FORD ESB-M2E93-A-2002 FIBERBOARD CELLULOSE - HIGH STRENGTH PHENOLIC RESIN IMPREGNATED TO BE USED WITH FORD WSS-M99P1111-A 《高强度酚醛树脂浸渍的纤维素纤维板 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2002 10 14 Revised Updated and renumbered 1978 12 01 Metricated, Renumbered & Retyped CAH1-RD572066-197 1973 09 13 Released AC1-6000-376 Printed copies are uncontrolled Page 1 of 1 Copyright 2002, Ford Globa

2、l Technologies, Inc. FIBERBOARD, CELLULOSE-HIGH STRENGTH PHENOLIC RESIN ESB-M2E93-A IMPREGNATED 1. SCOPE The material defined by this specification is a cellulose fiberboard impregnated with a high strength phenolic resin. 2. APPLICATION This specification was released originally for material used f

3、or body panel to rocker panel shims. 3. REQUIREMENTS All specimens and/or production parts shall be treated with a polymeric coating and post cured to case harden and seal. All tests shall be conducted in accordance with ASTM F 104, Type 3 materials, unless otherwise specified. 3.1 STANDARD REQUIREM

4、ENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COMPRESSIBILITY, max 15 % (4000 psi (27.6 MPa) load) Recovery, min 80 % 3.3 TENSILE STRENGTH, min 6400 psi (44.2 MPa) 3.4 DENSITY, min 60 lb/ft3 (962 kg/m3) ASTM F 104, Section A 2.14 Density (Type 2) 3.5 IMMERSION IN LIQUIDS (22 h at 23 +/- 2 C) Immersion Fluid Weight Increase, % max Thickness Change, % max ESE-M97B18 Antifreeze 12 6 ASTM Reference Fuel “B“ 15 5 ASTM Oil #1 10 5 ASTM Oil #3 10 5 Distilled Water 25 25