1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 12 10 Revised Para 2 , 3.6 , 4.2 , 4.3 M. Montgomery, EU 2008 05 19 Activated M. Montgomery, EU Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 1 of 2 FABRIC, PUR PATTERN, WOVEN JACQUARD, WSS-M1H1057-A U

2、NLAMINATED 1. SCOPE The material defined by this specification is a jacquard polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for use in the C344. Fabric developed using a Tri-Laminate construction with no back coating. 3.

3、REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materi

4、als (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/-10 % tolerance (ASTM D 3775) Warp 350 ends/10 cm Weft 180 picks/10 cm 3.2.2 Fabric Weight, +/-10 % tolerance (FLTM BN 106-01) 365 g/m23.3 COMPOSITION (ASTM D 629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp Packa

5、ge Dyed - 620dtex, f 102 (Air Jet Texturised) Weft Package Dyed - 620dtex, f 102 (Air Jet Texturised) Package Dyed - 167dtex, f 34 x 3 elastic effect ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1057-APrinted copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 2 of 2 3.5 METHOD OF

6、 DYEING Yarn Dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS - Washing - Drying - Fixing As approved by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Pu

7、rchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 Global C346 strategy to use Tri-laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above fabric construction, Composition & Yarn construction.The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4.