FORD WSD-M2D448-A2-2009 POLYACRYLIC RUBBER (ACM) HOT AIR HOT OIL AND COMPRESSION STRESS RELAXATION RESISTANT 65 IRHD TO BE USED WITH FORD WSS-M99P1111-A 《耐热空气、热油和压缩应力松弛的IRHD硬度为65.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 08 28 A2 N-STATUS No known use. No Replacement Named C. Mracna, NA 2004 09 30 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.12 & 4 1991 08 09 Released C10155132Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC

2、 Page 1 of 3 POLYACRYLIC RUBBER (ACM), HOT AIR, HOT OIL AND WSD-M2D448-A COMPRESSION STRESS RELAXATION RESISTANT, 50 IRHD POLYACRYLIC RUBBER (ACM), HOT AIR, HOT OIL AND WSD-M2D448-A2 COMPRESSION STRESS RELAXATION RESISTANT, 65 IRHD NOT TO BE USED FOR NEW DESIGN 1. SCOPE The materials described by th

3、ese specifications are 50 IRHD (WSD-M2D448-A) and 65 IRHD (WSD-M2D448-A2) polyacrylic rubber compounds with good resistance to hot air and hot oil. The materials have excellent resistance to compressive stress relaxation at temperatures up to 135 C. WSD-M2D448-A material also has excellent resistanc

4、e to splitting or bursting under combined conditions of compressive strains up to 60% and temperatures up to 150 C. 2. APPLICATION These specifications were released originally for material used as an intercooler tank gasket and O-rings or as shown on the engineering drawing 3. REQUIREMENTS 3.0 STAN

5、DARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 MATERIAL TESTING 3.4.1 Preparation of Test Specimens Whenever possible, all test specimens shall be die-cut from the fini

6、shed parts. When not feasible, specimens cut from molded test sheets manufactured from the same material and with equivalent state of cure to molded parts are recommended. The test sheets shall have the following dimensions: 150 x 150 mm, min x 2.0 +/- 0.2 mm 3.5 ORIGINAL PROPERTIES A A2 3.5.1 Hardn

7、ess, International 45 - 55 65 - 70 (ISO 48) 3.5.2 Tensile Strength, MPa, min 8 10 (ISO 37, Type 1 dumbell) 3.5.3 Elongation at break, %, min 200 100 (Test Method according to para 3.5.2) 3.5.4 Modulus at 100% Elongation, MPa 2.0 - 3.5 6.0 - 7.5 (Test Method according to para 3.5.2) ENGINEERING MATER

8、IAL SPECIFICATIONWSD-M2D448-A/A2Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 3 A A2 3.5.5 Ozone Resistance, Rating, max 0 0 (FLTM BP 101-01, Procedure A) 3.5.6 Compression Set, %, max 35 35 (ISO 815, Sample A) except 25% compression, plied-up specimens, 70

9、h at 135 +/- 2 C) 3.6 HEAT AGED (ISO 188, 150 +/- 50 air changes/h, 168 h at 150 +/- 2 C) 3.6.1 Hardness Change 0 to +10 3.6.2 Tensile Strength Change, max -20% 3.6.3 Elongation at Break Change, max -35% 3.6.4 Visual Evaluation No surface tackiness or cracks when folded flat against itself. 3.7 HEAT

10、 AGED (ISO 188, 150 +/- 50 air changes/h, 1,000 h at 135 +/- 2 C) 3.7.1 Hardness Change 0 to +10 3.7.2 Tensile Strength Change, max -20% 3.7.3 Elongation at Break Change, max -35% 3.7.4 Visual Evaluation No surface tackiness or cracks when folded flat against itself. 3.8 IMMERSION IN OIL No. 1 (ISO

11、1817, 168 h at 150 +/- 2 C) 3.8.1 Hardness change +/- 10 3.8.2 Tensile Strength Change, max -20% 3.8.3 Elongation at Break Change, max -30% 3.8.4 Volume Change -5 to +5% 3.8.5 Visual Evaluation No surface tackiness or cracks when folded flat against itself. ENGINEERING MATERIAL SPECIFICATIONWSD-M2D4

12、48-A/A2Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 3 of 3 3.9 IMMERSION IN OIL No. 3 (ISO 1817, 168 h at 150 +/- 2 C) 3.9.1 Hardness change +/- 15 3.9.2 Tensile Strength Change, max -15% 3.9.3 Elongation at Break Change, max -20% 3.9.4 Volume Change 0 to +25% 3

13、.9.5 Visual Evaluation No surface tackiness or cracks when folded flat against itself. 3.10 COMPRESSION STRESS RELAXATION (FLTM BP 116-02 at 25% compression) Test Method: Measure the initial back-force (Fo) after 30 minutes at 23 +/- 2 C. Age at 135 +/- 2 C and take back-force (Ft) measurements at 2

14、3 +/- 2 C after 24, 48, 96, 168 h and thereafter every 168 h until a total elapsed test time of 1,000 h has been completed. Plot Ft against log 10 time in hours. - Fo -A -A2 F1000/Fo, min 0.20 0.20 3.11 FINISHED PART (A only) 3.11.1 Compression Burst No splits or cracks in any of the samples Test Me

15、thod: Cut the 4 corners from each of 5 tank gaskets such that the test pieces have arms 15 +/- 2 mm in length, (or take 5 O-Rings as appropriate). Compress between metal plates by 60 +/- 2% (40 +/- 2% for O-Rings) of the original thickness. Age for 24 hours at 150 C, cool, release compression and examine both internally and externally.