FORD WRS-M1H1160-B1-2014 FABRIC FERRARI II PATTERN WARP KNIT 51% PIR PCR LAMINATED ELECRO-WELDED TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 00 2014 09 15 Released M. Dumitrescu, NA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 2 FABRIC, FERRARI II PATTERN, WARP KNIT, WRS-M1H1160-B1 51% PIR/PCR, LAMINATED, ELECRO-WELDED 1. SCOPE The m

2、aterial defined is a single needle bar knit polyester face fabric, laminated with foam and scrim and electro-welded. Material conforming to WRS-M1H1160-B1 contains 51% PIR/PCR (Post industrial/post consumer) recycled yarn. 2. APPLICATION This specification was released originally for material used a

3、s an interior trim fabric for 2015MY Mustang seat inserts. The material was originally approved laminated with foam and scrim and electro-welded. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirement

4、s For Production Materials (WSS-M99P1111-A). Materials with recycled content as defined by WRS-M99P42-A2 (Textile Materials, Identification of Recycled Content) should be used whenever technically feasible. 3.1.1 This specification must contain 51% recycled content as defined by WRS-M99P42-A2. The r

5、emaining portion of the material can come from virgin sources. 3.1.2 In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-B1/B2/B3/B4 as applicable. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, - 10 /+10 % tolerance (ASTM D3775) Wales 146 / 10 cm Courses

6、177 / 10 cm 3.2.2 Fabric Weight, - 10 / +10 % tolerance 305 g/m2 (FLTM BN 106-01) 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester ENGINEERING MATERIAL SPECIFICATION WRS-M1H1160-B1 Copyright 2014, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D1244) Face (A) 78 dtex (polyest

7、er yarn) Face (B) 78 dtex (polyester yarn) Middle 111 dtex (recycled textured polyester yarn) Back 78 dtex (polyester yarn) 3.5 METHOD OF DYEING Solution/Piece dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS Dye, tenter pad (resin), heatset, inspect, laminated,electrowelded Or a

8、s approved by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only.