FORD WRS-M1H1101-A3-2012 FABRIC ALCANTARA II SUSTAINABLE SUEDE PATTERN NON-WOVEN 27% PIR TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2012 7 23 Activated M. Dumitrescu, FNA Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 FABRIC, ALCANTARA II SUSTAINABLE WRS-M1H1101-A3 SUEDE PATTERN, NON-WOVEN 27% PIR 1. SCOPE The material def

2、ined by this specification is a needle punched non-woven fabric made from 0.016 tex polyester microfiber, impregnated with micro-porous polyurethane. The suede face fabric is backcoated and laminated to a backing fabric. 2. APPLICATION This specification was released originally for material used as

3、an insert for P415 2013 Model Year, seating application. 2.1 LIMITATIONS The face fabric could be perforated before lamination to the backing fabric. The selection of the backing fabric depends on perforation patterns. The product code of that backing scrim to be specified on approved source list (A

4、SL) for this specification. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.1.1 Recycled Content Materials approved to this specification must cont

5、ain 27% Post Industrial Recyclate (PIR) as defined by WRS-M99P42-A2 (Textile Materials, Identification of Recycled Content). The remaining portion of the material can come from virgin sources. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Weight (FLTM BN 106-01) Suede face fabric 355 30 g/m2 Backcoat with fl

6、ame retardant 100 10 g/m2 Woven backing fabric * or as approved 125+/-10 g/m2 by Materials Engineering and identified on ASL Alternative woven backing for climate seats * 95.5+/- 5 g/m2 * This is adhesively bonded by hot melt lamination ENGINEERING MATERIAL SPECIFICATION WRS-M1H1101-A3 Copyright 201

7、2, Ford Global Technologies, LLC Page 2 of 2 3.2.2 Fiber Construction (ASTM D1244) 0.016 tex polyester microfiber and 100% recycled polyester fiber layer (internal scrim) together are impregnated with micro-porous polyurethane 3.3 COMPOSITION (ASTM D629) Tolerance as specified in WSS-M8P18-A1/A4 Fac

8、e fabric 50% Polyester micro-fiber 27% Recycled polyester (100% recycled)23% Polyurethane Backing fabric 65% Polyester/35% cotton or as approved by Material Engineering 3.4 METHOD OF DYEING Piece dye or as approved by Materials Engineering 3.5 FINISHING OPERATIONS Heatset, inspection, backcoat, perf

9、.(optional) laminate w/backing fabric (optional), final inspection 4. GENERAL INFORMATION. This information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications 4.1 Purchasing department will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only.