FORD ESB-M4G316-A1-1989 SEALER REPAIR TWO COMPONENT - EPOXY BASE - HIGH FLOW《高流动性环氧树脂基两组分维修密封剂》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONMaterial Name Specification NumberDate Release No. Release/Revision1989 10 31 NB00E10044423000 Released WJC/ERR/MPWP 3948-a Page 1 of 6SEALER, REPAIR, TWO COMPONENT - EPOXY BASE - HIGH FLOW ESB-M4G316-A1SEALER, REPAIR, TWO COMPONENT - EPOXY BASE - LOW FLOW ESB-M4G3

2、16-A21. SCOPE:The material defined by this specification is a two component, roomtemperature curing epoxy base repair sealer.2. APPLICATION:This specification was released originally for material to seal andrepair defects such as pinholes and skips in vinyl plastsol. The sealeris also used to repair

3、 drip rail, coach joint and roof ditch sealerareas. The sealer can be painted and baked in current production andrepair procedures.3. REQUIREMENTS:3.1 STATISTICAL PROCESSSuppliers must conform to the requirements of Ford Quality SystemStandard Q-101. A mutually acceptable Control Plan as describedth

4、erein is required for material/source approval. Appropriatestatistical tools must be used to analyze process/product data sothat variation in the final product is continuously reduced.3.2 INFRARED SPECTROPHOTOMETRY/THERMAL ANALYSISFord Motor Company, at its option, may conduct infrared and/orthermal

5、 analysis of material/parts supplied to this specification.The IR spectra and thermograms established for initial approvalshall constitute the reference standard and shall be kept on fileat the designated material laboratory. All samples shall produceIR spectra and thermograms that correspond to the

6、 referencestandard when tested under the same conditions.3.3 CONDITIONING AND TEST CONDITIONSAll test values indicated herein are based on materials conditionedin a controlled atmosphere of 23 +/- 2 C and 50 +/- 5 % relativehumidity for not less than 24 h prior to testing and tested underthe same co

7、nditions unless otherwise specified.ENGINEERING MATERIAL SPECIFICATION WSS-M4G316-A1WSS-M4G316-A2WP 3948- b Page 2 of 63.4 SOLIDS, min(SAE J243, ADS-7, Method A)Base 99 % by weightHardener 90 % by weight3.5 WEIGHT PER VOLUME(ASTM D 816)Base 1.25 - 1.35 kg/LHardener 1.10 - 1.20 kg/L3.6 GEL TIME (afte

8、r mixing) 5 - 20 minutes(ASTM D 2471, 10 g at 23 +/- 2 C)3.7 SHEAR ADHESION STRENGTH, min(SAE J1523, substrate per para 5.2, 0.25 mm bondline thickness,material cure per specified time and temperature.)3.7.1 NormalAfter 1 h at 23 +/- 2 C 1.0 MPaAfter 72 h at 23 +/- 2 C 1.0 MPa3.7.2 Aged (After Norma

9、l Cure of 72 h). 14 days at 70 +/- 2 C 5.3 MPa. 14 days at 38 +/- 2 C and 95 - 100 % 5.6 MParelative humidity (RH). 4 cycles of 4 h at 82 +/- 2 C, 2.2 MPa4 h at 38 C and 95 - 100 % RHand 16 h at -29 +/- 1 C3.8 FLEXIBILITY No cracking or(FLTM BV 22-1) loss of adhesionApply a 1 x 25 x 150 mm ribbon of

10、 material to two 100 x 300 x0.8 mm E-coated panels per para 5.2. Cure the material for 72 h at23 +/- 2 C.3.8.1 Test at 23 +/- 2 C3.8.2 Test at -23 +/- 2 CENGINEERING MATERIAL SPECIFICATION WSS-M4G316-A1WSS-M4G316-A2WP 3948- b Page 3 of 63.9 REPAINT CRACK RESISTANCE No paint or sealercrackingTest Met

11、hod:. Fill the inside of six 1/2 pint can lids withESB-M4G177-B2 or equivalent and six with ESB-M4G177-C2 orequivalent sealer. Fill the lids approximately half full. Cure the material for 10 minutes metal temperature at163 +/- 2 C. Allow to cool and fill the lids with the repair sealer sothat half t

12、he lid shows the 4G177 type material and theother half shows the repair sealer (Masking half the lidprior to adding the repair sealer may help). Remove the tape, if applicable, and condition the samplefor a minimum of 5 minutes at 23 +/- 2 C. Apply currentproduction enamels as identified by the Body

13、 and ChassisProduct Engineering Office. Expose painted lids to the following paint repair cycles 10times:140 +/- 2 C for 17 minutes oven time.23 +/- 2 C for 20 minutes. Observe for any evidence of paint/sealer cracking aftereach cycle.3.10 FLOW TESTESB-M4G316-A1 Material shall be self-leveling(Type

14、III) to a smooth surface free ofwaves, irregularities orbubbles.ESB-M4G316-A2, max 50 mm after 10 minutes(Type IV)Test Method: ASTM C 639 except for the following modifications:. Condition all materials and fixtures for a minimum of 16 -24 h at 23 +/- 2 C. Hand mix the hardener and base for 2 minute

15、s. Fill the appropriate channels (Type III or Type IV) within5 minutes after mixing. Examine the channels after material has cured and reportresults.3.11 COMPATIBILITY WITH PRODUCTION PAINTS(SAE J1800)No tackiness, staining, discoloration, or other deleterious effectson topcoats.ENGINEERING MATERIAL

16、 SPECIFICATION WSS-M4G316-A1WSS-M4G316-A2WP 3948- b Page 4 of 63.11.1 500 h QUV(SAE J2020)3.11.2 336 h Heat Age at 70 +/- 2 CTest Method:. Prepare six test panels per SAE J1800, method #3. Use atopcoat bake of 17 minutes oven time at 130 C. Applycurrent production enamels as identified by the Body a

17、ndChassis Product Engineering Office. Condition painted panels at 23 +/- 2 C for 72 h. Subject one panel with topcoat to each exposure listedabove. Retain extra panel as control. After exposure, examine test panels and compare to thecontrol panel.3.12 STORAGE STABILITYThe material shall be stored at

18、 temperatures below 41 C away fromall sources of heat and sunlight. Heat greatly accelerates aging.Under these storage conditions, the shelf life of the materialshall be 12 months. When these materials are stored attemperatures below 23 C, they shall be conditioned at roomtemperature prior to applic

19、ation. Adequate conditioning permitsthe material to obtain its optimum application properties.3.13 MATERIAL CONSISTENCYThe base and hardener shall be smooth, homogenous mixtures freefrom foreign materials and properties detrimental to normalproduction operations.3.14 FUNCTIONAL APPROVALMaterials bei

20、ng evaluated for initial approval to thisspecification shall be subjected to a production trial. Functionaltrial results must be approved by the affected assembly operationand Design Engineering. Results shall be made available toMaterials Engineering prior to material approval and release.ENGINEERI

21、NG MATERIAL SPECIFICATION WSS-M4G316-A1WSS-M4G316-A2WP 3948- b Page 5 of 63.15 ADDITIONAL REQUIREMENTSSpecific requirements for material and or manufactured parts shallbe specified on the engineering drawing, engineering partsspecification and/or performance specifications All critical areaswith res

22、pect to these properties shall be designated on theEngineering drawing.3.16 SUPPLIERS RESPONSIBILITYAll materials supplied to this specification must be equivalent inall characteristics to the material upon which approval wasoriginally granted.Prior to making any change in the properties, compositio

23、n,construction, color, processing or labeling of the materialoriginally approved under this specification, whether or not suchchanges affect the materials ability to meet the specificationrequirements, the Supplier shall notify Purchasing, Toxicology andthe affected Materials Engineering activity of

24、 the proposed changesand obtain the written approval of the Materials Engineeringactivity. Test data, test samples and a new code identificationare to be submitted with the request.Substance restrictions imposed by law, regulations or Ford apply tothe materials addressed by this document. The restri

25、ctions aredefined in Engineering Material Specification WSS-M99P9999-A1,unless a different suffix (e.g., A2 or A3) is specified on theengineering document for the application.4. APPROVAL OF MATERIALS:Materials defined by this specification must have prior approval by theresponsible Materials Enginee

26、ring activity. Suppliers desiring approvalof their materials shall first obtain an expression of interest from theaffected Purchasing, Design and Materials Engineering activity. Uponrequest, the Supplier shall submit to the affected Materials Engineeringactivity its own laboratory report to the spec

27、ification (test results,not nominal values), the material designation and code number and testspecimens for Ford evaluation. Upon approval, the material will be addedto the Engineering Material Approved Source List.5. GENERAL INFORMATION:The information given below is provided for clarification and

28、assistancein meeting the requirements of this specification.5.1 COLORBase Gray, or as specified on drawingHardener White, or as specified on drawing5.2 SUBSTRATESNominal panel dimensions are 0.8 x 100 x 300 mm.Electrocoat primed steel panel: Prepared per ESB-M2P4 performancespecification. Use curren

29、t production paints as identified by theENGINEERING MATERIAL SPECIFICATION WSS-M4G316-A1WSS-M4G316-A2WP 3948- b Page 6 of 6body and Chassis Electrical Product Engineering Office.5.3 APPLICATION PROCEDURE FOR REPAIR OF SEVERE CRACKS, SKIPS ANDVOIDS IN SEALER1) Groove (V) out cracks, skips or voids, r

30、emoving oldsealer. Scuff sand enamel surfaces with 180 - 220 gradesandpaper.2) Clean the area thoroughly with a solvent cleaner. Blow offany dust particles.3) Fill the grooved area with two part repair sealer(thoroughly mix repair sealer before application). Apply asmall amount to area and feather smooth. Clean up excessmaterial with solvent.4) Allow 5 minutes to air dry then paint. Follow current spotrepair procedures.