FORD WSS-M1H1005-A-2005 FABRIC LUGANO CHARCOAL BLACK PATTERN WARP KNITTED UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A 《LUGANO炭黑图案的不分层经编针织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 06 15 Activated L. Neves Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 FABRIC, LUGANO CHARCOAL BLACK PATTERN, WARP KNITTED, WSS-M1H1005-A UNLAMINATED 1. SCOPE The material defined by this specif

2、ication is a warp knitted polyester fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for 2007 Model Year. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as ap

3、plicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 6% tolerance (ASTM D 3775) Wales 130 wales/10 cm Courses 23

4、0 courses/10 cm 3.2.2 Fabric Weight, +/- 6% tolerance 240 g/m (FLTM BN 106-01) 3.3 COMPOSITION (ASTM D 629) Fabric 100% Polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Pile 70 dtex f36, Semi-Dull, Round, Textured Polyester Back 70 dtex f36, Semi Dull, Round, Flat Polyester ENGINEERING MATERIAL SPECIFI

5、CATIONWSS-M1H1005-A Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 3.5 METHOD OF DYEING Piece Dyed 3.6 FINISHING OPERATIONS Knit, Dye, Raise, Heat Set 3.7 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/min. Note: Not required on face fabric when use

6、d as a fully bonded composite. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that material defined in this specification and shipped to anyone assembly plant will be produced by one supplier only.