FORD WSS-M12A4-A2-2005 LUBRICANT SOLID FILM HIGH TEMPERATURE ANTISEIZE (NICKEL FREE) TO BE USED WITH FORD WSS-M99P1111-A 《耐高温防卡塞（无镍）固态膜润滑剂 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 02 10 Revised Updated format 2002 08 19 Activated G. Stevens Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 LUBRICANT, SOLID FILM, HIGH TEMPERATURE ANTISEIZE WSS-M12A4-A2 (NICKEL FREE) 1. SCOPE T

2、he material defined by this specification is a metal-free, semi-synthetic lubricating paste containing inorganic lubricants and other additives to provide good adhesion to substrates and high temperature performance without the use of toxic metal powders. 2. APPLICATION This specification was releas

3、ed originally for materials used to provide high temperature (up to 1200 C) lubricity and sealing on metal parts used on automotive exhaust systems. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MAT

4、ERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 COMPOSITION Shall be a homogeneous mixture free from ingredients which are corrosive to ferrous metals. 3.3 HOMOGENEITY Samples from top, bottom, and interme

5、diate positions of packaged containers shall exhibit no visual difference in appearance or consistency. 3.4 STABILITY No visual change in homogeneity shall be observed when stored for a period of 6 months in air-tight metal containers. ENGINEERING MATERIAL SPECIFICATIONWSS-M12A4-A2Printed copies are

6、 uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 3.5 GALLING AND ANTISEIZE PROPERTIES No galling of the threads or block surfaces when the test apparatus is disassembled. The average torque for the removal of the nuts from the stud bolts shall not be more than 210 lb/ft (285 N

7、/m). Test Method: A block made of steel, 13 x 4.5 in (330 x 114 mm) by approximately 2 1/8 in (54 mm) thick, shall have 5 equally spaced, smoothly drilled 13/16 in (20.64 mm) diameter holes to allow for the insertion of 3/4 in (19.05 mm) studs. The top and bottom faces of the steel block shall be sm

8、ooth and parallel. Five unused studs in accordance with grade B16 of MIL-S-1222 or ASTM A193 and 10 unused nuts in accordance with grade 4 of MIL-S-1222 or ASTM A194 shall be used for this test. Each stud shall be approximately 4 in (102 mm) long. The threads of the studs and nuts shall be evenly co

9、ated with the compound, the studs inserted into the holes in the lock, and the nuts screwed on finger-tight. The overall length of each stud shall be measured with a dial indicator graduated in 0.0001 in (0.0025 mm) divisions. The nuts then shall be tightened until an elongation of 0.00165 in/in (mm

10、/mm) of test length is obtained, which corresponds to a stress of 50,000 psi (345 MPa) root area of stud. The test block assembly shall be placed in an electrically heated oven and subjected to 560 - 571 C for 6 h. Then the assembly shall be removed from the oven and allowed to cool to room temperat

11、ure. The nuts shall be tightened to reestablish the originally calculated stressed stud lengths. The heating, cooling and stud length adjustment shall be repeated. Then for the third time the assembly shall be heated and cooled. Without further stress adjustment, the assembly shall be subjected to a

12、 spray of 20% aqueous solution of sodium chloride for 7 days. At the end of the period, the assembly shall be removed and allowed to dry at room temperature for 24 hours. Determine the torque required to loosen the nuts and the conditions of the threads and surfaces of the test block, seizing of the nuts, and shearing of studs shall be noted.