1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 01 05 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, MAYA PATTERN, FLAT CIRCULAR KNIT WSS-M1H1014-A 1. SCOPE The material defined by this specification is a MAYA p
2、attern, flat CIRCULAR KNIT bodycloth of good quality and uniform composition. The fabric is approved as a trilaminated fabric with foam and knitted scrim. 2. APPLICATION This specification was released originally for material used as an insert of seat fabric for the 2008 D333 vehicle. 3. REQUIREMENT
3、S In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABR
4、IC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 106/10 cm Courses 98/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric 366 g/m2 Knitted Scrim 70 g/m2Laminated to 3mm foam and scrim 551 g/m2ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1014-A Printed copies
5、are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fabric 100% Polyester Knitted Scrim 100% PET Scrim 3.4 YARN CONSTRUCTION (ASTM D 1244) Face 61% 16.7 tex f68 (natural text polyester) x 2 17% 16.7 tex f34 (solution dye polyester) x 1 Back 22% 16.7 tex f36 (natural text polyester) x 1 3.5 METHOD OF DYEING Piece dyed 3.6 FINISHING OPERATIONS Knit, Setmake, Dye, Slit, Heatset, Inspect