FORD ESE-M8G178-A-2012 GASKET NON-ASBESTOS SYNTHETIC RUBBER BINDER TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions Rev 03 2012 05 08 N Status No usage or replacement N. Benipal, NA 2000 11 08 Revised Updated & renumbered A. Cockman 1984 05 22 Released CE3P-RD863100-E120 E. J. Duda Controlled document at www.MATS Page 1 o

2、f 3 Copyright 2012, Ford Global Technologies, Inc. GASKET, NON-ASBESTOS SYNTHETIC RUBBER BINDER ESE-M8G178-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a gasketing material comprised of non-asbestos reinforcing compounds in combination with synthetic elastom

3、eric binders. 2. APPLICATION This specification was released originally for material requiring high flange loads to seal against internal pressures at moderately high temperatures plus good oil resistance such as the intake manifold gasket. 3. REQUIREMENTS Material specification requirements are to

4、be used for initial qualification of materials. All tests shall be conducted in accordance with ASTM F 104 Type 1, Class 1 material unless otherwise specified. Test specimens are to be selected from finished gaskets when practicable. 3.1 QUALITY SYSTEM REQUIREMENTS Material suppliers and part produc

5、ers must conform to the Companys Quality System Requirements. 3.2 ORIGINAL PROPERTIES (All thicknesses) 3.2.1 Tensile Strength, min 15.0 MPa 3.2.2 Compressibility 15 - 28% 3.2.3 Recovery, min 45% 3.3 HEAT AGING (All thicknesses) (22 h at 150 +/- 3 C) 3.3.1 Weight Change, max -10% 3.3.2 Compressibili

6、ty 5 - 20% 3.3.3 Recovery, min 50% ENGINEERING MATERIAL SPECIFICATION ESE-M8G178-A Page 2 of 3 Copyright 2012, Ford Global Technologies, Inc. 3.3.4 Tensile Change, max -45% Test Method: Place 3 weight change samples 25 x 50 mm x sample thickness and 3 tensile change 13 x 100 mm x sample thickness or

7、 any sample size which is practicable between 100 x 125 x 13 mm steel plates. Place in furnace set at 150 +/- 3 C for 22 h. 3.4 IMMERSION IN LIQUIDS Tensile Thickness Weight Strength Change Change Loss, max, Immersion Fluid Test Conditions % % % ASTM Oil No. 1 5 h, 150 C 0 to +6 +8 to +25 -20 ASTM O

8、il No. 3 5 h, 150 C +2 to +15 +18 to +32 -40 ASTM Fuel “C“ 5 h, 23 C +6 to +20 +10 to +30 -86 3.5 DENSITY 1280 - 1450 kg/m3 3.6 SEALABILITY, max 4 mL/h (ASTM F 37, 760 mm Hg fluid pressure Fuel A, 13.7 MPa flange load) 3.7 IGNITION LOSS 54 - 60% (ASTM F 495) 3.8 SURFACE COATING Must not stick or sho

9、w any evidence of corrosion Metal Plates Aluminum to Aluminum Aluminum to Steel Steel to Steel Test Method: A 15.9 mm I.D. x 38.1 mm O.D. test specimen is clamped between 2 discs of 13.5 mm I.D. x 51 mm O.D. metal plates (maximum thickness 1.57 mm) backed by 12.7 mm steel plates. A 12.7 mm steel bol

10、t is inserted through the hole and a nut put on it. Tighten the bolt to 79 N.m. Heat the assembly to 150 +/- 3 C for 5 h. Remove and allow to cool to room temperature. The specimen shall come off the metal plates without tearing and the metal plates must show no evidence of corrosion. ENGINEERING MA

11、TERIAL SPECIFICATION ESE-M8G178-A Page 3 of 3 Copyright 2012, Ford Global Technologies, Inc. 3.9 INFRARED SPECTROPHOTOMETRY AND/OR THERMAL ANALYSIS IR spectra and thermograms established for initial approval shall constitute the reference standard and shall be kept on file at the designated material

12、 laboratory. All samples shall produce IR spectra and thermograms that correspond to the reference standard when tested under the same conditions. 3.10 SUPPLIERS RESPONSIBILITY All materials supplied to this specification must be equivalent in all characteristics to the material upon which approval

13、was originally granted. Prior to making any changes to the material originally approved under this specification, whether or not such changes affect the materials ability to meet the specification requirements, the Supplier shall notify the affected Purchasing, and Materials Engineering activities (

14、with reasons) of the proposed changes. Upon notification of the Company, further instructions will be provided. Note: Suppliers should be prepared to provide test data and samples demonstrating compliance to this specification, if requested. Substance restrictions imposed by regulations or Company d

15、irection applies to the materials addressed by this document. The restrictions are identified in Restricted Substance Management Standard WSS-M99P9999-A1. 4. APPROVAL OF MATERIALS Materials defined by this specification for direct supply to the Company must have prior approval. Certain materials sub

16、contracted by part suppliers may also require prior approval. These include materials critical to the Companys business for regulatory, safety, environmental or compatibility requirements or contractual agreements. Suppliers desiring approval of their materials shall first obtain an expression of in

17、terest from Purchasing, Design or Materials Engineering activity. Upon request, the Supplier shall submit a completed copy of their laboratory test reports, signed by a qualified and authorized representative of the test facility, demonstrating full compliance with all the requirements of this specification.