FORD ESB-M4D413-A2-2008 ABS - POLYCARBONATE MOLDING COMPOUND ELECTROPLATING ESB-M4D413-A2 AND PAINTING GRADE TO BE USED WITH FORD WSS-M99P1111-A 《ESB-M4D413-A2电镀和油漆级丙烯腈-丁二烯-苯乙烯共聚.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2008 02 22 N-STATUS Replaced by WSS-M4D585-B; Removed inactive ESB-M4D413-B2; Inserted 3.0; Deleted 3.1, 3.5, 3.5.1, 3.5.2, 3.5.3, 3.8 & 4 G. Kowalski 1981 12 11 Released AM1-6000-68 Printed copies are uncontrolled Copyright 2008, Ford Global

2、 Technologies, LLC Page 1 of 3 ABS - POLYCARBONATE MOLDING COMPOUND, ELECTROPLATING ESB-M4D413-A2 AND PAINTING GRADE NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is an acrylonitrile butadiene styrene (ABS) and polycarbonate alloy which may be electroplated or pai

3、nted and exhibits good impact and heat resistance. ESB-M4D413 suffix designations correspond to former type categorization as follows: ESB-M4D413-A2 replaces ESB-M4D413-A1 Drawings specifying ESB-M4D413-A1 or ESB-M4D413-B1 do not require revision to reflect this new suffix classification. 2. APPLICA

4、TION This specification was released originally for material used in painted radiator grilles and electroplated mirror housings where high impact and/or heat resistance is required. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform

5、to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 PROPERTIES 3.2.1 Specific Gravity 1.06 - 1.15 (ASTM D 792) 3.2.2 Hardness, Rockwell “R“ 106 - 114 (ASTM D 785) 3.2.3 Tensile Strength, min 6400 psi (44.1 MPa) (ASTM D 638) 3.2.4 Elongation, min 30% (ASTM D 638) ENGI

6、NEERING MATERIAL SPECIFICATION ESB-M4D413-A2 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 3 3.2.5 Flexural Modulus, min 350,000 psi (2.4 GPa) (ASTM D 790) 3.2.6 Flexural Strength, min 10,000 psi (69 MPa) (ASTM D 790) 3.2.7 Impact Strength, Izod, min (ASTM D

7、 256) Notched 5.0 ft.lb/in (267 J/m) Unnotched (No Notch Either Side) 15.0 ft.lb/in (800 J/m) 3.2.8 Deflection Temperature, min (ASTM D 648, 1/4 in (6.4 mm) specimen width, unannealed) At 66 psi (455 kPa) 105 C At 264 psi (1820 kPa) 101 C 3.3 REGRIND Parts manufactured from this material may contain

8、 a maximum of 20% clean, dried and nondegraded regrind unless otherwise specified on the engineering drawing. Regrind from parts that exhibit splay or brittleness may not be used. (Splay and/or brittleness indicates that the polycarbonate portion of the alloy has been irreversibly degraded.) 3.4 FLA

9、MMABILITY, max 4 in (101 mm)/min (FLTM BN 024-02, without the lot sampling plan) In addition, the test specimen shall not exhibit any flashing or sudden flaming on either surface in excess of the above maximum value. 3.6 MOLDED PARTS Specific requirements for physical properties of molded parts, whe

10、n required, shall be specified on the engineering drawing. 3.7 DECORABILITY When decorating is required on parts made of this material, they must be capable of accepting this decoration in accordance with the performance specification shown on the engineering drawing. ENGINEERING MATERIAL SPECIFICAT

11、ION ESB-M4D413-A2 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 3 of 3 5. GENERAL INFORMATION: The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 MOLD SHRINKAGE 0.006 - 0.008 in/in (mm/m

12、m) (ASTM D 955) 5.2 COEFFICIENT OF LINEAR THERMAL EXPANSION 6.2 x 10-5/ C (ASTM D 696) 5.3 IMPACT RESISTANCE, TYPICAL (Test fixture per FLTM BO 117-02, 0.125 in (3.2 mm) thick x 4 in (102 mm) diameter round plaques, virgin material non-decorated) At 23 C 200 in.lb (22.6 J) At -29 C 18 in.lb. (2.0 J)