FORD WSS-M1H1188-A1-2015 FABRIC MADRID PATTERN WARP KNITTED UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2015 05 19 Released M.Fontes - SA Controlled document at www.MATS Copyright 2015, Ford Global Technologies, LLC Page 1 of 2 FABRIC, MADRID PATTERN, WARP KNITTED, UNLAMINATED WSS-M1H1188-A1 1. SCOPE The material defined by this specific

2、ation is a warp knitted polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim bolster fabric for use in the B-562 program. The fabric was approved laminated with foam and backing fabric/scrim. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS

3、FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.1.1 WSS-M1H1188-A1 is based on virgin materials. 3.1.2 In addition to the requirements listed herein, the fabric shall meet all requirements

4、of WSS-M8P18-B1/B2/B3/B4 as applicable. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10% (ASTM D3775) Warp 120 ends/10 cm Weft 215 picks/10 cm3.2.2 Fabric Weight, +/- 10% (FLTM BN 106-01) Face Fabric 251 g/m2 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D1244) War

5、p 43 dtex, f24 - Semi dull, round, flat Weft 116 dtex, f34, Semi dull, round, texturized3.5 METHOD OF DYEING Solution Dye or as approved by Materials Engineering ENGINEERING MATERIAL SPECIFICATION WSS-M1H1188-A1 Copyright 2015, Ford Global Technologies, LLC Page 2 of 2 3.6 FINISHED OPERATIONS Washin

6、g / Heat setting or as approved by Materials Engineering 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments

7、will ensure that materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 Global strategy is to use Tri-laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above Fabric Construction, Composition & Yarn construction requirements. The fabric must also meet the requirements of WSS-M8P18-B1/B2/B3/B4.