FORD ESB-M3G51-A-2005 TAPE VINYL - PRESSURE SENSITIVE TO BE USED WITH FORD WSS-M99P1111-A 《乙烯基压敏带 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 09 20 Revised Inserted 3.0; Deleted 3.1, 3.6, 4 1978 11 03 Metricated, Renumbered & Retyped K. Gillen 1963 06 05 Released AS! #915 Original/s/G. M. Wolfe/E. P. DePalma Printed copies are uncontrolled Copyright 2005, Ford Global Technologi

2、es, LLC Page 1 of 4 TAPE, VINYL - PRESSURE SENSITIVE ESB-M3G51-A 1. SCOPE The material defined by this specification is a pressure sensitive, paper backed, vinyl tape. 2. APPLICATION This specification was released originally for material used over bright metal or painted surfaces for exterior appea

3、rance applications. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 PHYSICAL PROPERTIES 3.2.1 Tensile Strength, min 1000 psi (6.9 MPa) (ASTM D 88

4、2, Method “A“, 1 x 6 in (25 x 150 mm) sample, 2 in (50.8 mm) distance bench marks, jaw spaced at start 4 in (100 mm) pulling speed 2 in (50 mm)/min) 3.2.2 Elongation, min Metallic film 15% Non-metallic film 35% 3.2.3 Tear Strength, min 14 lb/in (2.5 N/mm) width (ASTM D 1938) 3.2.4 Adhesion, min (AST

5、M D 1000, except determine adhesion to anodized aluminum, stainless steel, chromium plating and ESB-M50J100 quality enameled steel) As received 30 oz/in (328 N/m) width Aged, except stainless steel 50 oz/in (547 N/m) width Aged, stainless steel 30 oz/in (328 N/m) width Test Method: Expose duplicate

6、samples to each of the following conditions. 72 h at 70 +/- 1 C 400 h weatherometer, per FLTM BO 101-01. ENGINEERING MATERIAL SPECIFICATIONESB-M3G51-APrinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 4 168 h at 38 +/- 1 C and 95-100% relative humidity. 240 h wat

7、er immersion per FLTM BI 104-01. 10 cycles consisting of 4 h at 70 +/- 1 C, 4 h at 38 +/- 1 C and 95 - 100% relative humidity, and 16 h at -29 +/- 1 C. Samples shall be conditioned for 48 h at 23 +/- 2 C prior to exposure. Tests shall be completed within 4 h after removal from the conditioning envir

8、onment. 3.3 FILM PROPERTIES 3.3.1 Appearance Shall match the Ford Motor Company Styling Master. 3.3.2 Thickness (ASTM D 1000) Vinyl Tape 0.002-0.005 in (0.05-0.13 mm) Release Paper 0.004-0.008 in (0.10-0.20 mm) 3.4 RESISTANCE PROPERTIES 3.4.1 Sample Preparation Except where otherwise noted, resistan

9、ce properties tests shall be conducted using appropriate sized steel panels (3 x 6 in (75 x 150 mm) painted with ESB-M50J100 quality enamel. The film shall be applied using assembly plant techniques and shall fully cover the face of the panel allowing a 1/8-1/4 in (3.2-6.4 mm) border around the peri

10、phery of the panel. Samples shall be conditioned for 48 h at 23 +/- 2 C prior to starting the tests. 3.4.2 Heat Resistance, max 1.0% shrinkage No evidence of cracking, checking, or color change after exposure for 30 minutes at 121 +/- 3 C. The test shall be conducted 2 h after application of a 1 x 1

11、0 in (25 x 250 mm) strip of the material to a 4 x 12 in (100 x 300 mm) ESB-M50J100 quality enameled steel panel. 3.4.3 Weather Resistance Minimum degree of fading, chalking, or dulling. No increase of brittleness or loss of adhesion is permitted and the material shall be completely free from evidenc

12、e of cracking, checking, blistering, or peeling when exposed as follows: Florida Exposure, Miami Area, min 12 mo. (5 facing south) Accelerated Weathering, min 400 h (FLTM BO 101-01, Atlas Weatherometer) ENGINEERING MATERIAL SPECIFICATIONESB-M3G51-APrinted copies are uncontrolled Copyright 2005, Ford

13、 Global Technologies, LLC Page 3 of 4 3.4.4 Resistance to Water and Soap Spotting (FLTM BI 113-01, except omit the use of colorimeter) No more dulling or color change than the approved master sample on file in the Body Materials Section, BEPE Materials Engineering Department. 3.4.5 Resistance to Aci

14、d Spotting (FLTM BI 113-02, except omit the use of colorimeter) No more dulling or color change than the approved master sample on file in the Body Materials Section, BEPE Materials Engineering Department. 3.4.6 Water Resistance, min 240 h (FLTM BI 104-01) No film degradation, blistering or loss of

15、adhesion. Evaluation shall be made upon removal from the water bath. No other visual defects, such as blushing shall be evident after the sample is allowed to recover for 8 h at 23 +/- 2 C. 3.4.7 Wet Spray Resistance, min 240 h (FLTM BI 103-01) No film degradation, blistering, or loss of adhesion. E

16、valuation shall be made upon removal from the salt spray chamber. No other visual defects, such as blushing shall be evident after the sample is allowed to recover for 8 h at 23 +/- 2 C. 3.4.8 Gasoline Resistance The tape, when applied to panels prepared as in para 3.4.1, shall resist gasoline. Test

17、 Method: Place taped panel in a 600 mL beaker, half full of M-14J148 Petroleum Naphtha-Aliphatic type at 23 +/- 2 C for 1 h. The tape, after removal from the naphtha, shall not be blistered and only slightly softened and dulled. Furthermore, the tape shall not exhibit any significant loss in adhesio

18、n. 3.5 REQUIREMENTS ON FINISHED PARTS 3.5.1 Cleanliness All substrates to be covered by the film shall be clean in keeping with good commercial practice. Oil, grease, dust, and other foreign materials which would affect the adhesion of the film shall be removed prior to material application. 3.5.2 A

19、ppearance Parts shall match master samples approved by Styling and initial samples approved by Quality Control for: Color match and uniformity Smoothness (absence of blisters) Absence of scratches and tool marks ENGINEERING MATERIAL SPECIFICATIONESB-M3G51-APrinted copies are uncontrolled Copyright 2

20、005, Ford Global Technologies, LLC Page 4 of 4 3.5.3 Adhesion, min As received 30 oz/in (328 N/m) width Aged 50 oz/in (547 N/m) width Test Method: Expose samples of the part to each of the following conditions:. 72 h at 70 +/- 1 C 96 h at 38 +/- 1 C and 95-100% relative humidity Samples shall be con

21、ditioned a minimum of 4 h at 23 +/- 2 C prior to starting the tests. Test shall be completed within 4 h after removal from the conditioning environment in accordance with ASTM D 1000. Adhesion tests are not required if the size and/or shape of the part does not permit testing in accordance with the

22、specified method. When this condition exists, the part shall be exposed to the specified test conditions and no blistering, lifting, peeling or loss of adhesion shall be permitted. 3.5.4 Heat Resistance Finished parts shall withstand a simulated paint repair bake (30 min at 121 +/- 3 C) without evid

23、ence of blistering, checking, cracking, or loss of adhesion. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. MATERIAL REFERENCES FOR TEST PANELS Anodized Aluminum: ESB-M2A34-A, anodized coating per ESB-M4P6-A. Stainless Steel: ESB-M1A67-A or ESB-M1A70-A. Chromium Plating: SAE 903 or SAE 925 zinc die casting chromium plated per ESB-M1P23-A. Enameled Steel: ESB-M50J100-A quality, prepared per FLTM BI 103-02, Method “C“.