FORD ESA-M8A6-A-2003 BEARING STEEL BACKED BRONZE-TFE Pb IMPREGNATED TO BE USED WITH FORD WSS-M99P1111-A 《四氟乙烯（TFE）、铅浸渗的青铜制钢背轴承 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2003 10 09 Revised Para 3.0 inserted; para 3.6 and 4 deleted 1983 03 28 3.4 Add Optional Procedure, CEM2-897050-C3 1963 08 21 Released AS2-368 Printed copies are uncontrolled Copyright 2003, Ford Global Technologies, Inc. Page 1 of 2 BEARING,

2、STEEL BACKED, BRONZE-TFE, Pb IMPREGNATED ESA-M8A6-A 1. SCOPE The material defined by this specification is a steel backed, tetrafluoroethylene and lead impregnated porous bronze bushing. 2. APPLICATION This specification was released originally for material used to reduce friction in the lower suspe

3、nsion arm pivots. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 STEEL BACKING Cold rolled low carbon steel 0.05 - 0.15% carbon. 3.2 LINING INTE

4、RLAYER MATERIAL AND THICKNESS 3.2.1 Composition, % Tin 10.0 - 12.0 Copper 88.0 - 90.0 Total Others 0.25 max 3.2.2 Average Thickness 0.009 - 0.013 in (0.23 mm - 0.33 mm) For initial approval section 30 bearings, mount and at 100 magnifications measure the thickness from the steel backing to highest b

5、ronze particle in four areas. Thickness will be the average of 120 readings. 3.3 OVERLAY COMPOSITION AND THICKNESS 3.3.1 Composition (% by volume) Polytetrafluoroethylene 65 min Lead Powder 35 max ENGINEERING MATERIAL SPECIFICATIONESA-M8A6-APrinted copies are uncontrolled Copyright 2003, Ford Global

6、 Technologies, Inc. Page 2 of 2 3.3.2 Average Film Thickness 0.0013 +/- 0.0003 in (0.033 +/- 0.008 mm) For initial approval use the 30 mounted sections from 3.2.2. At 100 magnifications measure the thickness of PTFE in the four thinnest areas from the bronze particles to outer edge. Thickness will b

7、e the average of 120 readings. 3.3.3 PENETRATION Lubricant shall penetrate the lining material to a depth of 0.003 in (0.08 mm) min. 3.4 CRUSHING STRENGTH, min 40,000 psi (276 MPa) Apply load to PTFE - bronze lining. Bronze interlayer must not be collapsed as determined by sectioning or by a 3% maximum change in section thickness as measured before and after loading. 3.5 BOND QUALITY (Steel Backing and Bronze) No flaking Test Method: Bend material through 90 around a radius not greater than 9-10 times the nominal steel thickness, with the lining material on the outside of the bend.