1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 03 19 Activated M. Dumitrescu Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 FABRIC, LUCAS PATTERN, FLAT WOVEN WSS-M1H1130-A 1. SCOPE The material defined by this specification is a LUCAS pattern
2、, flat woven bodycloth of good quality and uniform composition. The fabric is backcoated. 2. APPLICATION This specification was released originally for material used as a seat fabric, insert application for 2009 P415. 3. REQUIREMENTS Material specification requirements are to be used for initial qua
3、lification of materials. In addition to the requirements listed herein, the fabric shall meet all requirements of: WSS-M8P18-A1/A4. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WS
4、S-M99P1111-A) 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 5% tolerance (ASTM D 3775) Warp 340 ends/10 cm Fill 180 picks/10 cm 3.2.2 Fabric Weight, +/- 5% tolerance (FLTM BN 106-01) Face Fabric w/backcoat 440 g/m23.3 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4. Fabric 100%
5、Polyester Backcoating Latex ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1130-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 16.7 tex f34 (false twist polyester) x 3 Fill 16.7 tex f68 (textured polyester) x 3 16.7 tex f34 (sol dye polyester) x 3 3.5 METHOD OF DYEING Piece dye/solution dye 3.6 FINISHING OPERATIONS Woven, wash, dye, backcoated