation 50 19.1 and 19.2 % Min. 175 The ageing temperature shall be 120 C. 7 Breakdown voltage The breakdown voltage shall be determined by any of the methods

45、described in 21.2, 21.3 or 21.4 of IEC 60684-2. The central value shall comply with the minimum value in Table 4. The rate of application of the voltage shall be 500 V/s. BS EN 60684-3-205:201160684-3-205 IEC:2011 11 Table 4 Requirements for breakdown voltage Nominal recovered wall thickness amm Bre

46、akdown voltage min. kV 0,70 0,89 1,00 1,20 1,30 1,40 1,65 1,77 2,20 2,40 2,70 2,80 3,20 3,55 8,3 10,7 12,0 14,4 15,6 16,8 19,8 14,0 17,6 19,2 21,6 22,4 25,6 28,4 aFor non-standard wall thicknesses, the electric strength shall be at least that of the next smallest standard wall thickness. For wall th

47、icknesses smaller than 0,69 mm, the electric strength shall be at least 12,0 kV/mm. Table 5 Resistance to selected fluids Fluids Type Standard or symbol Immersion temperature C 2 K Fuels Gasoline ISO 1817 Liquid B 23 Kerosene ISO 1817 Liquid F 23 Hydraulic fluids Silicone base S-1714a23 Mineral base

48、 H-520a23 Oils Synthetic base ISO 1817 Liquid 101 23 Mineral base ISO 1817 Oil no. 2 23 Mineral base O-1176a23 Mineral base O-142a23 Cleaning fluids Solvent Isopropyl alcohol 23 Propanol 25 % White spirit 75 % 23 De-icing fluids Runway de-icers Inhibited potassium acetate in water, 50 % 23 Aircraft

49、de-icers Ethylene glycol 80 % Water 20 % 23 aThese are commercially available fluids which can be identified in aviation fluid guides. NOTE Other fluids and/or temperatures may be specified with specific needs. These additional fluids and/or temperatures should be applicable when incorporated into agreements between the supplier and customer