EN ISO 16120-2-2017 en Non-alloy steel wire rod for conversion to wire - Part 2 Specific requirements for general purpose wire rod《非合金钢线材转换为线-第2部分 通用线材的具体要求》.pdf

1、BS EN ISO 16120-2:2017Non-alloy steel wire rod forconversion to wirePart 2: Specific requirements for generalpurpose wire rod (ISO 16120-2:2017)BSI Standards PublicationWB11885_BSI_StandardCovs_2013_AW.indd 1 15/05/2013 15:06BS EN ISO 16120-2:2017 BRITISH STANDARDNational forewordThis British Standa

2、rd is the UK implementation of EN ISO 16120-2:2017. It supersedes BS EN ISO 16120-2:2011 which iswithdrawn.The UK participation in its preparation was entrusted to Technical Committee ISE/106, Wire Rod and Wire.A list of organizations represented on this committee can be obtained on request to its s

3、ecretary.This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. The British Standards Institution 2017.Published by BSI Standards Limited 2017ISBN 978 0 580 83834 7 ICS 77.140.65; 77.140.60 Compliance with a British

4、 Standard cannot confer immunity from legal obligations.This British Standard was published under the authority of the Standards Policy and Strategy Committee on 28 February 2017.Amendments/corrigenda issued since publicationDate T e x t a f f e c t e dEUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NO

5、RM EN ISO 16120-2 February 2017 ICS 77.140.60 Supersedes EN ISO 16120-2:2011English Version Non-alloy steel wire rod for conversion to wire - Part 2: Specific requirements for general purpose wire rod (ISO 16120-2:2017) Fil-machine en acier non alli destin la fabrication de fils - Partie 2: Exigence

6、s spcifiques au fil-machine dusage gnral (ISO 16120-2:2017) Walzdraht aus unlegiertem Stahl zum Ziehen - Teil 2: Besondere Anforderungen an Walzdraht fr allgemeine Verwendung (ISO 16120-2:2017) This European Standard was approved by CEN on 15 February 2017. CEN members are bound to comply with the C

7、EN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national standards may be obtained on application to the CEN-CENELEC Management C

8、entre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same status as

9、the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Neth

10、erlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMUNG CEN-CENELEC Management Centre: Avenue Marnix 17, B-1000 Brussels 2017 CE

11、N All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN ISO 16120-2:2017 EBS EN ISO 16120-2:2017EN ISO 16120-2:2017 (E) 3 European foreword This document (EN ISO 16120-2:2017) has been prepared by Technical Committee ISO/TC 17 “Steel” in col

12、laboration with Technical Committee ECISS/TC 106 “Wire rod and wires” the secretariat of which is held by AFNOR. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by August 2017, and conflicting nation

13、al standards shall be withdrawn at the latest by August 2017. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be held responsible for identifying any or all such patent rights. This document supersedes

14、 EN ISO 16120-2:2011. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of

15、Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. Endorsement notice The text of ISO 16120-2:2017 has been

16、approved by CEN as EN ISO 16120-2:2017 without any modification. BS EN ISO 16120-2:2017ISO 16120-2:2017(E)Foreword iv1 Scope . 12 Normative references 13 Terms and definitions . 14 Designation 15 Requirements 25.1 General . 25.2 Chemical composition 25.3 Internal soundness and surface quality 45.4 D

17、epth of surface discontinuities 45.5 Core segregation 45.6 Tensile strength 45.7 Scale characteristics . 55.8 Mechanical damage . 5Annex A (informative) Steel designations and designation of comparable steel grades . 6Bibliography 8 ISO 2017 All rights reserved iiiContents PageBS EN ISO 16120-2:2017

18、ISO 16120-2:2017(E)ForewordISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a sub

19、ject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (I

20、EC) on all matters of electrotechnical standardization.The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the different types of ISO documents should be

21、noted. This document was drafted in accordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identi

22、fying any or all such patent rights. Details of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see www .iso .org/ patents).Any trade name used in this document is information given for the conven

23、ience of users and does not constitute an endorsement.For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see th

24、e following URL: www .iso .org/ iso/ foreword .html.This document was prepared by Technical Committee ISO/TC 17, Steel, Subcommittee SC 17, Steel wire rod and wire products.This third edition cancels and replaces the second edition (ISO 16120-2:2011), which has been technically revised.A list of all

25、 parts in the ISO 16120 series can be found on the ISO website.iv ISO 2017 All rights reservedBS EN ISO 16120-2:2017INTERNATIONAL STANDARD ISO 16120-2:2017(E)Non-alloy steel wire rod for conversion to wire Part 2: Specific requirements for general purpose wire rod1 ScopeThis document is applicable t

26、o general purpose steel wire rod for drawing and/or cold rolling.2 Normative referencesThe following documents are referred to in the text in such a way that some or all of their content constitutes requirements of this document. For dated references, only the edition cited applies. For undated refe

27、rences, the latest edition of the referenced document (including any amendments) applies.ISO 4948-2, Steels Classification Part 2: Classification of unalloyed and alloy steels according to main quality classes and main property or application characteristicsISO 16120-1:,1)Non-alloy steel wire rod fo

28、r conversion to wire Part 1: General requirements3 Terms and definitionsNo terms and definitions are listed in this document.ISO and IEC maintain terminological databases for use in standardization at the following addresses: IEC Electropedia: available at h t t p :/ www .electropedia .org/ ISO Onli

29、ne browsing platform: available at h t t p :/ www .iso .org/ obp4 DesignationIn the designation C#D, “C” means non-alloy steel (see ISO/TS 4949); # is the indicative average content of carbon; “D” signifies that it is for wire-drawing.If steels are ordered according to chemical composition, # indica

30、tes the values to be inserted by the purchaser according to the steel names designated in Table 1, first column.The designations of comparable steel grades in national or regional standards are provided in Annex A.Steels can also be ordered according to tensile strength. The mid-point of the require

31、d ultimate tensile strength (UTS) range shall be indicated as a suffix to the grade designation, e.g. C#D 1020, where the required mid-point of the UTS is 1 020 MPa. “#” means “to be left blank” since the carbon content is at the discretion of the supplying mill, and the supplying mill indicates the

32、 exact number of # based on the grade designation until shipment. See Table 1 for the grade designation.1) Under preparation. Stage at the time of publication: ISO/FDIS 16120-1:2016. ISO 2017 All rights reserved 1BS EN ISO 16120-2:2017ISO 16120-2:2017(E)5 Requirements5.1 GeneralFor the general requi

33、rements, see ISO 16120-1.5.2 Chemical compositionFor the heat analysis, the values shown in Table 1 shall apply. If a product analysis is required, the permissible deviations of the product analysis relative to the specified value of the heat analysis are given in Table 2.Table 1 Chemical analysis (

34、heat analysis) Steel gradeaHeat analysisCb%Sic%Mnd%P%max.S%max.Cr%max.Ni%max.Mo%max.Cue%max.Alf%max.C4D 0,06 0,30 0,30 to 0,60 0,035 0,035 0,20 0,25 0,05 0,30 0,01C7D 0,05 to 0,09 0,30 0,30 to 0,60 0,035 0,035 0,20 0,25 0,05 0,30 0,01C9D 0,10 0,30 0,30 to 0,60 0,035 0,035 0,20 0,25 0,05 0,30 0,01C10

35、D 0,08 to 0,13 0,30 0,30 to 0,60 0,035 0,035 0,20 0,25 0,05 0,30 0,01C12D 0,10 to 0,15 0,30 0,30 to 0,60 0,035 0,035 0,20 0,25 0,05 0,30 0,01C15D 0,12 to 0,17 0,30 0,30 to 0,60 0,035 0,035 0,20 0,25 0,05 0,30 0,01C18D 0,15 to 0,20 0,30 0,30 to 0,60 0,035 0,035 0,20 0,25 0,05 0,30 0,01C20D 0,18 to 0,

36、23 0,30 0,30 to 0,60 0,035 0,035 0,20 0,25 0,05 0,30 0,01C26D 0,24 to 0,29 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,20 0,25 0,05 0,30 0,01C32D 0,30 to 0,35 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,20 0,25 0,05 0,30 0,01C38D 0,35 to 0,40 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,20 0,25 0,05 0,30 0,01C42

37、D 0,40 to 0,45 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,20 0,25 0,05 0,30 0,01C48D 0,45 to 0,50 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C50D 0,48 to 0,53 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C52D 0,50 to 0,55 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,

38、20 0,05 0,25 0,01C56D 0,53 to 0,58 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C58D 0,55 to 0,60 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01NOTE Elements not included in Table 1 may not be added intentionally to the steel without the agreement of the purchaser, e

39、xcept those intended for finishing the heat. By agreement at the time of ordering, the grades can contain additions (commonly termed microalloying additions) of Cr and V. The content of Cr is up to 0,30 % and the content of V is 0,05 % to 0,10 %.aNon-alloy quality steel for general purposes shall co

40、mply with unalloyed quality steel in ISO 4948-2.bFor steel grades C26D to C92D, the carbon range may be enlarged by lowering the minimum by 0,01 % and by increasing the maximum by 0,01%, by agreement between the supplier and purchaser.cFor wire rod intended for galvanization, the required lower limi

41、t of silicon content should be specified at the time of ordering. By agreement at the time of ordering, the maximum silicon level for grades C4D to C20D may be further restricted.dFor grades from C15D to C92D, a different range from the one indicated in Table 1, but of the same amplitude, can be agr

42、eed at the time of ordering, with a maximum not exceeding 1,20 % and a minimum not lower than 0,30 %.eA maximum copper content of 0,20 % may be agreed at the time of ordering. For steel grades C48D to C92D, Cu + Sn shall be 0,25 %.fBy agreement at the time of ordering, the value for aluminium can be

43、 fixed at 0,01 % to 0,06 %. In such cases, the value of silicon can be fixed at 0,10 % on request.2 ISO 2017 All rights reservedBS EN ISO 16120-2:2017ISO 16120-2:2017(E)Steel gradeaHeat analysisCb%Sic%Mnd%P%max.S%max.Cr%max.Ni%max.Mo%max.Cue%max.Alf%max.C60D 0,58 to 0,63 0,10 to 0,30 0,50 to 0,80 0,

44、030 0,030 0,15 0,20 0,05 0,25 0,01C62D 0,60 to 0,65 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C66D 0,63 to 0,68 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C68D 0,65 to 0,70 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C70D 0,68 to 0,73 0,10 to

45、0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C72D 0,70 to 0,75 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C76D 0,73 to 0,78 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C78D 0,75 to 0,80 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C80D 0

46、,78 to 0,83 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C82D 0,80 to 0,85 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C86D 0,83 to 0,88 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01C88D 0,85 to 0,90 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20

47、0,05 0,25 0,01C92D 0,90 to 0,95 0,10 to 0,30 0,50 to 0,80 0,030 0,030 0,15 0,20 0,05 0,25 0,01NOTE Elements not included in Table 1 may not be added intentionally to the steel without the agreement of the purchaser, except those intended for finishing the heat. By agreement at the time of ordering,

48、the grades can contain additions (commonly termed microalloying additions) of Cr and V. The content of Cr is up to 0,30 % and the content of V is 0,05 % to 0,10 %.aNon-alloy quality steel for general purposes shall comply with unalloyed quality steel in ISO 4948-2.bFor steel grades C26D to C92D, the

49、 carbon range may be enlarged by lowering the minimum by 0,01 % and by increasing the maximum by 0,01%, by agreement between the supplier and purchaser.cFor wire rod intended for galvanization, the required lower limit of silicon content should be specified at the time of ordering. By agreement at the time of ordering, the maximum silicon level for grades C4D to C20D may be further restricted.dFor grades from C15D to C92D, a different range from the one indicated in Table 1, but of the same amplitude, can be agreed at the