EN ISO 14692-2-2017 en Petroleum and natural gas industries - Glass-reinforced plastics (GRP) piping - Part 2 Qualification and manufacture.pdf

1、Petroleum and natural gas industries - Glass-reinforced plastics (GRP) pipingPart 2: Qualification and manufactureBS EN ISO 146922:2017BSI Standards PublicationWB11885_BSI_StandardCovs_2013_AW.indd 1 15/05/2013 15:06EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN ISO 14692-2 September 2017 ICS

2、75.200; 83.140.30 Supersedes EN ISO 14692-2:2002English Version Petroleum and natural gas industries - Glass-reinforced plastics (GRP) piping - Part 2: Qualification and manufacture (ISO 14692-2:2017) Industries du ptrole et du gaz naturel - Canalisations en plastique renforc de verre (PRV) - Partie

3、 2: Conformit aux exigences de performance et fabrication (ISO 14692-2:2017) Erdl- und Erdgasindustrie - Glasfaserverstrkte Kunststoffrohrleitungen (GFK) - Teil 2: Zulassung und Herstellung (ISO 14692-2:2017) This European Standard was approved by CEN on 22 June 2017. CEN members are bound to comply

4、 with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC M

5、anagement Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same

6、 status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg,

7、Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Bruss

8、els 2017 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 14692-2:2017 ENational forewordThis British Standard is the UK implementation of EN ISO 146922:2017. It is identical to ISO 146922:2017. It supersedes BS EN ISO 146922:20

9、02, which is withdrawn.The UK participation in its preparation was entrusted to Technical Committee PSE/17/6, Processing equipment and systems for petroleum and natural gas industries.A list of organizations represented on this committee can be obtained on request to its secretary.This publication d

10、oes not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. The British Standards Institution 2017 Published by BSI Standards Limited 2017ISBN 978 0 580 92673 0ICS 83.140.30; 75.200Compliance with a British Standard cannot confer immunity

11、 from legal obligations.This British Standard was published under the authority of the Standards Policy and Strategy Committee on 31 October 2017.Amendments/corrigenda issued since publicationDate Text affected BRITISH STANDARDBS EN ISO 146922:2017EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORMEN

12、ISO 14692-2 September 2017 ICS 75.200; 83.140.30 Supersedes EN ISO 14692-2:2002English Version Petroleum and natural gas industries - Glass-reinforced plastics (GRP) piping - Part 2: Qualification and manufacture (ISO 14692-2:2017) Industries du ptrole et du gaz naturel - Canalisations en plastique

13、renforc de verre (PRV) - Partie 2: Conformit aux exigences de performance et fabrication (ISO 14692-2:2017) Erdl- und Erdgasindustrie - Glasfaserverstrkte Kunststoffrohrleitungen (GFK) - Teil 2: Zulassung und Herstellung (ISO 14692-2:2017) This European Standard was approved by CEN on 22 June 2017.

14、CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on a

15、pplication to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC

16、 Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy,

17、Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre:

18、 Avenue Marnix 17, B-1000 Brussels 2017 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 14692-2:2017 EBS EN ISO 146922:2017EN ISO 14692-2:2017 (E) 3 European foreword This document (EN ISO 14692-2:2017) has been prepared by Tec

19、hnical Committee ISO/TC 67 “Materials, equipment and offshore structures for petroleum, petrochemical and natural gas industries“ in collaboration with Technical Committee CEN/TC 12 “Materials, equipment and offshore structures for petroleum, petrochemical and natural gas industries” the secretariat

20、 of which is held by NEN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by March 2018 and conflicting national standards shall be withdrawn at the latest by March 2018. Attention is drawn to the po

21、ssibility that some of the elements of this document may be the subject of patent rights. CEN shall not be held responsible for identifying any or all such patent rights. This document supersedes EN ISO 14692-2:2002. According to the CEN-CENELEC Internal Regulations, the national standards organizat

22、ions of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malt

23、a, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. Endorsement notice The text of ISO 14692-2:2017 has been approved by CEN as EN ISO 14692-2:2017 without any modification. ISO 14692-2:2017(E)Foreword vIntroductio

24、n vi1 Scope . 12 Normative references 13 Terms, definitions, symbols and abbreviated terms . 24 Manufacturers declarations 24.1 Procedure 24.2 Long term regression testing 44.3 Gradient, Gxx54.4 MPRxx. 54.5 Partial factors . 54.5.1 Partial factor for design lifetime, A054.5.2 Partial factor for chem

25、ical degradation, A2. 54.5.3 Partial factor for cyclic loading, A3. 64.6 Long term envelope data points 64.7 Dimensions . 64.8 Baseline values 64.9 Flexibility factors and SIFs 74.10 Production processes and jointing instructions 75 Qualification programme 75.1 General . 75.2 Scaling rules. 95.3 Pro

26、duct qualification 105.3.1 Validation of long term envelopes . 105.3.2 Density . 105.3.3 Thermal expansion coefficient . 105.3.4 Qualification procedure for external pressure 105.4 Elastic properties . 105.4.1 General. 105.4.2 Axial tensile modulus, Ea. 125.4.3 Hoop tensile modulus, Eh, and minor Po

27、issons ratio, ah.125.4.4 Major Poissons ratio, ha. 125.4.5 Circumferential bending modulus, Ehb135.5 Optional qualification requirements . 135.5.1 Electrical conductivity .135.5.2 Potable water certification . 135.5.3 Impact resistance .135.5.4 Qualification procedure for fire performance .135.5.5 L

28、ow temperature performance 136 Requalification 147 Quality programme for manufacture .157.1 General requirements 157.2 Quality control tests 167.2.1 General. 167.2.2 Mill hydrostatic test for pipes 167.2.3 Mill hydrostatic test for spoolpieces 177.2.4 Degree of cure .177.2.5 Barcol hardness .177.2.6

29、 Glass content 187.2.7 Visual inspection .187.2.8 Key component dimensions 187.2.9 Retest 19 ISO 2017 All rights reserved iiiContents PageBS EN ISO 146922:2017ISO 14692-2:2017(E)Foreword vIntroduction vi1 Scope . 12 Normative references 13 Terms, definitions, symbols and abbreviated terms . 24 Manuf

30、acturers declarations 24.1 Procedure 24.2 Long term regression testing 44.3 Gradient, Gxx54.4 MPRxx. 54.5 Partial factors . 54.5.1 Partial factor for design lifetime, A054.5.2 Partial factor for chemical degradation, A2. 54.5.3 Partial factor for cyclic loading, A3. 64.6 Long term envelope data poin

31、ts 64.7 Dimensions . 64.8 Baseline values 64.9 Flexibility factors and SIFs 74.10 Production processes and jointing instructions 75 Qualification programme 75.1 General . 75.2 Scaling rules. 95.3 Product qualification 105.3.1 Validation of long term envelopes . 105.3.2 Density . 105.3.3 Thermal expa

32、nsion coefficient . 105.3.4 Qualification procedure for external pressure 105.4 Elastic properties . 105.4.1 General. 105.4.2 Axial tensile modulus, Ea. 125.4.3 Hoop tensile modulus, Eh, and minor Poissons ratio, ah.125.4.4 Major Poissons ratio, ha. 125.4.5 Circumferential bending modulus, Ehb135.5

33、Optional qualification requirements . 135.5.1 Electrical conductivity .135.5.2 Potable water certification . 135.5.3 Impact resistance .135.5.4 Qualification procedure for fire performance .135.5.5 Low temperature performance 136 Requalification 147 Quality programme for manufacture .157.1 General r

34、equirements 157.2 Quality control tests 167.2.1 General. 167.2.2 Mill hydrostatic test for pipes 167.2.3 Mill hydrostatic test for spoolpieces 177.2.4 Degree of cure .177.2.5 Barcol hardness .177.2.6 Glass content 187.2.7 Visual inspection .187.2.8 Key component dimensions 187.2.9 Retest 19 ISO 2017

35、 All rights reserved iiiContents PageBS EN ISO 146922:2017ISO 14692-2:2017(E)7.2.9 7.2.9 .Retest 197.3 Optional quality control tests 207.3.1 Electrical conductivity per length 207.3.2 Fire performance 217.3.3 Residual styrene monomer content .217.3.4 Additional quality control tests 218 Component m

36、arking 229 Handling, storage and transportation.2210 Documentation 2210.1 General 2210.2 Enquiry and purchase order documentation 2210.3 Qualification documentation . 2210.3.1 General. 2210.3.2 Qualification reports2210.3.3 Potable water approval certificates 2310.4 Production quality control docume

37、ntation . 2310.4.1 General. 2310.4.2 Manufacturing procedure . 2310.4.3 Raw material certificates . 2310.4.4 Production quality control reports . 2310.5 Installation documentation . 23Annex A (normative) Gradients and temperature limits .24Annex B (normative) Long term envelope data points .29Annex

38、C (normative) Survival tests .34Annex D (normative) Scaling rules 39Annex E (normative) Representative products 50Annex F (normative) Flange qualification .53Annex G (normative) Major Poissons ratio .56Annex H (normative) Fire endurance testing .59Annex I (normative) Alternate material qualification

39、 68Annex J (normative) Visual inspection 74Annex K (informative) Example of qualification summary form .78Bibliography .80iv ISO 2017 All rights reservedBS EN ISO 146922:2017ISO 14692-2:2017(E)7.2.9 7.2.9 .Retest 197.3 Optional quality control tests 207.3.1 Electrical conductivity per length 207.3.2

40、 Fire performance 217.3.3 Residual styrene monomer content .217.3.4 Additional quality control tests 218 Component marking 229 Handling, storage and transportation.2210 Documentation 2210.1 General 2210.2 Enquiry and purchase order documentation 2210.3 Qualification documentation . 2210.3.1 General.

41、 2210.3.2 Qualification reports2210.3.3 Potable water approval certificates 2310.4 Production quality control documentation . 2310.4.1 General. 2310.4.2 Manufacturing procedure . 2310.4.3 Raw material certificates . 2310.4.4 Production quality control reports . 2310.5 Installation documentation . 23

42、Annex A (normative) Gradients and temperature limits .24Annex B (normative) Long term envelope data points .29Annex C (normative) Survival tests .34Annex D (normative) Scaling rules 39Annex E (normative) Representative products 50Annex F (normative) Flange qualification .53Annex G (normative) Major

43、Poissons ratio .56Annex H (normative) Fire endurance testing .59Annex I (normative) Alternate material qualification 68Annex J (normative) Visual inspection 74Annex K (informative) Example of qualification summary form .78Bibliography .80iv ISO 2017 All rights reserved ISO 14692-2:2017(E)ForewordISO

44、 (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical com

45、mittee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrot

46、echnical standardization.The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the different types of ISO documents should be noted. This document was draft

47、ed in accordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent righ

48、ts. Details of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see www.iso.org/patents).Any trade name used in this document is information given for the convenience of users and does not constitu

49、te an endorsement.For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following URL: www.iso.org/iso/foreword.html.This document was prepared by Technical Committee ISO/TC 67, Materials, equipment and offshore structures for petroleum, petrochemical and natural gas industries, Subcommittee SC 6, Proce