FORD WSS-M1H1069-A2-2012 FABRIC MALT PATTERN WOVEN DOBBY UNLAMINATED WITH ANTI SOILING COATING TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M1H1069-A).pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 1 2012 08 23 Released Released A2 suffix M. Montgomery, EU 2009 01 22 Released Released A suffix M. Montgomery, EU Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 FABRIC, MALT PATTERN, WOVEN DOBB

2、Y, WSS-M1H1069-A UNLAMINATED FABRIC, MALT PATTERN, WOVEN DOBBY, WSS-M1H1069-A2 UNLAMINATED, WITH ANTI SOILING COATING 1. SCOPE A - The material defined by this specification is a woven dobby polyester face fabric. A2 - The material defined by this specification is a woven dobby polyester face fabric

3、 that has been treated with an anti-soiling coating to meet the stain resistance requirement of the fabric performance specification. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for use in the V36x 2013 Model Year. 3. REQUIREMENTS In additio

4、n to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3

5、.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D3775) Warp 218/10 cm Weft 176/10 cm 3.2.2 Fabric Weight, +/- 10% tolerance (FLTM BN 106-01) 340 g/m2 3.3 COMPOSITION (ASTM D629) Fabric 100 % polyester ENGINEERING MATERIAL SPECIFICATION WSS-M1H1069-A Copyright 2012, Ford Global Tech

6、nologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D1244) Warp 830dtex;f192, Polyester, air textured, round, semi dull, Solution dyed Weft 830dtex; f192, Polyester, Air textured, round, semi dull solution dyed Weft 550dtex; f108, Polyester, Fully oriented, trilobal, bright, Solution dyed 3.5 METH

7、OD OF DYEING Solution dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS Washing Stenter frame 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engine

8、ering Material Specifications. 4.1 Purchase departments will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 Global V36x strategy to use Tri-laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above fabric construction, Composition & Yarn Construction. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4. 4.4 Lighter colors of this product will need an anti-soiling coating adding