FORD WSS-M1H1018-A-2016 FABRIC TECH PATTERN KNIT TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions2006 01 09 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, TECH PATTERN, KNIT WSS-M1H1018-A 1. SCOPEThe material defined by this specification is a TECH PATTERN, 4 bars, 2

2、8 Gauge, TRICOT knit, bodycloth of good quality and uniform composition.2. APPLICATIONThis specification was released originally for material used as an interior trim fabric for 2007 P356 seatinsert.3. REQUIREMENTSIn addition, to the requirements listed herein, the fabric shall meet all requirements

3、 ofWSS-M8P18-A1/A4 as applicable.3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3887) Wales 130

4、 wales/10 cm Courses 250 courses/10 cm 3.2.2 Fabric Weight, range, g/m2 (FLTM BN 106-01) Laminated * Face w/no Backcoat 411 - 454 320 - 354 * 3 mm foam thickness3.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100% Polyester NOT TO BE USED FOR NEW DESIGN2016 04 27 N Stat

5、us No longer used D. Murtonen, NAENGINEERING MATERIAL SPECIFICATIONWSS-M1H1018-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Face (A) 64 % 11.1 tex (textured polyester yarn) (B) 3.4% 11.1 tex (textured polyester yarn) Middle 3.4% 11.1 tex (textured polyester yarn) Back 29% 11.1 tex (textured polyester yarn) 3.5 METHOD OF DYEING Piece Dye and/or solution 3.6 FINISHING OPERATIONS Wash, preset, dye, scutch, heatset, inspect