FORD WSL-M4D632-A-2005 POLYTETRAFLUOROETHYLENE (PTFE) SINTER MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A 《聚四氟乙烯（PTFE）熔结成型料 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 09 20 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.11, 3.12, 4 1989 02 07 Released NL001 168890-081 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 POLYTETRAFLUOROETHYLENE (PTFE), SINTER WSL-M4D

2、632-A MOLDING COMPOUND 1. SCOPE The material defined by this specification is a polytetrafluoroethylene (PTFE) compound suitable for compression molding and subsequent sintering. 2. APPLICATION This specification was released originally for material used for fuel system tubing where high temperature

3、 and alternate fuel resistance is required. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 MOLDING COMPOUND 3.4.1 Melting Peak Temperature 317 -

4、 337 C (ASTM D 1457) 3.5 MOLDED TEST SPECIMEN 3.5.1 Preparation of Test Specimens Test specimens shall be prepared according to ASTM D 1457. 3.5.2 Density 2.14 2.16 g/cm3(ASTM D 1457) 3.5.3 Tensile Strength at Max Load, min 20 MPa (ASTM D 1457) 3.5.3.1 Elongation at Break, min 200% 3.6 HEAT AGING (A

5、STM D 573, 168h at 204 +/- 2 C) 3.6.1 Tensile Strength Change +/- 10% (ASTM D 1457) 3.6.2 Elongation Change +/- 10% (ASTM D 1457) ENGINEERING MATERIAL SPECIFICATIONWSL-M4D632-APrinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 3.7 IMMERSION IN 85% FUEL C +15% M

6、ETHANOL (ASTM D 471, 168 h at 40 +/- 2 C) 3.7.1 Tensile Strength Change +/- 15% (ASTM D 1457) 3.7.2 Elongation Change +/- 25% (ASTM D 1457) 3.8 IMMERSION IN 85% FUEL C +15% ETHANOL (ASTM D 471, 168 h at 40 +/- 2 C) 3.8.1 Tensile Strength Change +/- 15% (ASTM D 1457) 3.8.2 Elongation Change +/- 25% (

7、ASTM D 1457) 3.9 IMMERSION IN OXIDIZED (SOUR) FUEL (FLTM AZ 105-01, PN 90, 168 h at 40 +/- 2 C) 3.9.1 Tensile Strength Change +/- 15% (ASTM D 1457) 3.9.2 Elongation Change +/- 25% (ASTM D 1457) 3.10 THERMAL INSTABILITY INDEX, max 7.0 (ASTM D 1457) 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 PARTICLE SIZE 350 - 650 (ASTM D 1457) micrometer 5.2 EXTRUSION PRESSURE 15.5 - 36.2 MPa (ASTM D 1457, 400:1 reduction)