EN 62329-3-101-2010 en Heat-shrinkable moulded shapes - Part 3 Specification requirements for shape dimensions material requirements and compatibility performance - Sheet 101 Heat-.pdf

1、raising standards worldwideNO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAWBSI Standards PublicationHeat-shrinkable moulded shapesPart 3: Specification requirements for shape dimensions, material requirements and compatibility performanceSheet 101: Heat-shrinkable moulded shape

2、s, polyolefin, semi-rigid, limited fire hazard, material requirements and system performanceBS EN 62329-3-101:2010National forewordThis British Standard is the UK implementation of EN 62329-3-101:2010. It isidentical to IEC 62329-3-101:2010.The UK participation in its preparation was entrusted to Te

3、chnical CommitteeGEL/15, Solid electrical insulating materials.A list of organizations represented on this committee can be obtained onrequest to its secretary.This publication does not purport to include all the necessary provisions of acontract. Users are responsible for its correct application. B

4、SI 2011 ISBN 978 0 580 58368 1 ICS 29.035.01Compliance with a British Standard cannot confer immunity from legal obligations.This British Standard was published under the authority of the Standards Policy and Strategy Committee on 28 February 2011.Amendments issued since publicationAmd. No. Date Tex

5、t affectedBRITISH STANDARDBS EN 62329-3-101:2010EUROPEAN STANDARD EN 62329-3-101 NORME EUROPENNE EUROPISCHE NORM September 2010 CENELEC European Committee for Electrotechnical Standardization Comit Europen de Normalisation Electrotechnique Europisches Komitee fr Elektrotechnische Normung Management

6、Centre: Avenue Marnix 17, B - 1000 Brussels 2010 CENELEC - All rights of exploitation in any form and by any means reserved worldwide for CENELEC members. Ref. No. EN 62329-3-101:2010 E ICS 29.035.01 English version Heat-shrinkable moulded shapes - Part 3: Specification requirements for shape dimens

7、ions, material requirements and compatibility performance - Sheet 101: Heat-shrinkable moulded shapes, polyolefin, semi-rigid, limited fire hazard, material requirements and system performance (IEC 62329-3-101:2010) Profils thermortractables - Partie 3: Exigences relatives aux dimensions des profils

8、, exigences de matriaux et performances de compatibilit - Feuille 101: Profils thermortractables, exigences relatives aux matriaux semi-rigides en polyolfine, risque de feu limit et performances du systme (CEI 62329-3-101:2010) Wrmeschrumpfende Formteile - Teil 3: Anforderungen fr Formteilmae, Mater

9、ialeigenschaften und Kompatibilittsverhalten - Blatt 101: Wrmeschrumpfende Formteile aus Polyolefin, halbsteif, flammwidrig, Materialanforderungen und Systemeigenschaften (IEC 62329-3-101:2010) This European Standard was approved by CENELEC on 2010-09-01. CENELEC members are bound to comply with the

10、 CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the Central Secretariat or

11、 to any CENELEC member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CENELEC member into its own language and notified to the Central Secretariat has the same status as the offici

12、al versions. CENELEC members are the national electrotechnical committees of Austria, Belgium, Bulgaria, Croatia, Cyprus, the Czech Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, the Netherlands, Norway, Poland, P

13、ortugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and the United Kingdom. BS EN 62329-3-101:2010EN 62329-3-101:2010 Foreword The text of document 15/569/FDIS, future edition 1 of IEC 62329-3-101, prepared by IEC TC 15, Solid electrical insulating materials, was submitted to the IEC-CE

14、NELEC parallel vote and was approved by CENELEC as EN 62329-3-101 on 2010-09-01. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and CENELEC shall not be held responsible for identifying any or all such patent rights. The foll

15、owing dates were fixed: latest date by which the EN has to be implemented at national level by publication of an identical national standard or by endorsement (dop) 2011-06-01 latest date by which the national standards conflicting with the EN have to be withdrawn (dow) 2013-09-01 Annex ZA has been

16、added by CENELEC. _ Endorsement notice The text of the International Standard IEC 62329-3-101:2010 was approved by CENELEC as a European Standard without any modification. In the official version, for Bibliography, the following note has to be added for the standard indicated: IEC 60684-3-216 NOTE H

17、armonized as EN 60684-3-216. _ BS EN 62329-3-101:2010EN 62329-3-101:2010 Annex ZA (normative) Normative references to international publications with their corresponding European publications The following referenced documents are indispensable for the application of this document. For dated referen

18、ces, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. NOTE When an international publication has been modified by common modifications, indicated by (mod), the relevant EN/HD applies. Publication Year Title EN/H

19、D Year IEC 60695-11-10 - Fire hazard testing - Part 11-10: Test flames - 50 W horizontal and vertical flame test methods EN 60695-11-10 - IEC 60757 1983 Code for designation of colours HD 457 S1 1985 IEC 62329-1 - Heat shrinkable moulded shapes - Part 1: Definitions and general requirements EN 62329

20、-1 - IEC 62329-2 2006 Heat shrinkable moulded shapes - Part 2: Methods of test EN 62329-2 2006 IEC 62329-3-100 2010 Heat-shrinkable moulded shapes - Part 3: Specification requirements for shape dimensions, material requirements and compatibility performance - Sheet 100: Heat-shrinkable moulded shape

21、 dimensions EN 62329-3-100 2010 ISO 1817 2005 Rubber, vulcanized - Determination of the effect of liquids - - BS EN 62329-3-101:201062329-3-101 IEC:2010 CONTENTS INTRODUCTION.5 1 Scope.6 2 Normative references6 3 Designation 7 4 Conditions of test for the moulded shapes.7 5 Requirements .7 6 Moulded

22、 shapes material conformance .7 7 Moulded shapes compatibility .7 Annex A (informative) Adhesive compatibility guide for sheet 101 moulded shapes . 11 Bibliography 12 Table 1 Property requirements .8 Table 2 Resistance to selected fluids10 BS EN 62329-3-101:201062329-3-101 IEC:2010 5 INTRODUCTION Th

23、is International Standard is one of a series that deals with heat-shrinkable moulded shapes for electrical purposes. The series consists of three parts: Part 1: Definitions and general requirements (IEC 62329-1) Part 2: Methods of test (IEC 62329-2) Part 3: Specification requirements for moulded sha

24、pe dimensions, material requirements and compatibility performance (IEC 62329-3) This standard gives one of the sheets comprising Part 3 as follows: Sheet 101: Heat-shrinkable moulded shapes, polyolefin, semi-rigid, limited fire hazard, material requirements and system performance NOTE See IEC 62329

25、-3-100 for moulded shape dimensions. BS EN 62329-3-101:2010 6 62329-3-101 IEC:2010 HEAT-SHRINKABLE MOULDED SHAPES Part 3: Specification requirements for shape dimensions, material requirements and compatibility performance Sheet 101: Heat-shrinkable moulded shapes, polyolefin, semi-rigid, limited fi

26、re hazard, material requirements and system performance 1 Scope This sheet of IEC 62329-3 gives the requirements for heat-shrinkable moulded shapes, polyolefin, semi-rigid, limited fire hazard, material requirements and system performance. Experience of product performance indicates that this moulde

27、d shape material is suitable for inclusion in systems for operation in the following temperature range: 30 C to + 105 C. The moulded shapes may be supplied with a pre-coated adhesive. Refer to the manufacturers/suppliers for options. A guide to adhesive compatibility is given in Annex A. These mould

28、ed shapes are normally supplied in the styles and dimensions given in IEC 62329-3-100. The colour is normally black. Styles and dimensions other than those specifically listed in IEC 62329-3-100 may be available as custom items. These items shall be considered to comply with this standard if they co

29、mply with the property requirements listed in Table 1 with the exception of dimensions. Materials that conform to this specification meet established levels of performance. However, the selection of a material by a user for a specific application should be based on the actual requirements necessary

30、for adequate performance in that application and not based on this specification alone. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition o

31、f the referenced document (including any amendments) applies IEC 60695-11-10, Fire hazard testing Part 11-10: Test flames 50 W horizontal and vertical flame test methods IEC 62329-1, Heat-shrinkable moulded shapes Part 1: Definitions and general requirements IEC 62329-2:2006, Heat-shrinkable moulded

32、 shapes Part 2: Methods of test IEC 62329-3-100:2010, Heat-shrinkable moulded shapes Part 3: Specification requirements for shape dimensions, material requirements and compatibility performance Sheet 100: Heat-shrinkable moulded shape dimensions IEC 60757:1983, Code for designation of colours ISO 18

33、17: 2005, Rubber, vulcanized - Determination of the effect of liquids BS EN 62329-3-101:201062329-3-101 IEC:2010 7 3 Designation The moulded shapes shall be designated as shown by the following example: Description IEC publication number IEC Part number IEC Sheet number IEC Style/size code Colour Ad

34、hesive code (see NOTE) a Drain holes b Moulded shapes IEC 62329 3 101 B/01 BK W1 D a Insert UN if uncoated. b Insert N if no drain holes. NOTE For compatible adhesives and codes, see Annex A. Any abbreviation for colour shall comply with IEC 60757. Where no abbreviation is given, the colour shall be

35、 written in full. 4 Conditions of test for the moulded shapes The moulded shapes shall be shrunk in a forced air circulation oven for (10 1 ) min at the temperature specified in Table 1. 5 Requirements In addition to the general requirements given in IEC 62329-1, the heat-shrinkable moulded shapes s

36、hall comply with the dimensional requirements given in IEC 62329-3-100 and Table 1. 6 Moulded shapes material conformance Conformance with the requirements of this specification shall be based on the results form test sheets, ( 2 0,15 ) mm thick, unless otherwise specified1, which shall be prepared

37、from the same cross-linked heat-shrinkable material that is used to manufacture the heat-shrinkable moulded shapes. 7 Moulded shapes compatibility Conformance with the compatibility requirements of this specification shall be based on the results from the assembly configuration as shown in Figure 3

38、of IEC 62329-2. _ 1A suitable size has been found to be 150 mm 150 mm. BS EN 62329-3-101:2010 8 62329-3-101 IEC:2010 Table 1 Property requirements Property IEC 62329-2 clause or subclause Units Max. or Min. Requirements Remarks Heat shock Tensile strength Elongation at break 7 10 10 MPa % Min. Min.

39、5 100 Heat at 175C 3 K Bending at low temperature 8 No cracks shall be visible Condition at -30 C 2 K. Mandrel diameter shall be 20 mm 10+mm. Dimensional stability on storage 9 The dimensions shall be as specified in Tables 1 to 22 IEC 62329-3-100 Recovery conditions as Clause 4 for dimensions Tensi

40、le strength Elongation at break 10 10 MPa % Min. Min. 7 200 Use a jaw separation rate of 100 mm/min. Secant modulus at 2 % elongation 11 MPa 50 to 130 Electric strength 12 MV/m Min. 8 Volume resistivity after damp heat 13 m Min. 1010 Flammability 16 s Max. 30 Test in accordance with method A of IEC

41、60695-11-10 Copper corrosion 18 % Max. None above the allowable 8 Heat for (16 0,5 ) h at 150 C 3K Resistance to selected fluids Tensile strength Elongation at break 20 10 10 MPa % Min. Min. 4 100 Use the fluids and test temperatures specified in Table 2. Heat ageing Tensile strength Elongation at b

42、reak 23 10 10 MPa % Min. Min. 5 100 Heat at 150 C 3K Water absorption 24 % Max. 0,5 Mould growth Tensile strength Elongation at break 30 10 10 MPa % Min. Min. 7 200 Method B 56 days exposure Long term heat ageing Elongation at break 21 10 % Min. 100 Heat for (3000 5) h at 105 C 3 K Oxygen index 17.1

43、 Min. 29 Temperature index 17.2 C Min. 250 Smoke index 26 Max. 20 Toxicity index 27 Max. 5 Halogen content 28 28.1 28.2 % % Max. Max. 0,2 0,1 Expressed as chlorine Acid gas generation Conductivity 29 29.2 pH pH S/mm Min. Max. Max. 3,5 10,5 10,0 BS EN 62329-3-101:201062329-3-101 IEC:2010 9 Property I

44、EC 62329-2 clause or subclause Units Max. or Min. Requirements Remarks Compatibility Adhesive type 31 W1aTest at C 3K Dynamic shear At room temperature 31.1 N Min. 300 23 At elevated temperature 31.1.7 N Min. 30 105 Static load 31.2 kg Min. 10 23 At elevated temperature 31.1 N 0,5 105 Dynamic shear

45、Min. 300 23 Fluid type Standard or symbol (24 0,5) h immersion at C 2K Kerosene fuel F34 23 Grease G 354 23 Oil 0-156 23 Fluid resistance 31.3 N Min. 150 Water 23 Thermal ageing 31.4 N Min. 300 Heat for (168 1 ) h at 100 C 3 K Peel adhesion 31.5 N/25mm Min. 60 Altitude immersion 31.6 Min. 109 aThese

46、 system performance requirements are based on using W1 adhesive (see Annex A). When using other adhesives the performance may be different. Refer to the supplier/manufacturer. BS EN 62329-3-101:2010 10 62329-3-101 IEC:2010 Table 2 Resistance to selected fluids Fluids Type Standard or symbol Immersio

47、n temperature C 2K Gasoline ISO 1817 Liquid B 23 Fuels Kerosene ISO 1817 Liquid F 23 Phosphate base ISO 1817 Liquid 103 23 Silicone base S-1714 a23 Hydraulic fluids Mineral base H-520 a23 Synthetic base ISO 1817 Liquid 101 23 Mineral base ISO 1817 Oil No. 2 23 Mineral base O-1176 a23 Oils Mineral ba

48、se O-142 a23 Isopropyl alcohol 23 Propanol 25% White spirit 75% 23 Cleaning fluids Solvent Methylethylketone 23 Runway de-icers Inhibited potassium acetate in water, 50% 23 De-icing fluids Aircraft de-icers Ethylene glycol 80% Water 20% 23 NOTE Other fluids and/or temperatures may be specified with

49、specific needs. These additional fluids and/or temperatures should be applicable when incorporated into agreements between the supplier and customer. aThese are commercially available fluids which can be identified in aviation fluid guides.BS EN 62329-3-101:201062329-3-101 IEC:2010 11 Annex A (informative) Adhesive compatibility guide for sheet 101 moulded shapes Bon