FORD WRS-M1H1187-A1-2014 FABRIC RACE TRACK PATTERN WARP KNIT 51% PIR PCR UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 00 2014 07 02 Released M. Dumitrescu, NA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 2 FABRIC, RACE TRACK PATTERN, WARP KNIT, WRS-M1H1187-A1 51% PIR/PCR, UNLAMINATED 1. SCOPE The material defin

2、ed is a single needle bar knit polyester face fabric, laminated with foam and scrim and electro-welded. Material conforming to WRS-M1H1187-A1 contains 51% PIR/PCR (Post industrial/post-consumer) recycled yarn. 2. APPLICATION This specification was released originally for material used as an interior

3、 trim fabric for Mustang VP 2016MY as an insert. The fabric was originally approved as laminated with foam and scrim and electro-welded. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Pro

4、duction Materials (WSS-M99P1111-A). Materials with recycled content as defined by WRS-M99P42-A2 (Textile Materials, Identification of Recycled Content) should be used whenever technically feasible. 3.1.1 This specification must contain 51% recycled content as defined by WRS-M99P42-A2. The remaining

5、portion of the material can come from virgin sources. 3.1.2 In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-(latest) as applicable. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, -10 /+10 % tolerance (ASTM D3775) Wales 150 / 10 cm Courses 180 / 10 cm 3

6、.2.2 Fabric Weight, - 10 / +10 % tolerance 305 g/m2 (FLTM BN 106-01) 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester ENGINEERING MATERIAL SPECIFICATION WRS-M1H1187-A1 Copyright 2014, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D1244) Face (A) 78 dtex (polyester yarn) Face

7、 (B) 78 dtex (polyester yarn) Middle 111 dtex (recycled textured polyester yarn) Back 78 dtex (polyester yarn) 3.5 METHOD OF DYEING Solution/Piece dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS Dye, tenter pad (resin), heatset,laminated,electro-welded Or as approved by Material

8、s Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only.