FORD WSB-M1H644-A-2009 FABRIC NAUTILUS PATTERN KNIT TO BE USED WITH FORD WSS-M99P1111-A 《NAUTILUS图案的针织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2009 01 06 N-STATUS No Replacement B. Haggart, FNA 2003 03 31 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.10, 3.11, 4 deleted 1995 01 09 Released NB00I10043054414 B.H.C. A.J.S. Printed copies are uncontrolle

2、d Page 1 of 2 Copyright 2009, Ford Global Technologies, Inc. FABRIC, NAUTILUS PATTERN, KNIT WSB-M1H644-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a Nautilus pattern knit bodycloth of good quality and uniform composition. 2. APPLICATION This specification w

3、as released originally for material used as an interior trim fabric for the 1997 Tracer. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSB-M8P1-H. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must

4、conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 FABRIC CONSTRUCTION 3.3.1 Fabric Count, +/- 5 % tolerance (ASTM D 3887) Wales 7.1 wales/cm Courses 11.0 courses/cm 3.3.2 Fabric Weight, range 355 - 435 g/m2(FLTM BN 106-01) ENGINEERING MATERIAL SPECIFICATION

5、 WSB-M1H644-A Page 2 of 2 Copyright 2009, Ford Global Technologies, Inc. 3.4 COMPOSITION (ASTM D 629) Tolerance as specified in WSB-M8P1-H Fabric 100 % Polyester 3.5 YARN CONSTRUCTION (ASTM D 1244) Face (A & B & C) 16.7 tex f34 (polyester, space dye & yarn dye) Middle 16.7 tex f34 (polyester, soluti

6、on dye) Back 16.7 tex f34 (polyester, solution dye) 3.6 METHOD OF DYEING Yarn and solution dyed 3.7 FINISHING OPERATIONS Slit, brush, shear, dry, brush & shear 3.8 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute 3.9 STRETCH AND SET, %, range (SAE J855) Fabrics outside this range may be

7、 accepted provided they have been approved jointly by the Materials Engineering activity and the affected Design Engineering and Development activity. Stretch, range Wales Courses 0 - 23 0 - 23 Set, max* Wales Courses 5 9 *At no time shall the set exceed 40 % of the measured stretch unless approved jointly by the Materials Engineering activity and the affected Design Engineering and Development activity.