1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2014 11 24 N Status No replacement named D. Murtonen, NA 2003 01 10 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.12, 4 deleted 1993 05 27 NB00I100443054252 Released BCF J.D. Salow A.J. Stocki Page 1 of
2、2 Copyright 2014, Ford Global Technologies, Inc. FABRIC, VINYL COATED (PVC), WELL LINING WSB-M2F181-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a calendered polyvinyl chloride copolymer film laminated to a cotton drill fabric. 2. APPLICATION This specificat
3、ion was released originally for material used as a well lining for convertible tops. 3. REQUIREMENTS In addition to the requirements listed herein, this material shall meet all requirements of the WSB-M8P3-C, PERFORMANCE, FLEXIBLE POLYMERIC FILM, INTERIOR QUALITY material performance specification.
4、3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 APPEARANCE (FLTM BI 109-01) The color, pattern and finish shall match the approved master sample, or shall be as
5、specified on the engineering drawing. 3.5 BACKING FABRIC 100 % cotton drill Sulfur dyed black 3.6 WEIGHT, range (ASTM D 751, Sample Method) LSL USL Coating 339 g/m2 435 g/m2 (372 g/m2 average) Fabric 142 g/m2 175 g/m2 (158 g/m2 average) Total 542 g/m2 610 g/m2 (576 g/m2 average) ENGINEERING MATERIAL
6、 SPECIFICATION WSB-M2F181-A Page 2 of 2 Copyright 2002, Ford Global Technologies, Inc. 3.7 RESISTANCE TO TEAR, Trapezoid, min (ASTM D 1117) Warp 22 N (71 N average) Fill 22 N (66 N average) 3.8 BREAKING STRENGTH, min (ASTM D 751, Grab Method) Warp 222 N (448 N average) Fill 198 N (285 N average) 3.9
7、 ADHESION OF VINYL FILM TO BACKING FABRIC, min (FLTM BN 151-05, Method A/ ISO 2711) Warp & Fill 18 N/50 mm, width (24 N/50 mm average) 3.10 WICKING None (SAE J913, 4 h, solution b) 3.11 XENON WEATHEROMETER, min (SAE J1885, AATCC Evaluation Procedure 1/ISO 105-A02) 225.6 kJ Rating 4.0 5. GENERAL INFORMATION The information below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 RECYCLING CODE PVC,LF