1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 10 26 N-STATUS No known use. No Replacement Named D. DiGregorio, NA 2004 05 18 Revised Para 3.0 inserted; para 3.12 & 4 deleted 1963 04 12 Released F6-1046 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page

2、 1 of 2 OIL, TURBINE (300) ESF-M2C69-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material desired under this specification is a refined mineral oil compounded with suitable additives to improved its resistance to oxidation and its rust preventive characteristics. 2. APPLICATION This specification w

3、as released originally for oil used for impregnating sintered bronze bearings. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 VISCOSITY AT 40 C

4、58.0 - 64.0 mm2/s (ASTM D 445) 3.2 VISCOSITY INDEX, min 95 (ASTM D 567) 3.3 FLASH POINT, min 199 C (ASTM D 92) 3.4 FIRE POINT, min 230 C (ASTM D 92) 3.5 POUR POINT, max -13 C (ASTM D 97) 3.6 COLOR, max #5 (ASTM D 1500) 3.7 COPPER STRIP CORROSION pass (ASTM D 130, 100 C) 3.8 RUST PREVENTIVE CHARACTER

5、ISTICS no rust (ASTM D 665) 3.8.1 Synthetic Sea Water, min 24 h 3.9 OXIDATION STABILITY, min before oil reaches 1500 h (ASTM D 943) acid No. 2.0 ENGINEERING MATERIAL SPECIFICATIONESF-M2C69-A Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 2 3.10 RESISTANCE TO FOAMING No foam (ASTM D 892) 3.11 CONTAMINATION The material shall be free from acid, alkali, moisture, tarry or suspended matter, thickeners, or other foreign matter. It must also be free from objectionable odors.