FORD ESB-M17H93-C1-2006 PADDING POLYURETHANE FOAM - SLAB - FABRIC REINFORCED TO BE USED WITH FORD WSS-M99P1111-A (USE WSS-M99P32-B)《织物增强的板式聚氨酯泡沫衬垫 与标准FORD WSS-M99P1111-A一起使用 使用.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 04 28 N-STATUS Replaced by WSS-M99P32-B; Ins 3.0; Del 3.1, 3.5 ESB-M8B12-A. Denatured Alcohol; and 50% Soap Solution, made up of equal parts of ESB-M1B9-A (or 2% solution of “Lux Liquid“) and tap water for a period of 1 h each at 23 +/- 2

2、 C. 3.4.8 Ply Adhesion (Sheeting to Foam), min (ASTM D 413, Machine Method, Strip Specimen) ESB-M17H93-C1, C2, C3, & C4 0.75 lb/in (131 N/m) width ESB-M17H129-B 0.75 lb/in (131 N/m) width 3.4.9 Compression and Recovery, min (50% compression at 43 C) ESB-M17H93-C2, C3 & C4 Requirement Only Recovery a

3、fter 7 days at 43 C 90% Test Method: Prepare three 4 x 4 x 1 (100 x 100 x 25 mm) samples (parts less than 1 in (25 mm) thick may be piled up) and measure their initial thicknesses using the dial gauge specified in FLTM BN 115-07. Then compress each sample 50% in a compression set device and place th

4、e assembly in an air convection oven for the required length of time at 43 C. Upon removal from the oven, immediately release the test specimens and allow a 30 min (+10, -0 min) recovery period before re-measuring each sample to obtain its final thickness (T3). Calculate the recovery as a percent of

5、 the original deflection: % Recovery = T3 - T2 - T1 - T2 T1 = Original thickness T2 = Thickness at 50% compression T3 = Final thickness ENGINEERING MATERIAL SPECIFICATION ESB-M17H93-C1/C4 ESB-M17H129-B Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 6 of 6 3.4.10 K

6、inetic Friction, max, Avg. of 3 75 g (ASTM D 1894, sled weight with 12.7 mm thick test sample to be 300 g, cover plane surface with teflon sheet, 305 mm/min test velocity) Clean the surface of the teflon with chlorothane before each use. The teflon sheeting may be obtained from: F. B. Wright Company

7、, 9999 Mercier, Dearborn, Michigan 48121 - Teflon Coated Fiberglass No. N961-0062. 3.4.12 Flammability In order to comply with Federal Motor Vehicle Safety Standard No. 302, the materials, portions of components, and composites shall not burn, or transmit a flame across its surface, at a rate of mor

8、e than 4 in (101 mm) per min. To demonstrate compliance, the sample size and method of testing shall be in accordance with FLTM BN 024-02. 3.4.13 Performance - Environmental Aging All materials, portions of components, and composites defined by these specifications that have not been treated, modifi

9、ed or reformulated and exceed a max burn rate of 3.0 in (76 mm) per min as specified by the Flammability Lot Sampling Plan of FLTM BN 024-02, must be evaluated for permanency of the materials flame retardant properties per ESB-M25P3-A according to the accelerated environmental aging requirements app

10、licable to the basic material category of these particular specifications. Any material, portions of components, and composites defined by these specifications that have been treated, modified or reformulated to conform to Flammability Lot Sampling Plan of FLTM BN 024-02, regardless of max burn rate

11、, must be evaluated for both permanency of materials flame retardant properties and changes in mechanical, chemical and physical properties per ESB-M25P3-A applicable to the basic materials category of these particular specifications. 3.4.14 Flammability Test Program Materials, portions of component

12、s, and composites governed by these specifications must also comply with the requirements of ES-D3AB-11014-AA. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 BLOCKING The ESB-M17H93-C4 anti-friction coating will block when placed against itself and should not be shipped or stored in this manner. Blocking could occur against other substrates at elevated temperatures (60 C or above) for extended periods of time and appropriate precautions should be taken.