FORD WSD-M2D378-A6-2004 THERMOPLASTIC ELASTOMER (TEO) POLYOLEFIN EPDM RUBBER MODIFIED 66 DUROMETER A HARDNESS TO BE USED WITH FORD WSS-M99P1111-A 《硬度66 A的三元乙丙橡胶(EPDM)橡胶改性热塑性弹性体聚烯.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2004 11 22 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.4, 3.20 & 4 2001 03 05 Revised Revised Para. 3.9 Note & updated B Hennessey 1993 05 26 Released C10301724 P Thomas Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, L

2、LC Page 1 of 4 THERMOPLASTIC ELASTOMER (TEO) WSD-M2D378-A6 POLYOLEFIN, EPDM RUBBER MODIFIED 66 DUROMETER A HARDNESS THERMOPLASTIC ELASTOMER (TEO) WSD-M2D379-A6 POLYOLEFIN, EPDM RUBBER MODIFIED 76 DUROMETER A HARDNESS 1. SCOPE The materials defined by these specifications are thermoplastic elastomers

3、 of nominal instantaneous Durometer A hardnesses 66 and 76 having good long term resistance to heat at temperatures up to 125 C. Being thermoplastic, the material will soften and creep at temperatures exceeding 165 C. These materials provide low level fade resistance and have improved flow character

4、istics during injection molding. 2. APPLICATION These specifications were released originally for materials used for general interior components which are not color keyed and where there is no specific fade resistance requirements such as covered cup holders and pen holders on CDW27. The materials c

5、an be processed by conventional thermoplastics molding techniques such as injection molding, extrusion and blow-molding. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Material

6、s (WSS-M99P1111-A). 3.3 DYNAMIC MECHANICAL ANALYSIS Ford Motor Company, at its option, may establish shear modulus/damping vs. temperature curves plotted for -50 to +150 C temperature range for material/parts supplied to this specification. The shear modulus and damping curves established for initia

7、l approval shall constitute the reference standard and shall be kept on file at the designated material laboratory. All samples shall produce shear modulus and damping curves that correspond to the reference standard when tested under the same conditions. 3.5 PREPARATION OF TEST SPECIMENS Unless oth

8、erwise specified, all tests shall be conducted on specimens die cut from injection molded plaques 150 x 100 x 2.0 +/- 0.2 mm. The plaques shall be molded according to ISO 294 and film gated along the upper 100 mm edge, and preceded by a 0.8 mm diameter pin gate. No annealing allowed, unless specifie

9、d otherwise. ENGINEERING MATERIAL SPECIFICATIONWSD-M2D378-A6WSD-M2D379-A6Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 2 of 4 378-A6 379-A6 3.6 DENSITY, +/- 0.05 g/cm3(ISO 1183, Method A /ASTM D 792, Method A1) 0.97 0.96 3.7 HARDNESS, INTERNATIONAL (ISO 48/ASTM D

10、 1415) 66 - 77 76 - 86 3.8 HARDNESS, DUROMETER A (ISO 868/ASTM D 2240, instantaneous, plied-up specimen) 61 - 72 71 - 81 3.9 TENSILE STRENGTH, MPa, min (ISO R 527, type 2/ASTM D 412, Die C, 500 mm/min test speed. Measured Parallel to Flow) 3.3 4.4 3.9.1 Elongation at Break, %, min (Test per para 3.9

11、) 160 200 3.10 MODULUS AT 100% ELONGATION, min (Test per para 3.9) 2.1 2.5 3.11 TEAR STRENGTH, kN/m, min (ISO 34, Method B, procedure a/ ASTM D 624, Die C, tear direction as below) 3.11.1 Parallel to Flow 11 15 3.11.2 Perpendicular to Flow 11 15 3.12 COMPRESSION SET, %, max (ISO 815, Large Type plie

12、d specimen/ASTM D 395, Method B, Type 1 plied specimen) 3.12.1 22 h at 70 +/- 1 C 40 40 3.12.2 70 h at 80 +/- 1 C 60 60 3.13 BRITTLENESS POINT, C, max (ISO 812, Type B specimen/ ASTM D 2137, Method A) -60 -60 ENGINEERING MATERIAL SPECIFICATIONWSD-M2D378-A6WSD-M2D379-A6Printed copies are uncontrolled

13、 Copyright 2004, Ford Global Technologies, LLC Page 3 of 4 378-A6 379-A6 3.14 OZONE RESISTANCE, Rating, max (FLTM BP 101-01, at 20% elongation) 0 0 3.15 HEAT AGING (ISO 188/ASTM D 573, 150 +/- 50 air changes/h, 1,000 h at 125 +/- 2 C. Unaged property values shall be determined at the time of the age

14、d properties determination.) Hardness Change, max + 10 + 10 Tensile Strength Change, %, max +/- 30 +/- 30 Elongation Change, %, max +/- 30 +/- 30 3.16 IMMERSION IN OIL NO. 1 (ISO 1817/ASTM D 471, 168 h at 125 +/- 1 C) Hardness Change, max -25 -25 Tensile Strength Change, %, max -50 -50 Elongation Ch

15、ange, %, max -75 -75 Volume Change, %, max +90 +80 3.17 IMMERSION IN OIL NO. 3 (ISO 1817/ASTM D 471, 168 h at 125 +/- 1 C) Hardness Change, max -35 -35 Tensile Strength Change, %, max -65 -60 Elongation Change, %, max -95 -95 Volume Change, %, max +160 +150 3.18 FOGGING (OPTIONAL) (SAE J1756, 3 h at

16、 100 C heating, 21 C cooling plate, post test conditioning 1 h and 16 h) Fog Number, min 70 70 Formation of clear film, droplets or crystals is cause for rejection. ENGINEERING MATERIAL SPECIFICATIONWSD-M2D378-A6WSD-M2D379-A6Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, L

17、LC Page 4 of 4 3.19 FLAMMABILITY (ISO 3795) Burn Rate, max 100 mm/minute The specimen size required for material approval is 355 x 100 x 1.0 +/- 0.1 mm with a smooth surface. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements o

18、f these specifications. 378-A6 379-A6 5.1 COEFFICIENT OF LINEAR THERMAL EXPANSION, -6/C (ASTM D 696) 270 230 5.2 MOLD SHRINKAGE (ISO 2577, 150 x 100 x 2.0 +/- 0.2 mm injection molded specimen) 5.2.1 Molding Shrinkage After 48 h at 23 +/- 2 C, mm/mm . Length 0.024 0.022 . Width 0.023 0.022 5.2.2 Post Shrinkage (Separate specimens required for each test) After 48 h at 110 +/- 2 C . Length 0.009 0.009 . Width 0.007 0.006 5.3 HARDNESS, DUROMETER (ISO 868/ASTM D 2240, 5 second delay, plied-up specimen) 59 - 70 69 - 79 5.4 RECYCLING CODE TEO