1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2010 09 28 Activated M.Fontes - FSAOPrinted copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 1 of 2 FABRIC, SOGANLI PATTERN, WOVEN JACQUARD WSS-M1H1216-A 1. SCOPE The material defined by this specification is a jacqua
2、rd woven polyester fabric applied to seat. The fabric has been developed using a trilaminate construction. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for H534 MY2011 Project. 3. REQUIREMENTS In addition to the requirements listed herein, th
3、e fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Cou
4、nt, +/- 5% tolerance (ASTM D 3775) Warp 37.0 yarn/cm Fill 19.0 yarn/cm 3.2.2 Fabric Weight, +/- 10% tolerance (FLTM BN 106-01) Seat (laminated to 2,0mm fabric+ foam+ backing fabric) 406 - 496 g/m 3.3 COMPOSITION (ASTM D 629) Fabric 100% Polyester Foam 100% Polyeter Backing Fabric (Seats only) 100% P
5、olyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 500 dtex, Semi Dull, Round, False Twist, Polyester Fill 390 dtex, Semi Dull, Round, False Twist Polyester ENGINEERING MATERIAL SPECIFICATIONWSS-M1H1216-A Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 2 of 2 3.5 ME
6、THOD OF DYEING Warp Solution Dyed Fill Solution Dyed and Yarn Dyed 3.6 FINISHING OPERATIONS Heat Setting 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to anyone assembly plant will be produced by one supplier only.