FORD WSS-M1H1075-A3-2013 FABRIC CATALYST ARGENTINA WOVEN DOBBY UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M1H1075-A1).pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 0 2013 09 16 Released R.Kyle, EU Controlled document at www.MATS Copyright 2013, Ford Global Technologies, LLC Page 1 of 2 FABRIC, CATALYST, AAT (THAILAND), WOVEN DOBBY, UNLAMINATED WSS-M1H1075-A1 FABRIC, CATALYST, SOUTH AFRICA, WOVEN DOB

2、BY, UNLAMINATED WSS-M1H1075-A2 FABRIC, CATALYST, ARGENTINA, WOVEN DOBBY, UNLAMINATED WSS-M1H1075-A3 1. SCOPE The material defined by this specification is a polyester woven dobby face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim bolster fabr

3、ic for use in the T6 program. Fabric was developed as a Tri-Laminate, using local content. The fabric is used back coated and unlaminated in seat back applications only. A1 is for AAT (Thailand) A2 is for South Africa A3 is for Argentina 3. REQUIREMENTS In addition to the requirements listed herein,

4、 the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric

5、Count, +/- 10% (ASTM D3775) A1 (AAT) A2 (South Africa) A3 (Argentina) Warp 610 ends/10 cm 600 ends/10 cm 610 ends/10 cm Weft 196 picks/10 cm 180 picks/10 cm 200 picks/10 cm 3.2.2 Fabric Weight, +/- 10% (FLTM BN 106-01) A1 (AAT) A2 (South Africa) A3 (Argentina) Face Fabric 340 g/m2 355 g/m2 330 g/m2

6、Back coat 70 g/m2 65 g/m2 60 g/m2 Total Weight 410 g/m2 420 g/m2 390 g/m2 ENGINEERING MATERIAL SPECIFICATION WSS-M1H1075-A1/A2/A3 Copyright 2013, Ford Global Technologies, LLC Page 2 of 2 3.3 COMPOSITION (ASTM D 629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D1244) A1 (AAT) A2 (South Africa)

7、 A3 (Argentina) Warp 167dtex, f48/2 167dtex, f48/2 167dtex, f34/3 Weft 167dtex, f48/2 250dtex, f72/2 250dtex, f72/2 220dtex, f48/2 3.5 METHOD OF DYEING Yarn dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS Washing Drying Back coating Or as approved by Materials Engineering 4. GEN

8、ERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that the material defined in this specification and

9、 shipped to any one assembly plant will be produced by one supplier only. 4.2 Global Strategy is to use Tri-Laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above fabric construction, composition and yarn construction requirements. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4.