FORD ESB-M6J127-B-2008 PRIMER SURFACER CONDUCTIVE - THERMOPLASTIC SUBSTRATES - HIGH GLOSS (EXTERIOR) TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD ESB-M6J127-A)《热塑基底高光泽导电型中途.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2008 04 23 Revised Revised 4; Format Updated 2002 07 26 Revised Updated and ESB-M50J100 and 32J101 quality color coat. Chipping shall not exceed Figure 1. 3.7.2 Water Immersion, min 240 h (FLTM BI 104-01) 3.7.3 Florida Exposure Panels, prepar

2、ed as in paragraph 3.4, scribe with an “X“ to bare plastic and exposed in the Miami, Florida area at 5 facing south for 12 months, shall show no blistering, peeling, checking, or brittleness. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting t

3、he requirements of this specification. 4.1 FLASH POINT, min 16 C (ASTM D 92) ENGINEERING MATERIAL SPECIFICATION ESB-M6J127-A/B Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 4 of 4 4.2 FLAMMABILITY This material represents a potential fire hazard. The Manufacturin

4、g Engineering Department shall notify both the Plant Security and the Safety Units of its presence in the Plant to assure that proper fire precautions are provided. The location in which it is used or stored shall be included in the notifications. 4.3 ZINC REACTIVITY This material is highly zinc reactive and, therefore should not be stored or used in galvanized or zinc-lined tanks or equipment. 4.4 APPLICABLE SPECIFICATIONS Substrate ESB-M4D353, 4D354 or as specified on Engineering Drawing. Primer ESB-M6J127 Enamels ESB-M50J100 quality ESB-M32J101 quality