FORD WSS-M1H715-C1-2008 FABRIC MARQUIS PATTERN KNITTED 3mm - TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M1H715-A)《侯爵(KESTREL)图案的3毫米厚针织织物 与标准FORD WSS-M99P1111-A一起使用 .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2008 11 26 N-STATUS No Replacement L. Schmalz, FNA / M. Montgomery, FOE2003 04 10 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.14, 3.15, 4 deleted 1996 07 29 Activated N.J. Komatsu Printed copies are unc

2、ontrolled Page 1 of 3 Copyright 2008, Ford Global Technologies, Inc. FABRIC, MARQUIS PATTERN, KNITTED, UNLAMINATED WSS-M1H715-A FABRIC, MARQUIS PATTERN, KNITTED, 3mm WSS-M1H715-B1 FABRIC, MARQUIS PATTERN, KNITTED, 6mm WSS-M1H715-B2 FABRIC, MARQUIS PATTERN, KNITTED, 3mm WSS-M1H715-C1 FABRIC, MARQUIS

3、PATTERN, KNITTED, 6mm WSS-M1H715-C2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by these specifications is a 3 bar 28 gauge, warp knitted simulated velour polyester bodycloth. 2. APPLICATION These specifications were originally released for material used as interior trim fabrics. MAR

4、QUIS PATTERN WSS-M1H715-A Unlaminated WSS-M1H715-B1 3.0 mm flame laminated to polyether foam and knitted fabric WSS-M1H715-B2 6.0 mm flame laminated to polyether foam and knitted fabric WSS-M1H715-B2 6.0 mm flame laminated to polyether foam and knitted fabric WSS-M1H715-C1 3.0 mm flame laminated to

5、polyester foam and knitted fabric WSS-M1H715-C2 6.0 mm flame laminated to polyester foam and knitted fabric 3. REQUIREMENTS In addition to the requirements listed herein, the fabric or laminate shall meet all requirements of WSB-M8P1-I. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material sup

6、pliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). ENGINEERING MATERIAL SPECIFICATION WSS-M1H715-A/B1/B2/C1/C2 Page 2 of 3 Copyright 2008, Ford Global Technologies, Inc. 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5% tolerance

7、(ASTM D 3887) Wales 145 ends 10/cm Courses 235 picks 10/cm 3.4.2 Fabric Weight, range 310 - 390 g/m2(FLTM BN 106-01) (350 average)3.5 COMPOSITION (ASTM D 629) Fabric 100 % polyester 3.6 YARN CONSTRUCTION (ASTM D 1244) Pile 76 dTex f 24 (polyester, fuly-dul) Middle 78 dtex f 24 (polyester bight) Back

8、 78 dtex f 24 (polyester semi-dul) 3.7 METHOD OF DYEING Yarn dyed or as approved by Material Enginering 3.8 FINISHED OPERATIONS As approved by Material Engineering 3.9 REQUIREMENTS FOR POLYETHER FOAM As specified in WSD-M2D243-A2 3.10 REQUIREMENTS FOR BACKING As pecifed inFABRIC WSD-M9H125-B2 ENGINE

9、ERING MATERIAL SPECIFICATION WSS-M1H715-A/B1/B2/C1/C2 Page 3 of 3 Copyright 2008, Ford Global Technologies, Inc. 3.11 REQUIREMENTS FOR THE FLAME LAMINATED MATERIAL 3.11.1 Thickness, range (ASTM D 1777, circular presser foot area 645 mm2, 2.8 g force, 43 Pa pressure) WSS-M1H715-B1 3.0 +/- 1.0 mm WSS-

10、M1H715-B2 6.0 +/- 1.0 mmWSS-M1H715-C1 3.0 +/- 1.0 mm WSS-M1H715-C2 6.0 +/- 1.0 mm3.11.2 Weight, min (FLTM BN 106-01) WSS-M1H715-B1 470 +/- 50 g/m2WSS-M1H715-B2 590 +/- 50 g/m2WSS-M1H715-C1 450 +/- 50 g/m2WSS-M1H715-C2 550 +/- 50 g/m23.12 BACK MARKING The contrast between the batch marking print and

11、the backing fabric must be no greater than that shown by the master sample approved by Materials & Fastener Engineering. 3.13 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of these specifications. 5.1 Purchase departments will ensure that both materials defined in these specifications and shipped to any one assembly plant will be produced by one supplier only.