FORD WSS-M1H1117-A-2008 FABRIC LAS VEGAS MIDNIGHT BLACK PATTERN WARP KNITTED TO BE USED WITH FORD WSS-M99P1111-A 《拉斯维加斯午夜黑（LAS VEGAS MIDNIGHT BLACK）图案的经编针织织物 与标准FORD WSS-M99P111.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 12 17 N-STATUS V. Demarchi, FSAO 2007 08 22 Activated L. Neves Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 FABRIC, LAS VEGAS MIDNIGHT BLACK PATTERN, WARP KNITTED WSS-M1H1117-A NOT TO BE USED F

2、OR NEW DESIGN 1. SCOPE The material defined by this specification is a warp knitted polyester fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for Ford Ka 2006 Model Year. 3. REQUIREMENTS In addition to the requirements listed herein, the

3、 fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Coun

4、t, range (ASTM D 3775) Warp 15 - 17 yarn/cm Fill 11 - 13 yarn/cm 3.2.2 Fabric Weight, range (FLTM BN 106-01) Seat (laminated to 4.5 mm foam + backing fabric) 376 - 480 g/m Door Panel (laminated to 7.3 mm foam) 416 - 532 g/m 3.3 COMPOSITION (ASTM D 629) Fabric 100% Polyester Foam - Seat PUR/Polyester

5、 - D28 Foam - Door Panel PUR/Polyester D28 Backing Fabric 100% Polyamide 45 g/m ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1117-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 200 and 80 dtex, Semi Dull, Round, False

6、Twist Polyester 3.5 METHOD OF DYEING Warp Yarn Dyed and Solution Dyed 3.6 FINISHING OPERATIONS Heat Set 3.7 THICKNESS, mm, range (ASTM D 1777) Seat (laminated to 4.5 mm foam + backing fabric) 3.4 - 4.3 mm Door Panel (laminated to 7.3 mm foam) 6.8 - 8.0 mm 3.8 TRIMMABILITY PROPERTIES 3.8.1 Stretch, %

7、, range (SAE J855) Seat Warp 10 - 20% Fill 10 - 20% Door Panel Warp = 8.0% Fill = 3.5% 3.9 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that material defined in this specification and shipped to anyone assembly plant will be produced by one supplier only.