FORD WSD-M1H665-C2-2008 FABRIC BURR PATTERN WOVEN JACQUARD 6 mm - TO BE USED WITH FORD WSS-M99P1111-A 《毛边（BURR）图案的6 mm厚提花机织织物 与标准FORD WSS-M99P1111-A一起使用 列于标准FORD WSD-M1H665-A上》.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2008 11 18 N-STATUS No Replacement L. Schmalz, FNA / M. Montogomery, FOE 2003 03 19 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.18, 3.19, 4 deleted 1995 04 28 C10460378 Released Printed copies are unco

2、ntrolled Page 1 of 5 Copyright 2008, Ford Global Technologies, Inc. FABRIC, BURR PATTERN, WOVEN JACQUARD, UNLAMINATED WSD-M1H665-A FABRIC, BURR PATTERN, WOVEN JACQUARD, 3 mm WSD-M1H665-B1 FABRIC, BURR PATTERN, WOVEN JACQUARD, 6 mm WSD-M1H665-B2 FABRIC, BURR PATTERN, WOVEN JACQUARD, 3 mm WSD-M1H665-C

3、1 FABRIC, BURR PATTERN, WOVEN JACQUARD, 6 mm WSD-M1H665-C2 FABRIC, BURR PATTERN, WOVEN JACQUARD, 6 mm WSD-M1H665-D2 FABRIC, BURR PATTERN, WOVEN JACQUARD, HFW WSD-M1H665-G FABRIC, BURR PATTERN, WOVEN JACQUARD, HFW WSD-M1H665-H FABRIC, BURR PATTERN, WOVEN JACQUARD, HFW WSD-M1H665-J FABRIC, BURR PATTER

4、N, WOVEN JACQUARD, HFW WSD-M1H665-K NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by these specifications is a woven jacquard polyester face fabric which can be flame laminated to polyester or polyether urethane foam and backed with a knitted fabric. It can also be backed with an HFW w

5、eldable backcoating. 2. APPLICATION WSD-M1H665-A is used for molded headrests and also adhesive coated for use on inner door panels. WSD-M1H665-B1, B2, C1, C2, are for seat wearing surfaces. WSD-M1H665-D2 is used for adhesively bonded door and quarter trim panel applications WSD-M1H665-G, H, J R 500

6、 dtex Weft 250 dtex (polyester, semi-dull, spun) x 2; R 500 dtex ENGINEERING MATERIAL SPECIFICATION WSD-M1H665-A/B1/B2/C1/C2/D2/ G/H/J/K Page 3 of 5 Copyright 2008, Ford Global Technologies, Inc. 3.7 METHOD OF DYEING Yarn dyed and spun dyed or as approved by Materials Engineering 3.8 FINISHED OPERAT

7、IONS As approved by Materials Engineering 3.9 REQUIREMENTS FOR POLYESTER FOAM As specified in WSD-M2D43-A4 3.10 REQUIREMENTS FOR POLYETHER FOAM As specified in WSD-M2D43-A2 3.11 REQUIREMENTS FOR THE BACKING FABRIC As pecifed inWSD-M9H136-A 3.12 REQUIREMENTS FOR THE FLAME LAMINATED MATERIAL 3.12.1 Th

8、ickness, range (ASTM D 1777, circular presser foot area 645 mm2, 2.8 g Force, 43 Pa pressure) WSD-M1H665-B1 3.0 +/- 1.0 mm WSD-M1H665-B2 6.0 +/- 1.0 mmWSD-M1H665-C1 3.0 +/- 1.0 mm WSD-M1H665-C2 6.0 +/- 1.0 mmWSD-M1H665-D2 6.0 +/- 1.0 mm 3.12.2 Compressed Thickness (ASTM D 1777, circular presser foot

9、 area 645 mm2, 1 kg force, 5 s dwell) WSD-M1H643-D2 2.45 +/- 0.3 mm 3.12.3 Weight, range WSD-M1H665-B1 430 +/- 40 g/m2WSD-M1H665-B2 540 +/- 40 g/m2WSD-M1H665-C1 410 +/- 40 g/m2WSD-M1H665-C2 500 +/- 40 g/m2WSD-M1H665-D2 510 +/- 40 g/m2ENGINEERING MATERIAL SPECIFICATION WSD-M1H665-A/B1/B2/C1/C2/D2/ G/

10、H/J/K Page 4 of 5 Copyright 2008, Ford Global Technologies, Inc. 3.12.4 Stretch and Set, %, range (SAE J855) Stretch (WSD-M1H665-B1, B2, C1, C2) Warp 1 - 10 % Weft 1 -10Set (B1, B2, C1, C2) Warp 0 - 5 % Weft 0 -53.12.5 Modulus, max (WSD-M1H652-D2) Strain, 6 % 280 N 3.13 REQUIREMENTS FOR THE BACKCOAT

11、ED MATERIAL (WSD-M1H665-G) 3.13.1 Weight, min (FLTM BN 106-01) PVC film 100 g/m2Face fabric weight as specified in para 3.4.2. Or an engineering approved alternative. 3.14 REQUIREMENTS FOR BACKCOATED MATERIAL (WSD-M1H665-H) 3.14.1 Weight, min (FLTM BN 106-01) Acrylic Backcoating 35 g/m2Face fabric a

12、s specified in para 3.4.2. Or an engineering approved alternative. ENGINEERING MATERIAL SPECIFICATION WSD-M1H665-A/B1/B2/C1/C2/D2/ G/H/J/K Page 5 of 5 Copyright 2008, Ford Global Technologies, Inc. 3.15 REQUIREMENTS FOR THE BACKCOATED MATERIAL (WSD-M1H665-J) 3.15.1 Weight, min (FLTM BN 106-01) PVC B

13、ackcoating 40 g/m2Face fabric weight as specified in para 3.4.2 Or an engineering approved alternative. 3.16 REQUIREMENTS FOR THE BACKCOATED MATERIAL (WSD-M1H665-K) 3.16.1 Weight, min (FLTM BN 106-01) PU Backcoating 40 g/m2Face fabric weight as specified in para 3.4.2. Or an engineering approved alt

14、ernative. 3.17 FLAMMABILITY (ISO 3795/SAE J369) Burn rate, max 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of these specifications. 5.1 Purchase departments will ensure that both materials defined in these specifications and shipped to any one assembly plant will be produced by one supplier only.