FORD WSA-M2P170-A2-2005 PAINT PERFORMANCE CORROSION HEAT RESISTANT COATING 450 MAX TO BE USED WITH FORD WSS-M99P1111-A (Shown on WSA-M2P170-A1 Supersedes ESEN-M91J8-B ESE-M99J1-A.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 10 28 Revised Completely revised; deleted 3.8 Para 3.1, 3.2, 3.12, 4 deleted 1993 06 29 NC00E10244447013 Released J.M. Greene, G. Stevens Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 PAINT PERF

2、ORMANCE, CORROSION/HEAT RESISTANT WSA-M2P170-A1 COATING, 150 C, max PAINT PERFORMANCE, CORROSION/HEAT RESISTANT WSA-M2P170-A2 COATING, 450 C, max PAINT PERFORMANCE, CORROSION/HEAT RESISTANT WSA-M2P170-A3 COATING, 650C, max 1. SCOPE These specifications define three levels of heat and corrosion resis

3、tant coatings for exhaust components. 2. APPLICATION WSA-M2P170-A1: Typical applications include chassis brackets and exhaust hangers where operating temperatures do not exceed 150 C. WSA-M2P170-A2: Originally released for cosmetic purposes on muffler rear heads and tail pipes where operating temper

4、atures do not exceed 450 C. WSA-M2P170-A3: To be used on exhaust components where exceptional heat and corrosion protection properties are required. Temperature resistance is 650 C maximum. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must

5、conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). All requirements of these specifications must be met with actual production intent components. 3.3 CLEANING All surfaces to be coated must be free from oil, grease, rust and other foreign materials. Phosphating

6、or other surface preparations must comply with the coating manufacturers recommendations. 3.4 FILM THICKNESS, Dry (FLTM BI 117-01, Eddy Mag 2000/Oxford CM1700 or equivalent) Coating thickness must be sufficient to meet all requirements of this specification. Each coating manufacturers thickness requ

7、irements are to be specified on the applicators Control Plan. ENGINEERING MATERIAL SPECIFICATIONWSA-M2P170-A1/A2/A3 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 3.5 COLOR A1 & A2 - Black or as specified on Engineering Drawing A3 -Gray 3.6 ADHESION Grade 0

8、 (FLTM BI 106-01, Method B) Adhesion tests to be performed 24 hours after force curing, per manufacturers recommendation. For air dry coatings, age samples for 72 hours prior to the adhesion test. 3.7 MATERIAL CURE Materials conforming to the specification shall be cured according to the coating man

9、ufacturers recommendation and must be listed on the applicators Control Plan. 3.10 HEAT RESISTANCE Heat cycle samples as follows: WSA-M2P170-A1 150 C, 1 hour, water quench (0 + 2 C) WSA-M2P170-A2 450 C, 1 hour, water quench (0 + 2 C) WSA-M2P170-A3 650 C, 1 hour, water quench (0 + 2 C) Upon removal,

10、the samples shall show no blistering, chipping, flaking or cracking or loss of adhesion. Adhesion tests are to be performed 24 hours after heat cycle testing (Par 3.6) and the samples must meet the Grade 0 requirement. 3.11 CORROSION RESISTANCE After cure and heat resistance (para 3.7 & 3.10), sampl

11、es shall be exposed to 10 cycles of FLTM BI 123-03 and must meet rust grade #6 or better per ASTM D 610 (red or white corrosion). For air dry coatings, age samples for 72 hours prior to corrosion testing. Components coated to these specifications must meet the Corporate Standard for Total Vehicle Corrosion per ARL 18-0034 (DVM-0161-18). Note: For -A3 Coating, white corrosion is acceptable.