FORD ESB-M2P7-B2-2008 PAINT PERFORMANCE HIGH VISIBILITY PLASTIC PARTS - EXTERIOR - TEXTURED PAINT TO BE USED WITH FORD WSS-M99P1111-A 《高可见性塑料部件用外部装饰用涂料的油漆性能 与FORD WSS-M99P1111-A一.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Ver. 4 2008 08 27 N-STATUS Replaced by WSS-M2P180-A or WSS-M2P180-C G. Weber, FNA 2003 07 31 Revised Para 3.0 inserted 1977 07 18 Released AGI-6000-233 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 1 of 2

2、 PAINT PERFORMANCE, HIGH VISIBILITY PLASTIC PARTS - ESB-M2P7-B2 EXTERIOR - TEXTURED PAINT NOT TO BE USED FOR NEW DESIGN 1. SCOPE This specification defines the performance requirements of a low gloss textured paint finish on high visibility exterior plastic parts. A wet-on-wet catalyzed paint system

3、 with no primer is used to achieve the desired finish. 2. APPLICATION This specification was released originally for a system used as the total paint finish for pick-up truck box covers. 3. REQUIREMENTS The requirements for this specification are contained in ESB-M2P7-B1. The exceptions are as follo

4、ws: Paragraphs 3.1.3 Primer Surfacer, 3.1.4 Sealer or Guidecoat and 3.1.5 Repair Primer are not applicable. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1.6 Col

5、or Coat Color is provided by 2 coat wet on wet catalyzed paint system. The basecoat is a smooth uniform coating sprayed to a dry film thickness of 0.0015 in (38.1 m). The second coat is an overlay finish used to provide a uniform textured appearance matching the Design Center Standard. No minimum fi

6、lm thickness is required as this coating is discontinuous and required for appearance only. 3.2.4 Film Thickness (FLTM BI 117-01) Basecoat: 0.0015 in (38.1 m), minimum dry film thickness. Top Coat: No minimum thickness required. 3.2.5 Polishing Not applicable 3.3 RESISTANCE PROPERTIES All requiremen

7、ts apply to the basecoat with and/or without the textured topcoat. Note: Parts may be evaluated for resistance properties with or without being aged 16 h at 43 C or 72 h above 21 C before test. ENGINEERING MATERIAL SPECIFICATION ESB-M2P7-B2 Printed copies are uncontrolled Copyright 2008, Ford Global

8、 Technologies, Inc. Page 2 of 2 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 MATERIAL REFERENCES Base Coat: ESB-M2J116-B Top Coat: ESB-M2J117-B 5.2 SUBSTRATES ESB-M3D105 Polyester Resin - Fiberglass Reinforced Matched Metal die molding compound.