FORD WSS-M1H717-F2-2008 FABRIC ARCO II PATTERN WOVEN JACQUARD 6 mm TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD WSS-M1H717-A)《ARCO II图案的6 mm厚提花机织织物 与标准FORD WSS-M99P1111-A一.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2008 11 26 N-STATUS No Replacement L. Schmalz, FNA / M. Montgomery, FOE2003 03 21 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.16, 3.17, 4 deleted 1996 10 10 Activated N. Komatsu Printed copies are unco

2、ntrolled Page 1 of 4 Copyright 2008, Ford Global Technologies, Inc. FABRIC, ARCO II PATTERN, WOVEN JACQUARD, WSS-M1H717-A UNLAMINATED FABRIC, ARCO II PATTERN, WOVEN JACQUARD, 3 mm WSS-M1H717-B1 FABRIC, ARCO II PATTERN, WOVEN JACQUARD, 6 mm WSS-M1H717-B2 FABRIC, ARCO II PATTERN, WOVEN JACQUARD, 3 mm

3、WSS-M1H717-C1 FABRIC, ARCO II PATTERN, WOVEN JACQUARD, 6 mm WSS-M1H717-C2 FABRIC, ARCO II PATTERN, WOVEN JACQUARD, 6 mm WSS-M1H717-D2 FABRIC, ARCO II PATTERN, WOVEN JACQUARD, 3 mm WSS-M1H717-F1 FABRIC, ARCO II PATTERN, WOVEN JACQUARD, 6 mm WSS-M1H717-F2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The mat

4、erial defined by these specifications is a woven jacquard polyester face fabric which can be flame laminated to polyester or polyether urethane foam and backed with either a knitted fabric or polyurethane film. It can also be backed with an HFW weldable backcoating. 2. APPLICATION WSD-M1H717-A is us

5、ed for molded headrests and also adhesive coated for use on inner door panels. WSD-M1H717-B1, B2, C1, C2, F1, F2 are used for seat wearing surfaces. WSD-M1H717-D2 is used for adhesively bonded door and quarter trim panel applications. ARCO II PATTERN WSS-M1H717-A Unlaminated WSS-M1H717-B1 3.0 mm, fl

6、ame laminated to polyether foam and knitted fabric WSS-M1H717-B2 6.0 mm, flame laminated to polyether foam and knitted fabric WSS-M1H717-C1 3.0 mm, flame laminated to polyester foam and knitted fabric (EAO use only) WSS-M1H717-C2 6.0 mm, flame laminated to polyester foam and knitted fabric (EAO use

7、only) WSS-M1H717-D2 6.0 mm, flame laminated to polyether foam WSS-M1H717-F1 3.0 mm, flame laminated to polyester foam and polyurethane film (EAO use only) WSS-M1H717-F2 6.0 mm, flame laminated to polyester foam and polyurethane film (EAO use only) ENGINEERING MATERIAL SPECIFICATION WSS-M1H717-A/B1/B

8、2/C1/C2/D2/F1/F2 Page 2 of 4 Copyright 2008, Ford Global Technologies, Inc. 3. REQUIREMENTS In addition to the requirements listed herein, the fabric shall meet all requirements of WSB-M8P1-I. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to th

9、e Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5 % tolerance (ASTM D 3775) Warp 242 ends/10 cm Weft 150 picks/10 mm 3.4.2 Fabric Weight, range 285 - 315 g/m2(FLTM BN 106-01) 3.5 COMPOSITION (ASTM D 629) Fabric 100 % polyest

10、er 3.6 YARN CONSTRUCTION (ASTM D 1244) Warp 760 dtex f192 (polyester, semi-dull air texturised round section)760 dtex f28 (polyester, bright air texturised trilobal section) Weft 760 dtex f192 (polyester, semi-dull air texturised round section)3.7 METHOD OF DYEING Yarn dyed and spun dyed or as appro

11、ved by Materials Engineering ENGINEERING MATERIAL SPECIFICATION WSS-M1H717-A/B1/B2/C1/C2/D2/F1/F2 Page 3 of 4 Copyright 2008, Ford Global Technologies, Inc. 3.8 FINISHING OPERATIONS As approved by Materials Engineering 3.9 REQUIREMENTS FOR POLYESTER FOAM As specified in WSD-M2D243-A4 3.10 REQUIREMEN

12、TS FOR POLYETHER FOAM As specified in WSD-M2D243-A2 3.11 REQUIREMENTS FOR THE BACKING As specified in FABRIC (B1, B2) WSD-M9H111-B 3.12 REQUIREMENTS FOR THE BACKING As specified in FABRIC (C1, C2) WSD-M9H136-A 3.13 REQUIREMENTS FOR THE PU As specified in BACKING FILM WSD-M9H134-B1 3.14 REQUIREMENTS

13、FOR THE FLAME LAMINATED MATERIAL 3.14.1 Thickness, range (ASTM D 1777, circular presser foot area 645 mm2, 2.8 g force, 43 Pa pressure) WSS-M1H717-B1 3.0 +/- 1.0 mm WSS-M1H717-B2 6.0 +/- 1.0 mmWSS-M1H717-C1 3.0 +/- 1.0 mm WSS-M1H717-C2 6.0 +/- 1.0 mmWSS-M1H717-D2 6.0 +/- 1.0 mm WSS-M1H717-F1 3.0 +/-

14、 1.0 mmWSS-M1H717-F2 6.0 +/- 1.0 mm 3.14.2 Compressed Thickness, (ASTM D 1777, circular presser foot area 645 mm2, 1 kg force, 5 s dwell) WSS-M1H717-D2 2.8 +/- 0.3 mm WSS-M1H717-F1 2.0 +/- 0.3 mmWSS-M1H717-F2 2.8 +/- 0.3 mm ENGINEERING MATERIAL SPECIFICATION WSS-M1H717-A/B1/B2/C1/C2/D2/F1/F2 Page 4

15、of 4 Copyright 2008, Ford Global Technologies, Inc. 3.14.3 Weight, range (FLTM BN 106-01) WSS-M1H717-B1 450 +/- 40 g/m2WSS-M1H717-B2 550 +/- 40 g/m2WSS-M1H717-C1 450 +/- 40 g/m2WSS-M1H717-C2 530 +/- 40 g/m2WSS-M1H717-D2 510 +/- 40 g/m2WSS-M1H717-F1 440 +/- 40 g/m2WSS-M1H717-F2 520 +/- 40 g/m23.14.4

16、Stretch and set, %, range (SAE J855) Stretch (B1, B2, C1, C2, F1, F2) Warp 1 - 15 Weft 1 -20 Set Warp 0 - 5 Weft 0 -5 3.14.5 Modulus, max (D2, F1, F2) Strain, 6 % Warp 200 N Weft 50 N3.15 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Note: Not required on face fabric when used as a f

17、ully bonded composite 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of these specifications. 5.1 Purchase departments will ensure that both materials defined in these specifications and shipped to any one assembly plant will be produced by one supplier only.