FORD WSS-M1H1088-A-2006 FABRIC ZINC II PATTERN FLAT WOVEN TO BE USED WITH FORD WSS-M99P1111-A 《ZINC II图案的平织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 11 08 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 1 of 2 FABRIC, ZINC II PATTERN, FLAT WOVEN WSS-M1H1088-A 1. SCOPE The material defined by this specification is a ZINC II pat

2、tern, Dobby woven, bodycloth of good quality and uniform composition. The fabric is backcoated. 2. APPLICATION This specification was released originally for material used as a seat fabric, insert/bolster application for 2007 P356 Super Duty. 3. REQUIREMENTS Material specification requirements are t

3、o be used for initial qualification of materials. In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for

4、 Production Materials (WSS-M99P1111-A) 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 338 ends/10 cm Fill 185 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric w/backcoat 400 g/m23.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-

5、M8P18-A1/A4. Fabric 100% Polyester Backcoating Latex ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1088-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp A. 16.7 tex f34 (false twist polyester) x 3 Fill W 16.7 tex f68 (air textured polyester) x 3 X 16.7 tex f34 (solution dye polyester) x 3 3.5 METHOD OF DYEING piece dye/solution dye 3.6 FINISHING OPERATIONS woven, wash, dye, backcoated