FORD WRS-M1H1176-A1-2014 FABRIC ZIPLINE PATTERN FLAT WOVEN 36 % PCR PIR UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION DATE Action Revisions Rev. 0 2014 03 18 Released M.Dumitrescu, NA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 2 FABRIC, ZIPLINE PATTERN, FLAT WOVEN WRS-M1H1176-A1 36 % PCR/PIR, UNLAMINATED 1. SCOPE The material defined b

2、y this specification is a woven jacquard polyester face fabric. The material contains 36% PIR/PCR (post industrial/post consumer) recycled yarn. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for seat inserts on 2016MY Explorer (NA). The fabric

3、 was originally approved as backcoated and laminated with foam. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). Materials with recycled content as de

4、fined by WRS-M99P42-A2 (Textile Materials, Identification of Recycled Content) should be used whenever technically feasible. 3.1.1 This specification must contain 36% recycled content as defined by WRS-M99P42-A2. The remaining portion of the material can come from virgin sources. 3.1.2 In addition t

5、o the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-B1/B2/B3/B4 as applicable. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10 % tolerance (ASTM D3775) Warp 307 / 10 cm Weft 170 / 10 cm 3.2.2 Fabric Weight, +/- 10 % tolerance (FLTM BN 106-01) Face fabric 320 g/m2

6、 Backcoat 29 g/m2 Total 349 g/m2 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester Backcoat EVAENGINEERING MATERIAL SPECIFICATION WRS-M1H1176-A1 Copyright 2014, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D1244) Warp 167dtexf34 (textured polyester) x 3 Weft 167dtexf34 (100%

7、 recycled polyester) x 3 167dtexf34 (100% recycled polyester) x 3 3.5 METHOD OF DYEING Package dyed/Solution dyed or as approved by Materials Engineering, 3.6 FINISHED OPERATIONS Washing, drying,back coated or as approved by Materials Engineering. 4. GENERAL INFORMATION The information given below i

8、s provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that the material defined in this specification and shipped to any one assembly plant will be pro

9、duced by one supplier only. 4.2 If yarn is locally sourced it must meet the above fabric construction, composition and yarn construction. The fabric must also meet the requirements of WSS-M8P18-B1/B2/B3/B4. 4.3 Global strategy for this fabric is to use tri-laminate/foam & scrim construction in all regions