FORD WSK-M4D829-A-2006 POLYAMIDE 12 (PA12) HEAT STABILIZED 30% GLASS FIBER REINFORCED MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A 《受热稳定、30%玻璃纤维增强的聚酰胺12成型料 与标准FORD WSS-M.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 04 11 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.8, 3.9 & 4 1991 11 04 Released EP00E01089490000 M. Siewert Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 5 POLYAMIDE 12 (PA12), HEAT STABILIZED 30%

2、GLASS WSK-M4D829-A FIBER REINFORCED MOLDING COMPOUND 1. SCOPE The material defined by this specification is a heat stabilized 30% glass fiber reinforced polyamide 12 molding compound. 2. APPLICATION This specification was released originally for material used for bush of link arm w/s wiper drive arm

3、. NOTICE: This material absorbs and retains moisture. Part design and tolerances must accommodate changes in part dimensions and physical properties due to moisture absorption or loss in the service/assembly environment. 3. REQUIREMENT 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material supp

4、liers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 CONDITIONING AND TEST CONDITIONS All test values indicated herein are based on material and specimens with moisture content not exceeding 0.2% (test according to ISO 960, Method

5、 B/ASTM D 789). All test materials immediately after processing have to be sealed in containers that are impermeable to water vapor. If the moisture content exceeds 0.2%, condition the material for a minimum of 16 h at 40 - 50 C at a reduced pressure below 133 Pa. Conduct tests in a controlled atmos

6、phere of 23 +/- 2 C and 50 +/- 5% relative humidity. Individual specimens shall not be removed from closed containers until immediately before testing. 3.4 MOLDING COMPOUND 3.4.1 Glass Fiber Content 28 - 32% (ISO 3451/4, test temperature 600 +/- 25 C, test portion 1 g) 3.4.2 Melt Temperature 175 - 1

7、81 C (ISO 1218, Method B/ASTM D 789, or DSC - ASTM E 794) ENGINEERING MATERIAL SPECIFICATIONWSK-M4D829-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 5 3.5 MOLDED TEST SPECIMEN 3.5.1 Preparation of Test Specimens Unless otherwise specified all tests shall b

8、e carried out on injection molded one-end gated test specimens. The following dimensions are required: A. 150 min x 10 x 4.0 +/- 0.2 mm (Tensile Bar, ISO 3167) B. 120 x 10 x 4.0 +/- 0.2 mm Specimens with shorter dimensions shall be cut from the center portion of the test specimen A and/or B. The spe

9、cimens shall be prepared according to ISO 294. No annealing allowed. 3.5.2 Density 1.22 - 1.26 g/cm3(ISO 1183, Method A/ASTM D 792, Method A1) 3.5.3 Tensile Strength at Max Load, min 55 MPa (ISO R 527/ASTM D 638M, 150 x 10 x 4.0 +/- 0.2 mm specimen, 5 mm/minute test speed) 3.5.4 Flexural Modulus, mi

10、n 3.2 GPa (ISO 178/ASTM D 790M, Method I, Procedure A, 80 x 10 x 4.0 +/- 0.2 mm specimen, 2 mm/min test speed, 64 mm support span, the radius of the loading nose 5.0 +/- 0.1 mm and of the supports 2.0 +/- 0.2 mm) 3.5.5 Shear Modulus at 23 C 0.87 - 1.46 GPa (ASTM D 4065, forced constant amplitude, fi

11、xed frequency of 1 Hz +/- 15%, strain level below 1%. Specimen approx. 60 x 10 x 4.0 +/- 0.2 mm cut from the center of specimen A. Specimen length between clamps 35-40 mm. Soak time at each temperature interval - 3 minutes minimum). Additionally, a Shear Modulus vs. Temperature curve shall be plotte

12、d for -50 to +160 C temperature range, at 5 C minimum intervals. The plotted curve must be within tolerance range shown on page 5. 3.5.6 Impact Strength, Izod, min (ISO 180, Method A/ASTM D 256, Method A, 80 x 10 x 4.0 +/- 0.2 mm specimen, 10 specimens for each test) 3.5.6.1 At 23 +/- 2 C 5 kJ/m23.5

13、.6.2 At -40 +/- 2 C 4 kJ/m2The test specimens must be conditioned for minimum of 6 h at the above specified temperature prior to impact test. Low temperature testing shall be done within the cold box, if not possible, test can be conducted outside, but within 5 s. ENGINEERING MATERIAL SPECIFICATIONW

14、SK-M4D829-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 3 of 5 3.5.7 Heat Deflection Temperature, min (ISO 75/ASTM D 648, 120 x 10 x 4.0 +/- 0.2 mm specimen, at standard deflection of 0.32 +/- 0.01 mm) 3.5.7.1 At 1.80 MPa 110 C 3.5.7.2 At 0.45 MPa 160 C 3.5.8 H

15、eat Aging Performance (ISO 188/ASTM D 573, 150 +/- 50 air changes/h, 1000 h at 120 +/- 2 C. After heat aging test specimens are to be conditioned in a desiccator for 3 - 5 h at 23 +/- 2 C. Unaged property values shall be determined at the time of the aged properties determination) 3.5.8.1 Impact Str

16、ength, Izod Change +/- 25% (Test Method per para 3.5.6.1, specimens to be notched before heat aging) 3.6 FLAMMABILITY (ISO 3795) Burn Rate, max 100 mm/minute The specimen size required for material approval is 355 x 100 x 1.0 +/- 0.1 mm with a smooth surface. 3.7 FOGGING (FLTM BO 116-03) Fog Number,

17、 min 90 Formation of excessive amounts of clear film or droplets is cause for rejection. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 COEFFICIENT OF LINEAR THERMAL EXPANSION 4 6-5/C (ASTM D 696)

18、 5.2 MOLD SHRINKAGE (ISO 2577, approx. 150 x 100 x 3.2 +/- 0.2 mm injection molded specimen) 5.2.1 Molding Shrinkage . After 48 h at 23 +/- 2 C 0.7 - 1.0% 5.2.2 Post Shrinkage (Separate specimens required for each test) . After 48 h at 80 C 0.05 - 0.15% . After 30 minutes at 120 C 0.05 - 0.15% ENGIN

19、EERING MATERIAL SPECIFICATIONWSK-M4D829-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 4 of 5 5.3 WATER ABSORPTION 0.1 - 0.25% (ISO 62, 24 h/ASTM D 570, 24 h, 50 +/- 1 mm diameter, 3.2 +/- 0.2 mm thick specimen) 5.4 RECYCLING CODE SAE PA12-GF30 OPTIONAL ENGINEERING MATERIAL SPECIFICATIONWSK-M4D829-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 5 of 5