FORD ESB-M3G54-A-2005 TAPE PAPER BACKED - PRESSURE SENSITIVE TO BE USED WITH FORD WSS-M99P1111-A 《压敏带纸背型胶带 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 09 21 Revised Inserted 3.0; Deleted 3.1, 3.12, 4 1978 09 01 Metricated, Renumbered & Retyped CAH1-RD572066-86 1963 05 31 Released DS1 #615 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 TAPE, PAP

2、ER BACKED - PRESSURE SENSITIVE ESB-M3G54-A 1. SCOPE The material defined by this specification is a paper backed pressure sensitive tape. 2. APPLICATION This specification was released originally for tape used to retain the polyethylene coated paper water shield on the lower door inner panel assembl

3、y. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 BREAKING STRENGTH, min (ASTM D 1000, 20 in (508 mm)/min rate of pull) 3.2.1 Dry 15 lb/in (2.6

4、N/mm) width 3.2.2 Wet 10 lb/in (1.8 N/mm) width Test Method: Immerse specimens in tap water at 23 +/- 2 C for 6 h. Remove, and blot off excess water from surfaces of specimens and pull immediately. 3.3 UNWIND PULL, max 48 oz/in (525 N/m) width Test Method: Condition roll of tape for 22 h at 23 +/- 2

5、 C in a relative humidity atmosphere of 50 - 55%. Place core of tape around a fixture which will allow it to revolve. Attach the free end of the tape to a 10 lb (4.5 kg) maximum limit spring scale. Pull tape from its roll at the rate of 12 in (305 mm)/min. Measure and record the unwind pull as a dir

6、ect scale reading. 3.4 ADHESION TO BACKING, min 10 oz/in (109 N/m) width (ASTM D 1000) 3.5 ADHESION TO STEEL, min 18 oz/in (197 N/m) width (ASTM D 1000) 3.6 ADHESIVE SOLUBILITY The adhesive shall be soluble in M-14J167, Special Spirits and M-14J147, Petroleum Light Naphtha. 3.7 MOISTURE VAPOR TRANSM

7、ISSION RATE, max 23 g (FLTM BU 001-01) ENGINEERING MATERIAL SPECIFICATIONESB-M3G54-APrinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 3.8 WATER PENETRATION RATE, max 50 g (FLTM BU 001-02) 3.9 ACCELERATED AGING, Storage Stability (ASTM D 1000, except maintain t

8、he humidity cabinet at 95 - 100% relative humidity and 38 +/- 1 C) No signs of separating from its backing, nor loss in adhesion or tack. It shall not become a pasty or stringy mass. The backing shall not become brittle. 3.10 WATERFASTNESS OF DYE Waterfast Test Method: Vigorously shake a 4 in (100 mm) strip of tape in 200 ml of distilled water at 23 +/- 2 C. Allow to stand in the water at 23 +/- 2 C for 6 h. Any discoloration of the water shall be cause for rejection. 3.11 MIGRATION STAINING None (FLTM BU 105-01, 72 h)