FORD ESB-M1C106-A-2008 GREASE - REDUCED POLYETHYLENE 1-3 - TO BE USED WITH FORD WSS-M99P1111-A 《低聚乙烯1-3含量的润滑脂 与标准FORD WSS-M99P1111-A一起使用 ［使用 FORD WSS-M13P12-A FORD WSS-M13P12-A.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 10 09 N-STATUS Replaced by WSS-M13P12-A L. Schmalz, FNA 2003 10 24 Revised Para 3.0 inserted; paras 3.7 and 4 deleted 1963 12 10 Released AS1 #1171 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 1 of 1

2、 GREASE - REDUCED POLYETHYLENE 1-3 ESB-M1C106-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is an NLGI No. 2 grade of polyethylene grease (ESB-M1C93) reduced 1-3 parts by weight with M-5B58, Inhibited Methyl Chloroform. 2. APPLICATION This specification was rele

3、ased originally for grease used to lubricate hood and deck-lid hinge pivot points. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 APPEARANCE Bei

4、ge to light brown in color, transparent when applied in thin films. 3.2 COMPOSITION 3.2.1 Volatile, min as M-5B58 70% (10 g, 24 h at 100 +/- 2 C) 3.2.2 Non-Volatile, max 30% Soap Identification Lithium 3.3 FILLER Polyethylene (ASTM D 128) 3.4 SPECIFIC GRAVITY AT 15.6 C 1.130 - 1.190 3.5 WATER RESIST

5、ANCE 3.5.1 The material, when applied to metal strips and solvent evaporated, shall withstand 168 h at 38 +/- 1 C in a 98 +/- 2% relative humidity atmosphere without breaking. 3.5.2 The material, when applied to metal strips and solvent evaporated, shall withstand 16 h immersion in a bath of running cold water without breaking per ASTM D 1264. 3.6 QUALITY The material shall be free from dirt, lumps, abrasive material, or other impurities and shall be uniform in appearance.