FORD WSK-M2G400-B-2014 ADHESIVE TWO PACK EPOXY SOLVENT FREE REPAIR COMP B TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSK-M2G400-A).pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 3 2014 07 08 Revised Added Weldability, see Summary of Revision J.Herl, EU 2002 12 10 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.11, 3.12, 4 deleted 1990 06 01 Released EP00E01031536000 B. Lange Conc. J. Schult, FOE Controlled doc

2、ument at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 3 ADHESIVE, TWO PACK, EPOXY, SOLVENT FREE, REPAIR, COMP A WSK-M2G400-A ADHESIVE, TWO PACK, EPOXY, SOLVENT FREE, REPAIR, COMP B WSK-M2G400-B 1. SCOPE The materials defined by these specifications are the separate parts of a two

3、 pack, epoxy base, solvent-free and room temperature curing structural metal to metal adhesive. WSK-M2G400-A is a modified epoxy resin based on Bisphenol A. WSK-M2G400-B is a modified polyamine hardener. 2. APPLICATION These specifications were released originally for materials used for bonding roof

4、 to body side panel (cold rolled steel, sanded and wiped by cleaning solvent) only for repair. Mechanical structural adhesive properties are dependent on bondline thickness. In the uncured state, the adhesive can be welded. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material

5、suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COMPOSITION 3.2.1 Resin WSK-M2G400-A Modified epoxy, based on Bisphenol A 3.2.2 Hardener WSK-M2G400-B Modified polyamine 3.2.3 Pigments WSK-M2G400-A/B Pigments to obtain the

6、 desired color 3.3 MATERIAL PROPERTIES WSK-M2G400-A WSK-M2G400-B 3.3.1 Color undefined undefined 3.3.2 Solids, (FLTM BV 150-10) 97 % min 93 % min 3.3.3 Ash, (FLTM BV 150-10) 30% 42% 3.3.4 Density, kg/L, (ASTM D 792) 1.2 - 1.5 1.2 - 1.5 3.3.5 Mixing Ratio, by Volume 100 100 3.3.6 Viscosity (FLTM BV 1

7、03-01) 60s 180s 3.4 FLOW less than 3 mm (Fig. 1 of FLTM BV 153-01, freshly mixed components, test at 23 +/- 2 C) ENGINEERING MATERIAL SPECIFICATION WSK-M2G400-A/B Copyright 2014, Ford Global Technologies, LLC Page 2 of 3 3.5 PREPARATION OF TEST PANELS 3.5.1 Prior to application, metal surfaces must

8、be cleaned with acetone to remove oils, dirt and moisture before and after sanding (grinding). 3.5.2 Application of Material by Tube Gun or Cartridge Film Thickness: 0.1 0.3 mm To be Cured: at 23 C for 48 h or at 80 C for 30 minutes 3.6 RESISTANCE PROPERTIES Test panels and parts prepared with mater

9、ials according to this specification shall meet all requirements of performance specification WSK-M11P47-A1. 3.7 WELDING ACCEPTANCE TEST Adhesives released to WSK-M2G400-A/B must be weldable. After application follow up welding operations must be executed within two (2) hours. Within these two (2) h

10、ours the adhesive film shall have sufficient conductibility to have a spot weld applied to the metal beneath the film. The tests must be executed according to FLTM BV 109-01 with the following changes: - Application of material by gun or cartridge - 25 coupon assemblies per condition - Steel substra

11、tes only - Assembly aged at 23 +/- 2 C for 2 hours - The investigation (point 6 in FLTM BV 109-01) after 30 days is not required. 3.8 QUALITY The material shall be a smooth homogeneous mixture, free from foreign materials. It must be adaptable for application in accordance with the appropriate Ford

12、Motor Company Process Specification. The adhesive must be compatible with all related materials. 3.9 STORAGE STABILITY 1 year (From date of receipt at Ford Motor Company) During the storage at ambient temperatures between 5 and 32 C in sealed unopened containers out of direct sunlight the material a

13、s supplied shall not liver and must be free from settling. After the storage the material must pass all specification requirements. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for question

14、s concerning Engineering Material Specifications. 4.1 POT LIFE, MIXED COMPONENTS, Greater than 60 minutes (100 g sample, 23 +/- 2 C) ENGINEERING MATERIAL SPECIFICATION WSK-M2G400-A/B Copyright 2014, Ford Global Technologies, LLC Page 3 of 3 5. SUMMARY OF REVISIONS 2014 07 08 Changed color to undefin

15、ed Re-numbered Added 3.9 Welding Acceptance Test according to FLTM BV 109-01 Revised 4.1 Pot Life increased from 15 to 60 min. Lower film thickness max from 7.0 mm to 0.3 mm 1991 03 01 Revised EP00E01089482000. B. Lange concurred J. Schult 2002 12 10 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.11, 3.12, 4 deleted