FORD WSK-M4D799-A-2012 POLYETHYLENE (PE) MEDIUM DENSITY LOW MELT FLOW RATE MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A 《中等密度 低熔态流动率的聚乙烯(PE)模塑材料 与福特WSS-M99P1111-A 一起使用》.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 02 2012 02 07 N Status No replacement named A. Pan, APA 2006 03 13 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.8, 3.9 aluminum foil, 180 - 200 C molding temperature, 15 +/- 2 C/min cooling rate. The values of this specification are bas

2、ed on unannealed specimens. 3.5.2 Density 0.925 - 0.940 g/cm3 (ISO 1183, Method A/ASTM D 792, Method A1) 3.5.3 Tensile Strength at Yield, min 10 MPa (ISO R 527/ASTM D 638M, 150 min x 10 x 4.0 +/- 0.2 mm specimen, 50 mm/minute test speed) 3.5.3.1 Elongation at Yield, min 200% (Test Method according t

3、o para 3.5.3) 3.5.4 Flexural Modulus, min 330 MPa (ISO 178/ASTM D 790M, Method I, Procedure A, 80 x 10 x 4.0 +/- 0.2 mm specimen, 64 mm support span) ENGINEERING MATERIAL SPECIFICATION WSK-M4D799-A Copyright 2012, Ford Global Technologies, LLC Page 2 of 4 3.5.5 Shear Modulus at 23 C 169 - 254 MPa (A

4、STM D 4065, forced constant amplitude, fixed frequency of 1 Hz +/- 15%, strain level below 1%. Specimen approx. 60 x 10 x 4.0 +/- 0.2 mm cut from the center of specimen A.). Additionally, a Shear Modulus vs. Temperature curve shall be plotted for -50 to +100 C temperature range, at 5 C minimum inter

5、vals. The plotted curve must be within tolerance range shown on page 4. 3.5.6 Impact Strength, Izod, min (ISO 180, Method A/ASTM D 256, Method A, 80 x 10 x 4.0 +/- 0.2 mm specimen, 10 specimens for each test) 3.5.6.1 At 23 +/- 2 C No break 3.5.6.2 At -20 +/- 2 C 7 kJ/m2 3.5.6.3 At -40 +/- 2 C 2 kJ/m

6、2 The test specimens must be conditioned for minimum of 6 h at the above specified temperature prior to impact test. Low temperature testing shall be done within the cold box, if not possible, test can be conducted outside, but within 5 s. 3.5.7 Heat Deflection Temperature, min 40 C (ISO 75/ASTM D 6

7、48, 120 x 10 x 4.0 +/- 0.2 mm specimen. At 0.45 MPa) 3.5.8 Heat Aging Performance (ISO 188/ASTM D 573, 150 +/- 50 air changes/h, 1000 h at 100 +/- 2 C. Unaged property values shall be determined at the time of the aged properties determination) 3.5.8.1 Tensile Strength Change +/- 15% (Test Method pe

8、r para 3.5.3) 3.5.8.2 Impact Strength, Izod Change No break (Test Method per para 3.5.6.1, specimens to be notched before heat aging) 3.6 FOGGING (FLTM BO 116-03) Fog Number, min 80 Formation of excessive amounts of clear film or droplets is cause for rejection. 3.7 FLAMMABILITY (ISO 3795) Burn Rate

9、, max 100 mm/minute The specimen size required for material approval is 355 x 100 x 1.0 +/- 0.1 mm with a smooth surface. ENGINEERING MATERIAL SPECIFICATION WSK-M4D799-A Copyright 2012, Ford Global Technologies, LLC Page 3 of 4 5. GENERAL INFORMATION The information given below is provided for clari

10、fication and assistance in meeting the requirements of this specification. 5.1 COEFFICIENT OF LINEAR THERMAL EXPANSION 25-5/C (ASTM D 696) 5.2 MOLD SHRINKAGE (ISO 2577, approx. 150 x 100 x 3.2 +/- 0.2 mm injection molded specimen) 5.2.1 Molding Shrinkage . After 48 h at 23 +/- 2 C 2.0% 5.2.2 Post Shrinkage (Separate specimens required for each test) . After 48 h at 80 C 1.0% . After 30 minutes at 120 C 2.0% 5.3 RECYCLING CODE SAE PE OPTIONAL ENGINEERING MATERIAL SPECIFICATION WSK-M4D799-A Copyright 2012, Ford Global Technologies, LLC Page 4 of 4