FORD WSK-M2D389-A3-2009 POLYURETHANE (PUR) FOAM OPEN CELL TO BE USED WITH FORD WSS-M99P1111-A 《开孔式聚氨酯（PUR）泡沫 与标准FORD WSS-M99P1111-A一起使用 ［使用 FORD WSS-M99P32-C］》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 08 27 N-STATUS Replaced by WSS-M99P32-C C. Mracna, NA 2004 09 15 Revised Para 3.0 inserted; para 3.1, 3.2, 3.3, 3.6, 3.7 & 4 deleted 1989 11 17 Released SM/EQ9859 TP K. Gerhards Printed copies are uncontrolled Copyright 2009, Ford Global

2、Technologies, LLC Page 1 of 2 POLYURETHANE (PUR) FOAM, OPEN CELL WSK-M2D389-A3 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a completely open cell polyurethane foam with 110 pores per 100 mm. 2. APPLICATION This specification was released originally for materi

3、al used as element crankcase vent oil seperator. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 APPEARANCE The foam shall have a homogeneous med

4、ium sized cell structure with no large voids or cracks which may impair the serviceability of the part. 3.5 MOLDED TEST SPECIMEN 3.5.1 Density, min 31 kg/m3(ISO 845/ASTM D 3574, Test A) 3.5.2 Tensile Strength, min 150 kPa (ISO 1798/ASTM D 3574, Test E, 5 specimens minimum) 3.5.2.1 Elongation, min 25

5、0% (test acc. to para 3.5.2) 3.5.3 Compression Set, max 15% (ISO 1856, Method A/ASTM D 3574, Test D, 22 h at 70 C, 50% deflection, 3 specimens, minimum) 3.5.4 Compression Deflection Stress 2.5 - 4.5 kPa (ISO 3386/1 at 40% compression, specimen size 100 x 100 x 50 mm, test speed 100 +/- 20 mm/min) 3.

6、5.5 Humidity Ageing (Autoclave) (ISO 2440/ASTM D 3574, Test J, 3 h at 105 C) ENGINEERING MATERIAL SPECIFICATIONWSK-M2D389-A3 Printed copies are uncontrolled Copyright 2004, Ford Global Technologies, LLC Page 2 of 2 3.5.5.1 Compression Deflection Stress Change, max +/- 35% (Test acc. to para 3.5.4) 3

7、.5.6 Cell Count 110 +/- 20 cells/100 mm Test Method: Cell count to be determined on a 1 mm thick sample placed on an overhead projector. 3.5.7 Fogging, min (FLTM BO 116-03) Fog Number, min 70 3.5.8 Odor, max Rating 2 (FLTM BO 131-01/SAE J1351) 3.5.9 Ash Content, max 1% (ISO 247, Method B/ASTM D 1278, 800 +/- 25 C) 3.5.10 FLAMMABILITY (ISO 3795) Burn Rate, max 100 mm/minute